Nano ion composite for wastewater treatment and preparation method of nano ion composite

A nano-ion and composite material technology, applied in the field of nano-ion composite material and its preparation, can solve problems such as low solubility, and achieve the effect of improving purification treatment efficiency and enhancing oxidative degradation ability.

Inactive Publication Date: 2018-01-23
六合天地(武汉)环境有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The solubility of ozone in water is small and it is easy to spontaneously decompose into oxygen that is ineffective for the oxidation and degradation of wastewater treatment, and the concentration of negative oxygen ions in water is usually very small. Solubility and catalytic activation of ozone decomposes into hydroxyl radicals with stronger oxidative degradation ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of nano ion composite material for waste water treatment, it is prepared by following method:

[0020] First, weigh 400g of negative ion powder, 500g of ozone-activated catalyst (manganese oxide / activated carbon, loading capacity: 0.1-0.3wt%) and 50g of solid slow-release demulsifier, then mix and fully grind until the particle size of the powder is below 0.001 μm , and then add 50g of silicone gel to the ground powder and stir and mix, and finally make pellets with a particle size of 4-8mm in a pellet machine, that is.

Embodiment 2

[0022] A kind of nano ion composite material for waste water treatment, it is prepared by following method:

[0023] First, weigh 400g of negative ion powder, 450g of ozone-activated catalyst (nickel oxide / alumina, loading capacity of 0.1-0.2wt%) and 80g of solid sustained-release demulsifier, then mix and fully grind until the particle size of the powder is below 0.001 μm , and then add 70g of silicone gel to the ground powder, stir and mix well, and finally make pellets with a particle size of 6-12mm in a pellet machine, that is.

Embodiment 3

[0025] A kind of nano ion composite material for waste water treatment, it is prepared by following method:

[0026] First, take negative ion powder 500g, ozone activation catalyst (copper oxide / activated carbon, loading capacity is 0.2-0.4wt%) 400g and solid sustained-release demulsifier 50g, then mix and fully grind until the particle size of the powder is below 0.001 μm, Then add 50g of organosilicon gel into the ground powder, stir and mix evenly, and finally prepare pellets with a particle diameter of 6-12mm in a pelletizing machine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a nano ion composite for wastewater treatment. The composite comprises the following raw materials by mass percentage: 40-50wt% of anion powder, 40-50wt% of an ozone activating catalyst, 5-8wt% of a solid slow release demulsifying agent and 5-10wt% of gel. The preparation method of the composite comprises the following steps of weighing the raw materials according to the corresponding mass percentage, mixing and sufficiently grinding the anion powder, the ozone activating catalyst and the solid slow release demulsifying agent, adding the gel of the corresponding mass to the ground powder, stirring and mixing, and finally performing pelleting in a pelleting machine. The nano ion composite has the benefits that the nano ion composite can effectively improve solubility of ozone and negative oxygen ions in water, and activate and decompose partial ozone into a hydroxyl radical with better oxidative degradation capability, and the oxidative degradation treatment efficiency of organic pollutants such as oil in wastewater is improved.

Description

technical field [0001] The invention belongs to the field of waste water treatment, and in particular relates to a nano ion composite material used for waste water treatment and a preparation method thereof. Background technique [0002] Today, the speed of sewage treatment cannot keep up with the speed of water pollution, the artificial treatment of water cannot catch up with the speed of water pollution, the understanding of viruses cannot keep up with the speed of virus mutation, the degradation of organic matter cannot keep up with the speed of organic compound synthesis, and the restoration of the earth's ecology cannot keep up with the destruction of modern economic development. Domestic wastewater has high oil content, high suspended solids, high cod, high ammonia nitrogen, and high heavy metals, which have seriously affected the living environment of surrounding people, animals and plants. If the domestic wastewater as the source of pollution cannot be properly treat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F1/78B01D17/04C02F101/30
Inventor 梁宇王德坤
Owner 六合天地(武汉)环境有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap