Heat-absorbing material and preparation method thereof

The technology of an endothermic material and a manufacturing method, applied in the field of materials, can solve the problems of poor applicability of the endothermic material, high cost of the preparation method, poor endothermic effect, etc., and achieves strong endothermic effect, simple preparation method, and favorable selection. effect of sexual absorption

Inactive Publication Date: 2018-04-17
NANNING KEYU ENERGY TECH CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the shortcomings of the existing technology, the heat-absorbing material has poor applicability, poor heat-absorbing effect, poor environmental protection, poor high temperature resistance, cumbersome preparation method, and high cost of the preparation method. The solution of the present invention proposes a heat-absorbing material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A heat-absorbing material, the components of the heat-absorbing material and the parts by weight of each component are as follows:

[0033] 4 parts of urea, 5 parts of borax, 30 parts of silicon nitride, 2.5 parts of carbon material, 14 parts of suspending agent, 15 parts of ammonium chloride, 3.2 parts of graphite powder, 9 parts of magnesium sulfate, 3 parts of acrylic water-absorbing resin, 5 parts of silica gel , 5.5 parts of molybdenum oxide, 1.6 parts of glass fiber, 13 parts of polyvinyl alcohol, 6 parts of titanium dioxide, 6 parts of raw gypsum powder, 5 parts of hydroxypropyl guar gum, 7 parts of hydroxypropyl cellulose, 5 parts of coconut acid diethanolamide Parts, 12 parts of hydroxypropyl phosphate distarch.

[0034] The acrylic water-absorbing resin is composed of the following raw materials in parts by weight: 8 parts of sodium hydroxide, 23 parts of acrylamide, 4 parts of acrylic acid, 6 parts of N, N-methylenebisacrylamide, and 16 parts of initiator.

...

Embodiment 2

[0044] A heat-absorbing material and its components and parts by weight of the heat-absorbing material are as follows:

[0045] 8 parts of urea, 9 parts of borax, 55 parts of silicon nitride, 3.5 parts of carbon material, 16 parts of suspending agent, 25 parts of ammonium chloride, 7.3 parts of graphite powder, 12 parts of magnesium sulfate, 10 parts of acrylic water-absorbing resin, 12 parts of silica gel, 13.5 parts of molybdenum oxide, 12.5 parts of glass fiber, 20 parts of polyvinyl alcohol, 12 parts of titanium dioxide, 12 parts of raw gypsum powder, 10 parts of hydroxypropyl guar gum, 15 parts of hydroxypropyl cellulose, 12 parts of diethanolamide cocoate , 28 parts of hydroxypropyl phosphate distarch.

[0046] As a further specific optimization of the scheme of the present invention, the acrylic water-absorbing resin is composed of the following raw materials in parts by weight: 10 parts of sodium hydroxide, 30 parts of acrylamide, 8 parts of acrylic acid, and 9 parts o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of materials and particularly relates to a heat-absorbing material and a preparation method thereof. The heat-absorbing material is prepared from the following components: 4-8 parts of urea, 5-9 parts of borax, 30-55 parts of silicon nitride, 2.5-3.5 parts of carbon material, 14-16 parts of suspending agent, 15-25 parts of ammonium chloride, 3.2-7.3 parts of graphite powder, 9-12 parts of magnesium sulfate, 3-10 parts of acrylic water-absorbent resin, 5-14 parts of silica gel, 5.5-14.5 parts of molybdenum oxide, 1.6-13.5 parts of glass fiber, 13-22parts of polyvinyl alcohol, 6-13 parts of titanium dioxide, 6-12 parts of raw gypsum powder, 5-10 parts of hydroxypropyl guar gum, 7-15 parts of hydroxypropyl cellulose, 5-12 parts of coconut diethanolamide and 12-28 parts of hydroxypropyl distarch phosphate. The heat-absorbing material disclosed by the invention has the advantages of simple preparation method, strong applicability, long service life, recyclable utilization, strong heat-absorbing effect, good environmental friendliness, no harmful-gas volatilization in the heat-absorbing process, no corrosivity and good high-temperature resistance.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a heat-absorbing material and a manufacturing method thereof. Background technique [0002] With the continuous development of human society, the contradiction between man and nature has become more and more prominent. The most prominent problems facing the world at present are environment and energy, that is, environmental degradation and energy shortage. Faced with such a situation, the governments of various countries have adopted correct countermeasures to deal with it, and the most effective method is to develop new materials and corresponding technologies. In fact, people have shown positive and effective effects on the development and utilization of solar heat absorbing materials in the past few years. The development of this new functional material can not only solve the energy shortage faced by human beings, but also not cause environmental pollution. Al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/14
Inventor 谢彤方凤才陈明贤黄可煜
Owner NANNING KEYU ENERGY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products