Preparation method of efficient deepening type composite deepening agent

A deepening agent and high-efficiency technology, which is applied in the field of preparation of high-efficiency deepening type compound deepening agent, can solve the problems of poor deepening effect of the deepening agent and the like, and can improve the apparent depth, improve the deepening effect, and be widely used. Foreground effect

Inactive Publication Date: 2017-12-22
常州禾吉纺织品有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a method for preparing a high-efficiency deepening composite darkening agent in view of the defect that most of the current darkening agents have poor darkening effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0020] Mix methyltrichlorosilane, urea-formaldehyde resin, urea, and formic acid with a concentration of 5mol / L in a mass ratio of 3:2:1:10, put them into a beaker, and react at 80°C for 1 hour to obtain self-made modified silicone , mixed trifluoroethyl methacrylate and n-butyl acrylate at a volume ratio of 1:3 and stirred for 12 minutes to obtain a mixed solution, and added 3 mL of lauryl polyoxyethylene ether and 8 mL of distilled water to 20 mL of the mixed solution, and continued to mix and stir for 5 minutes , after stirring, add 1g of sodium persulfate, and react at 60°C for 2h, which is self-made emulsion 1; in parts by weight, add 11 parts of isophthalic acid to a 250mL four-necked flask equipped with a stirrer, reflux device and thermometer. Phorone diisocyanate, 3 parts of dibutyltin dilaurate, 2 parts of polyethylene glycol and 1 part of methyl ethyl ketone, after passing nitrogen gas, reflux reaction at a temperature of 60 ° C for 1 hour to obtain self-made emulsio...

example 2

[0022] Mix methyltrichlorosilane, urea-formaldehyde resin, urea, and formic acid with a concentration of 5mol / L in a mass ratio of 3:2:1:10, put them into a beaker, and react at 90°C for 1.5h to obtain a self-made modified organic compound. Silicon, mix trifluoroethyl methacrylate and n-butyl acrylate at a volume ratio of 1:3 and stir for 14 minutes to obtain a mixed solution, add 4 mL of lauryl polyoxyethylene ether and 9 mL of distilled water to 25 mL of the mixed solution, and continue to mix and stir 6min, after stirring, add 2g of sodium persulfate, and react at 70°C for 3h, which is self-made emulsion 1; in parts by weight, add 12 parts of Isophorone diisocyanate, 4 parts of dibutyltin dilaurate, 3 parts of polyethylene glycol and 2 parts of methyl ethyl ketone, after passing nitrogen gas, reflux reaction at a temperature of 70 ° C for 2 hours to obtain self-made emulsion 2; parts by weight In total, 14 parts of self-made emulsion 1, 12 parts of self-made emulsion 2, 7 p...

example 3

[0024]Mix methyltrichlorosilane, urea-formaldehyde resin, urea, and formic acid with a concentration of 5mol / L in a mass ratio of 3:2:1:10, put them into a beaker, and react at 100°C for 2 hours to obtain self-made modified silicone , mixed trifluoroethyl methacrylate and n-butyl acrylate at a volume ratio of 1:3 and stirred for 16 minutes to obtain a mixed solution, and added 5 mL of lauryl polyoxyethylene ether and 10 mL of distilled water to 30 mL of the mixed solution, and continued to mix and stir for 7 minutes , after stirring, add 3g of sodium persulfate, and react at 80°C for 4h, which is self-made emulsion 1; in parts by weight, add 13 parts of isophthalic acid to a 250mL four-necked flask equipped with a stirrer, reflux device and thermometer. Phorone diisocyanate, 5 parts of dibutyltin dilaurate, 4 parts of polyethylene glycol and 3 parts of methyl ethyl ketone, after passing nitrogen gas, reflux reaction at a temperature of 80 ° C for 3 hours to obtain self-made emu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of textile dyeing and finishing auxiliaries, in particular to a preparation method of an efficient deepening type composite deepening agent. The preparation method has the advantages that urea resin and urea are used to perform double modification on methyl trichlorosilane to allow amino-modified organic silicon to have a good deepening effect so as to increase the deepening effect of the deepening agent; two kinds of emulsions formed by trifluoroethyl methacrylate and isophorone diisocyanate are added to lower reflected light quantity of fabric, and the apparent depth of substances such as dyed fabric is increased; the organic silicon has high hydrophobicity and low refractive index, so that the refractive index of the two emulsions above is reduced, the apparent depth of the substances such as the dyed fabric is increased, the deepening effect of the deepening agent is further increased, and the prepared deepening agent is promising in application prospect.

Description

technical field [0001] The invention relates to the field of textile dyeing and finishing auxiliaries, in particular to a preparation method of a high-efficiency darkening compound darkening agent. Background technique [0002] With the improvement of living standards, people's requirements for textiles are getting higher and higher. Synthetic fibers have been widely used in recent years because of their high strength. Among them, polyester fibers are often used to replace natural fibers such as silk due to their cost advantages. But a big disadvantage of polyester fiber is that it is poor in dyeing dark color, especially black and other dark fabrics. Boundless visual effects. The problem of deep staining has become more and more serious. The emergence of the darkening agent is to solve this problem. It is an auxiliary agent that can improve the dyeing depth of disperse dyes on polyester fabrics. The excellent performance of the darkening agent directly affects the dark c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06P1/52D06P1/642D06P1/651
CPCD06P1/5292D06P1/525D06P1/5285D06P1/6426D06P1/65125
Inventor 杨立军张淑娴林大伟
Owner 常州禾吉纺织品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products