A high-temperature-resistant resin and friction material technology, applied in friction linings, other chemical processes, chemical instruments and methods, etc., can solve problems such as unstable friction coefficient, low safety factor, poor high-temperature resistance, etc., and achieve friction coefficient The effects of improved stability, better performance, and good economic and social benefits

Inactive Publication Date: 2018-01-19
SUZHOU CUINAN ELECTRONICS TECH CO LTD
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a high temperature resistant resin-based friction material, which can solve the problems of poor high temperature resistance, unstable friction coefficient and low safety factor of the prior art friction materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A high temperature resistant resin-based friction material, comprising the following raw materials in parts by weight:

[0041] 6 parts of modified phenolic resin;

[0042] 6 parts of nitrile rubber powder;

[0043] Reinforcing fiber 4 parts,

[0044] Wherein, the reinforcing fiber is a combination of glass fiber, aramid fiber, and non-asbestos mineral fiber;

[0045] Friction modifier 10 parts,

[0046] Wherein, the friction modifier is a composition of flake graphite, artificial graphite, molybdenum disulfide, antimony trisulfide, potassium titanate whiskers, and calcium sulfate whiskers;

[0047] 2 parts of epoxy resin lubricant;

[0048] Filling 12 parts,

[0049] Wherein, the filler is a combination of silica fume, friction powder, expanded vermiculite and kaolin.

Embodiment 2

[0051] A high temperature resistant resin-based friction material, comprising the following raw materials in parts by weight:

[0052] 8 parts of modified phenolic resin;

[0053] 7 parts of nitrile rubber powder;

[0054] Reinforcing fiber 6 parts,

[0055] Wherein, the reinforcing fiber is a combination of glass fiber, aramid fiber, and non-asbestos mineral fiber;

[0056] 12 parts of friction modifier,

[0057] Wherein, the friction modifier is a composition of flake graphite, artificial graphite, molybdenum disulfide, antimony trisulfide, potassium titanate whiskers, and calcium sulfate whiskers;

[0058] 3 parts of epoxy resin lubricant;

[0059] Filling 13 parts,

[0060] Wherein, the filler is a combination of silica fume, friction powder, expanded vermiculite and kaolin.

Embodiment 3

[0062] A high temperature resistant resin-based friction material, comprising the following raw materials in parts by weight:

[0063] 10 parts of modified phenolic resin;

[0064] 8 parts of nitrile rubber powder;

[0065] Reinforcing fiber 8 parts,

[0066] Wherein, the reinforcing fiber is a combination of glass fiber, aramid fiber, and non-asbestos mineral fiber;

[0067] 14 parts of friction modifier,

[0068] Wherein, the friction modifier is a composition of flake graphite, artificial graphite, molybdenum disulfide, antimony trisulfide, potassium titanate whiskers, and calcium sulfate whiskers;

[0069] 4 parts of epoxy resin lubricant;

[0070] Filling 14 parts,

[0071] Wherein, the filler is a combination of silica fume, friction powder, expanded vermiculite and kaolin.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high temperature resistant resin-based friction material. The material is composed of the following raw materials of, by weight, 6-10 parts of modified phenolic resin, 6-8 parts of butadiene-acrylonitrile rubber powder, 4-8 parts of reinforced fibers, 10-14 parts of a friction modifier, 2-4 parts of an epoxy resin lubricant, and 12-14 parts of a filler. According to the high temperature resistant resin-based friction material provided by the invention, phenolic resin is modified through a cashew nut shell oil modifier, and the modified phenolic resin is more excellentin performance and applied to preparation of the resin-based friction material; the abrasion resistance, the high temperature resistance and the friction coefficient stability of the prepared resin-based friction material are improved; and sources of the raw materials are extensive, and the high temperature resistant resin-based friction material is applicable to industrial production and has good economical and social benefits.

Description

technical field [0001] The invention relates to the technical field of friction materials, in particular to a high temperature resistant resin-based friction material. Background technique [0002] Friction material is a component material used in power machinery that relies on friction to perform braking and transmission functions. It is widely used in automobiles, trains, aircraft and various construction machinery and equipment. Friction materials for automobiles are mainly composed of bonding, fiber reinforced materials, friction performance modifiers and fillers, which are mixed and pressed. With the development of vehicles in the direction of environmental protection, high speed and heavy load, people put forward higher requirements on the performance of automobile braking materials, especially in high temperature braking, the stability and safety of materials are very important. [0003] In the prior art, the friction material will thermally decompose when the workin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F16D69/02C09K3/14
Inventor 黄荣翠
Owner SUZHOU CUINAN ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap