Novel composite decorative material

A decorative material, a new type of technology, applied in the field of wood, can solve the problems of less research and application of glass fiber, and achieve high strength, increase static bending strength, and improve the effect of elastic modulus

Inactive Publication Date: 2017-11-24
龙门县品汐竹木制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are few studies and applications of glass fiber in wood-plastic composite materials, and there are few research reports on its performance, and the relevant research reports on the actual working conditions of materials are even rarer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel composite decorative material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A new type of composite decorative material, which is composed of a wear-resistant layer 5, a breathable layer 4, an insulating layer 3, a buffer layer 2, and a composite core board 1 arranged in sequence; the wear-resistant layer 5 is super-amphiphobic and wear-resistant polyphenylene sulfide Ether-based coating, the air-permeable layer 4 is a flax fiber layer, the thermal insulation layer 3 is a composite layer of polystyrene and polyurethane foam, the buffer layer 2 is a self-resetting bending-resistant steel frame structure, and the composite The raw materials of core plate 1 and the parts by weight of each raw material are:

[0052] Mixed wood flour: 27 parts;

[0053] Wood fiber powder: 20 parts;

[0054] Alkali-free long-cut glass fiber: 15 parts;

[0055] Polyethylene terephthalate: 6 parts;

[0056] 12 parts of polybenzobisoxazole fiber;

[0057] Basalt fiber: 20 parts;

[0058] Pseudoboehmite: 19 parts;

[0059] 10 parts of silane coupling agent;

[0060]...

Embodiment 2

[0071] A new type of composite decorative material, which is composed of a wear-resistant layer 5, a breathable layer 4, an insulating layer 3, a buffer layer 2, and a composite core board 1 arranged in sequence; the wear-resistant layer 5 is super-amphiphobic and wear-resistant polyphenylene sulfide Ether-based coating, the air-permeable layer 4 is a flax fiber layer, the thermal insulation layer 3 is a composite layer of polystyrene and polyurethane foam, the buffer layer 2 is a self-resetting bending-resistant steel frame structure, and the composite The raw materials of core plate 1 and the parts by weight of each raw material are:

[0072] Mixed wood flour: 22 parts;

[0073] Wood fiber powder: 29 parts;

[0074] Alkali-free long-cut glass fiber: 11 parts;

[0075] Polyethylene terephthalate: 9 parts;

[0076] 9 parts of polybenzobisoxazole fiber;

[0077] Basalt Fiber: 16 parts;

[0078] Pseudoboehmite: 21 parts;

[0079] 7 parts of silane coupling agent;

[0080]...

Embodiment 3

[0086] A new type of composite decorative material, which is composed of a wear-resistant layer 5, a breathable layer 4, an insulating layer 3, a buffer layer 2, and a composite core board 1 arranged in sequence; the wear-resistant layer 5 is super-amphiphobic and wear-resistant polyphenylene sulfide Ether-based coating, the air-permeable layer 4 is a flax fiber layer, the thermal insulation layer 3 is a composite layer of polystyrene and polyurethane foam, the buffer layer 2 is a self-resetting bending-resistant steel frame structure, and the composite The raw materials of core plate 1 and the parts by weight of each raw material are:

[0087] Mixed wood flour: 34 parts;

[0088] Wood fiber powder: 16 parts;

[0089] Alkali-free long-cut glass fiber: 19 parts;

[0090] Polyethylene terephthalate: 4 parts;

[0091] 16 parts of polybenzobisoxazole fiber;

[0092] Basalt Fiber: 16 parts;

[0093] Pseudoboehmite: 21 parts;

[0094] 7 parts of silane coupling agent;

[0095...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a novel composite decorative material, which is composed of a wear-resistant layer, a breathable layer, a thermal insulation layer, a buffer layer and a composite core plate sequentially. The wear-resistant layer is a super-amphiphobic wear-resistant polyphenylene sulfide based coating, the breathable layer is a flax fiber layer, the thermal insulation layer is a polystyrene and polyurethane foamed composite layer, the buffer layer is self-resetting steel moment-resisting frame structure, the composite core plate comprises the following raw materials by weight: 22-34 parts of mixed wood powder; 16-29 parts of wood fiber powder; 11-19 parts of non-alkali long-cut glass fiber; 4-9 parts of polyethylene terephthalate; 9-16 parts of polybenzobisoxazole fiber; 16-23 parts of basalt fiber; 17-21 parts of pseudo-boehmite; and 7-15 parts of a silane coupling agent. The novel composite decorative material provided by the invention has good wear-resistant, breathable and stable performance, and can also have the advantages of high strength, simple structure and long service life.

Description

technical field [0001] The invention relates to the technical field of wood, in particular to a novel composite decorative material. Background technique [0002] Wood-plastic composite materials are composite materials made of wood or other cellulose materials and thermoplastics with uniform temperature matching. Although they have many advantages, there are still certain limitations and defects in the application of wood-plastic products in China. Wood-plastic products have defects such as insufficient mechanical strength, poor heat resistance, and large thermal expansion coefficient during use. When used as floor boards and other materials, the tribological properties of the material are not ideal. In order to improve the above limitations and make up for the defects, and expand the advantages of replacing wood products, the research and development of high-filling plant fibers and high-performance wood-plastic composite products will be the leading direction of enterpris...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L67/02C08L79/04C08K13/04C08K7/14C08K7/10C08K5/54C09D181/02B32B33/00B32B9/02B32B9/04B32B27/30B32B27/40B32B15/18B32B15/02B32B15/095B32B15/082B32B15/16B32B21/02
CPCC08L97/02B32B5/02B32B5/18B32B5/245B32B15/046B32B15/16B32B15/18B32B21/02B32B33/00B32B2255/02B32B2255/26B32B2262/02B32B2262/065B32B2262/10B32B2262/101B32B2266/0228B32B2266/0278B32B2270/00B32B2307/554B32B2307/724B32B2471/00C08L2205/025C08L2205/035C08L2205/16C09D181/02C08L67/02C08L79/04C08K13/04C08K7/14C08K7/10C08K5/54
Inventor 王历文
Owner 龙门县品汐竹木制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap