Tear-resistant plug connecting wire of low-voltage charger

A low-voltage charging and tear-resistant technology, applied to rubber insulators, organic insulators, etc., can solve the problem of long tear-resistant plug connecting wires, aging-resistant connecting wires, high tear-resistant requirements, and tear-resistant plug connecting wires. Adapt to people's needs and other issues, to achieve the effect of good anti-aging performance, low cost, and safe use

Inactive Publication Date: 2018-02-23
天长市平康电子科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The tear-resistant plug connecting wire of the existing low-voltage charger is relatively long. When storing, the connecting wire must be wound into shape, and when used, it is unrolled and connected to the low-voltage electrical appliance, so the aging resistance and tear resistance of the connecting wire are improved. With the fast-paced and high-efficiency modern life of people, the tear-resistant plug cables of the existing low-voltage chargers are increasingly unable to meet people's needs and need to be improved urgently.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A tear-resistant plug connection wire for a low-voltage charger, including a wire and an outer sheath, and the raw materials of the outer sheath include: 90kg of methyl vinyl silicone rubber, 60kg of natural rubber, 3kg of crosslinking agent, 4kg of zinc oxide, lauric acid 2kg, dimethyldiethoxysilane 12kg, plasticizer 4kg, hydrotalcite compound 30kg, muscovite powder 20kg, bentonite 40kg, fly ash 40kg, vermiculite powder 20kg, antioxidant 2kg.

[0016] The crosslinking agent includes: 2.5kg of cyclohexane peroxide, 1kg of vulcanization accelerator M, and 1.2kg of N,N'-m-phenylene bismaleimide. Plasticizers include: 2 kg of hydroxyl silicone oil, 4 kg of methyl epoxy acetyl linoleate. Anti-aging agents include: anti-aging agent DNP 0.5kg, anti-aging agent 2264 2.5kg.

[0017] The hydrotalcite composite is prepared by the following process: 15kg of polylactic acid, 16kg of polyethylene glycol, and 80kg of dichloromethane are stirred evenly at a temperature of 95°C, and 2...

Embodiment 2

[0019] A tear-resistant plug connection wire for a low-voltage charger, including a wire and an outer sheath, and the raw materials of the outer sheath include: 100kg of methyl vinyl silicone rubber, 40kg of natural rubber, 7kg of crosslinking agent, 2kg of zinc oxide, lauric acid 4kg, dimethyldiethoxysilane 6kg, plasticizer 8kg, hydrotalcite compound 10kg, muscovite powder 40kg, bentonite 30kg, fly ash 50kg, vermiculite powder 10kg, antioxidant 4kg.

[0020] The crosslinking agent includes: 1.5kg of cyclohexane peroxide, 3kg of vulcanization accelerator M, and 0.6kg of N,N'-m-phenylene bismaleimide. Plasticizers include: 4 kg of hydroxyl silicone oil, 2 kg of methyl epoxy acetyl linoleate. Anti-aging agents include: anti-aging agent DNP 1.3kg, anti-aging agent 2264 1.5kg.

[0021] The hydrotalcite composite is prepared by the following process: Stir 25kg polylactic acid, 8kg polyethylene glycol, and 120kg dichloromethane evenly at a stirring temperature of 85°C, add 4kg lant...

Embodiment 3

[0023] A tear-resistant plug connection wire for a low-voltage charger, including a wire and an outer sheath, the raw materials of the outer sheath include: 92g of methyl vinyl silicone rubber, 55g of natural rubber, 4g of crosslinking agent, 3.5g of zinc oxide, laurel Acid 2.5g, dimethyldiethoxysilane 10g, plasticizer 5g, hydrotalcite compound 25g, muscovite powder 25g, bentonite 38g, fly ash 42g, vermiculite powder 18g, antioxidant 2.5g.

[0024] The crosslinking agent includes: 2.2g of cyclohexane peroxide, 1.5g of vulcanization accelerator M, and 1g of N,N'-m-phenylene bismaleimide. The plasticizer includes: 2.5 g of hydroxyl silicone oil, and 3.5 g of methyl epoxyacetyl linoleate. Antiaging agents include: antiaging agent DNP 0.7g, antiaging agent 2264 2.2g.

[0025] The hydrotalcite composite was prepared by the following process: 18g polylactic acid, 14g polyethylene glycol, and 90g methylene chloride were stirred evenly at a stirring temperature of 92°C, and 2.5g lant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a tear-resistant plug connecting wire of a low-voltage charger. The tear-resistant plug connecting wire comprises a lead and an outer sheath, wherein the outer sheath comprises, by weight, 90-100 parts of methyl vinyl silicone rubber, 40-60 parts of natural rubber, 3-7 parts of cross-linking agents, 2-4 parts of zinc oxide, 2-4 parts of lauric acid, 6-12 parts of Dimethyl diethoxy silicane, 4-8 parts of plasticizers, 10-30 parts of hydrotalcite compounds, 20-40 parts of white mica powder, 30-40 parts of bentonite, 40-50 parts of coal ash, 10-20 parts of vermiculite and2-4 parts of anti-aging agents. The hydrotalcite compounds are prepared by the process: uniformly stirring polylactic acid, polyethylene glycol and dichloromethane; adding and stirring lanthanum citrate, zinc stearate and magnesium aluminum carbonate hydrotalcite; spraying epoxidized soybean oil in a stirring state; continuing stirring; adjusting a system to be neutral; removing methylene dichloride and water to obtain the hydrotalcite compounds.

Description

technical field [0001] The invention relates to the technical field of chargers, in particular to a tear-resistant plug connection wire of a low-voltage charger. Background technique [0002] The tear-resistant plug connecting wire of the existing low-voltage charger is relatively long. When storing, the connecting wire must be wound into shape, and when used, it is unrolled and connected to the low-voltage electrical appliance, so the aging resistance and tear resistance of the connecting wire are improved. With the fast-paced and high-efficiency modern life of people, the tear-resistant plug and cable of existing low-voltage chargers are increasingly unable to meet people's needs and need to be improved urgently. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a tear-resistant plug connection cable for a low-voltage charger, which not only has extremely high tensile strength and elon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L7/00C08L67/04C08L71/02C08L91/00C08K13/02C08K5/14C08K3/22C08K5/098C08K3/26H01B3/28
CPCC08K2003/2296C08L83/04C08L2201/06C08L2201/08C08L2203/202C08L2205/035C08L2312/00H01B3/28C08L7/00C08L67/04C08L71/02C08L91/00C08K13/02C08K5/14C08K3/22C08K5/098C08K3/26
Inventor 顾宜亮
Owner 天长市平康电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com