A waterproof coating and construction technology, applied in the direction of fireproof coatings, coatings, etc., can solve the problems of environmental protection not meeting the requirements, and achieve the effects of short curing time, high adhesion and cost saving

Inactive Publication Date: 2018-04-06
MAANSHAN SONGHAK INFORMATION TECH CO LTD
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the rapid development of the construction industry, its supporting coating technology is also constantly updated. Waterproof coating is one of the most popular coatings in modern society. It not only requires good waterproof performance on the wall, but also has Good flame retardant effect and high-strength adhesion ability, but the existing waterproof coating is very strong and at the same time, and due to the need for viscosity and anti-oxidation performance, it does not meet the requirements in terms of environmental protection, and contains a large amount of harmful substances such as formaldehyde

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A special waterproof coating for buildings and a preparation method thereof. The raw material components are composed of 5 parts by weight of polyurethane, 18 parts of acrylic emulsion, 4 parts of titanium dioxide, 4 parts of polyvinyl ether, and 3 parts of hydrophobic silica. 8 parts of mica powder, 13 parts of styrene-acrylate emulsion, 4 parts of sodium carboxymethyl cellulose, 3 parts of diacetone acrylamide, 4 parts of polyaramid, 3 parts of putty powder, 28 parts of ethanol.

[0013] The preparation method is as follows:

[0014] A. Add polyurethane, polyvinyl ether, hydrophobic silica and polyaramide to an appropriate amount of ethanol for copolymerization. The temperature is set to 200°C, the pressure is 1.6MPa, titanium dioxide is a catalyst, and ethanol is a solvent to obtain mixture A;

[0015] B. Mix and stir acrylic emulsion, styrene-acrylate emulsion, sodium carboxymethylcellulose and diacetone acrylamide at a stirring rate of 470r / min. After stirring, add mixtur...

Embodiment 2

[0018] A special waterproof coating for buildings and a preparation method thereof. The raw materials are composed of 5 parts by weight of polyurethane, 17 parts of acrylic emulsion, 4 parts of titanium dioxide, 3 parts of polyvinyl ether, and 2 parts of hydrophobic silica. 7 parts of mica powder, 12 parts of styrene-acrylate emulsion, 4 parts of sodium carboxymethyl cellulose, 3 parts of diacetone acrylamide, 4 parts of polyaramid, 3 parts of putty powder, and 26 parts of ethanol.

[0019] The preparation method is as follows:

[0020] A. Add polyurethane, polyvinyl ether, hydrophobic silica and polyaramide to an appropriate amount of ethanol for copolymerization, the temperature is set to 190°C, the pressure is 1.6MPa, titanium dioxide is a catalyst, ethanol is a solvent, and mixture A is obtained;

[0021] B. Mix and stir acrylic emulsion, styrene-acrylate emulsion, sodium carboxymethyl cellulose and diacetone acrylamide at a stirring rate of 460r / min. After stirring, add mixture ...

Embodiment 3

[0024] A special waterproof coating for buildings and a preparation method thereof. The raw material components are composed of 4 parts by weight of polyurethane, 20 parts of acrylic emulsion, 3 parts of titanium dioxide, 4 parts of polyvinyl ether, and 2 parts of hydrophobic silica. 10 parts of mica powder, 10 parts of styrene-acrylate emulsion, 5 parts of sodium carboxymethyl cellulose, 2 parts of diacetone acrylamide, 5 parts of polyaramid, 2 parts of putty powder, and 30 parts of ethanol.

[0025] The preparation method is as follows:

[0026] A. Add polyurethane, polyvinyl ether, hydrophobic silica and polyaramide to an appropriate amount of ethanol for copolymerization, the temperature is set to 180°C, the pressure is 1.7MPa, titanium dioxide is the catalyst, ethanol is the solvent, and mixture A is obtained;

[0027] B. Mix and stir the acrylic emulsion, styrene-acrylate emulsion, sodium carboxymethyl cellulose and diacetone acrylamide at a stirring rate of 450r / min. After sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to special waterproof paint for a building and a preparation method thereof. The special waterproof paint is prepared from the following ingredients in parts by weight: 4 to 6 parts of polyurethane, 15 to 20 parts of acrylic emulsion, 3 to 5 parts of titanium dioxide, 3 to 4 parts of polyvinylether, 2 to 3 parts of hydrophobic silica, 6 to 10 parts of mica powder, 10 to 15 parts of styrene-acrylate emulsion, 3 to 5 parts of sodium carboxymethyl cellulose, 2 to 4 parts of diacetone acrylamide, 3 to 5 parts of aromatic polyamides, 2 to 3 parts of putty powder and 25 to 30 parts of ethyl alcohol. The special waterproof paint has the advantages that the materials can be easily obtained; the anti-ultraviolet radiation is effectively realized; the oxidization resistance, aging resistance, insulation and flame retardance are realized; a surface coating is formed for achieving the waterproof effect; the paint can also seep into the substrate to form crystals so as to prevent water passing; the duplex waterproof effect is achieved; the bonding performance is high; the dispersion is uniform; the smooth degree is high; one-step coating is performed; the work efficiency is improved; the cost is reduced; the curing time is short; the application range is wide.

Description

Technical field [0001] The invention relates to the field of waterproof coatings, in particular to a special waterproof coating for buildings and a preparation method thereof. Background technique [0002] With the rapid development of the construction industry, the matching coating technology is constantly updated. Waterproof coating is one of the most popular coatings in modern society. It not only requires good waterproof performance on the wall, but also has Good flame-retardant effect and high-strength adhesion ability, but the existing waterproof coatings are very strong and take into account at the same time, and due to the needs of viscosity and oxidation resistance, they cannot meet the environmental protection requirements and contain a large amount of formaldehyde and other harmful substances . Summary of the invention [0003] The purpose of the present invention is to provide a special waterproof coating for buildings and a preparation method thereof in order to over...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/18C09D4/06C09D4/02C09D7/61C09D7/65C09D5/25
CPCC09D4/06C09D5/18
Inventor 施享
Owner MAANSHAN SONGHAK INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap