Water-based flame-retardant white bright back glue PVC and preparation method thereof

A flame retardant adhesive and adhesive technology, applied in the direction of adhesives, adhesive types, film/sheet adhesives, etc., can solve the problems of non-standard flame retardant properties of adhesive PVC, easy residual adhesive, easy to burn, etc. , to achieve the effect of high color reduction, good anti-oxidation performance and good surface adhesion

Inactive Publication Date: 2018-01-19
ZHEJIANG FULAI NEW MATERIAL CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, although the PVC material does not produce an open flame, it has the defect of being easy to burn, and it will also produce a large amount of toxic smoke during combustion, and it is also more likely to have potential combustion hazards. an important direction
But now there are some common problems with back-adhesive PVC: (1) The primer is generally a flammable substance, which makes the flame-retardant performance of the back-adhesive PVC not up to the standard; (2) But if too much inorganic flame-retardant powder is added to the primer Adhesive PVC has compatibility problems, which affects viscosity and tends to leave glue when removing advertising materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based flame-retardant white bright back glue PVC and preparation method thereof
  • Water-based flame-retardant white bright back glue PVC and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] In terms of weight percentage, weigh the following components:

[0036] (1) Flame retardant coating: in 89.9% polyvinyl alcohol solution, add 3.5% aluminum hydroxide, 3% ammonium polyphosphate, 3.5% melamine and 0.1% wetting agent and mix well;

[0037] (2) Flame retardant glue layer: 50% butyl acrylate, 12% methyl methacrylate, 6% acrylic acid, 8% acryl alcohol, 12.9% 2-ethyl (methacrylic acid acyloxymethyl) phosphate, Melamine 3%, sodium lauryl sulfate 0.1%, mix evenly, then add initiator 2%, react at 70-90°C for 7-9h, then add latex powder 1%, nano-attapulgite 2% and continue the reaction for 1-3 hours; after cooling to normal temperature, add 3% curing agent, stir for 20-40 minutes, filter, and set aside;

[0038] (3) Coating flame retardant coating 15-30g / m on the white PVC layer 2 , after drying; on the other side of the white PVC layer, apply a flame-retardant glue layer of 15-30g / m 2 , the coating speed is 20-40m / min, after drying, after laminating with the r...

Embodiment 2

[0040] In terms of weight percentage, weigh the following components:

[0041] (1) Flame retardant coating: add 10% aluminum hydroxide, 10% ammonium polyphosphate, 10% melamine and 0.5% wetting agent to 69.5% polyvinyl alcohol solution and mix evenly;

[0042] (2) Flame retardant glue layer: 38% butyl acrylate, 12% methyl methacrylate, 6% acrylic acid, 8% acrylic alcohol, 9.7% 2-ethyl (methacrylic acid acyloxymethyl) phosphate, Melamine 8%, sodium lauryl sulfate 0.3%, mix evenly, then add initiator 4%, react at 70-90°C for 7-9h, then add latex powder 5%, nano-attapulgite 6% and continue the reaction for 1-3 hours; after cooling to normal temperature, add 3% curing agent, stir for 20-40 minutes, filter, and set aside;

[0043] (3) Coating flame retardant coating 15-30g / m on the white PVC layer 2 , after drying; on the other side of the white PVC layer, apply a flame-retardant glue layer of 15-30g / m 2 , the coating speed is 20-40m / min, after drying, after laminating with the ...

Embodiment 3

[0045] In terms of weight percentage, weigh the following components:

[0046] (1) Flame retardant coating: add 7% aluminum hydroxide, 6.5% ammonium polyphosphate, 6.5% melamine and 0.3% wetting agent to 79.7% polyvinyl alcohol solution and mix well;

[0047](2) Flame retardant glue layer: 45% of butyl acrylate, 8% of methyl methacrylate, 5% of acrylic acid, 6% of acryl alcohol, 15% of 2-ethyl (methacrylic acid acyloxymethyl) phosphate, Melamine 6%, sodium lauryl sulfate 0.2%, mix evenly, then add initiator 3%, react at 70-90°C for 7-9h, then add latex powder 3%, nano-attapulgite 4% and continue the reaction for 1-3 hours; after cooling to normal temperature, add 4.8% curing agent, stir for 20-40 minutes, filter, and set aside;

[0048] (3) Coating flame retardant coating 15-30g / m on the white PVC layer 2 , after drying; on the other side of the white PVC layer, apply a flame-retardant glue layer of 15-30g / m 2 , the coating speed is 20-40m / min, after drying, after laminatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to digital image receiving materials, especially to water-based flame-retardant white bright back glue PVC. The water-based flame-retardant white bright back glue PVC comprises aflame-retardant coating, a white PVC layer, a flame-retardant glue layer and a release white silicon paper layer, which are arranged from top to bottom. The flame-retardant glue layer is composed ofthe following ingredients (by weight): 38-50% of butyl acrylate, 6-12% of methyl methacrylate, 2-6% of acrylic acid, 4-8% of propenol, 10-17% of a phosphorus-containing acrylic monomer, 3-8% of melamine, 0.1-0.3% of alkyl sulfate, 3-8% of a curing agent, 2-4% of an initiator, 1-5% of latex powder and 2-6% of nanometer attapulgite. The flame retardant property of the water-based flame-retardant white bright back glue PVC can reach the fireproofing grade of VTM-2, has high color reduction degree, 100% removes residual glue, and can be applied to water-based spray painting and portray printing equipment.

Description

technical field [0001] The invention relates to a digital image receiving material, in particular to a water-based flame-retardant white bright adhesive PVC and a preparation method thereof. Background technique [0002] In recent years, green and environmentally friendly products have attracted people's attention, and the government has also vigorously advocated environmental protection. More than 80% of adhesive-backed PVC products in the market today use oil-based glue, which contains carcinogenic chemical components such as benzene or releases VOC gases that are harmful to the environment. [0003] However, although PVC material does not produce open flames, it has the defect of being easy to burn, and it will also produce a lot of toxic smoke during combustion, and it is more likely to have potential combustion hazards. an important direction. But now there are some common problems with back-adhesive PVC: (1) The primer is generally a flammable substance, which makes ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/25C09J7/38C09J133/08C09J11/06C09J11/04C08F220/18C08F220/14C08F220/06C08F216/08C08F230/02C09D129/04C09D5/18
Inventor 夏厚君代树祥潘华
Owner ZHEJIANG FULAI NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products