Graphene doped metallic oxide electrode material and preparation method thereof

An electrode material, graphite electrode technology, applied in the field of electrochemical materials, can solve the problems of reducing the specific surface area and specific capacity of graphene, graphene is easy to agglomerate, etc., achieve good market application prospects, simple preparation method, easy to operate effect

Active Publication Date: 2018-05-11
XIAMEN UNIV OF TECH
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existence of van der Waals force makes graphene easy to agglomerate, thereby reducing the specific surface area and specific capacity of graphene.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene doped metallic oxide electrode material and preparation method thereof
  • Graphene doped metallic oxide electrode material and preparation method thereof
  • Graphene doped metallic oxide electrode material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] An embodiment of the present invention provides a method for preparing a graphene-doped metal oxide electrode material, comprising the following steps:

[0033] S1, obtaining a pair of graphite electrodes and an electrolyte solution, inserting the pair of graphite electrodes into the electrolyte solution, electrifying and electrolyzing, and obtaining graphene obtained by electrolysis;

[0034] S2, dissolving Ru salt, Sn salt and Co salt in a solvent to obtain a mixed metal salt solution, wherein, in the mixed metal salt solution, the atomic ratio of Ru:Sn:Co is 4:1~4:2~4 ;

[0035] S3, in the mixed metal salt solution, add the graphene, after mixing, dry to obtain the graphene-metal salt precursor;

[0036] S4, calcining the graphene-metal salt precursor at a temperature of 220° C. to 300° C. to obtain a graphene / metal oxide composite electrode material.

[0037] Further, in step S1, the electrolyte solution is a NaCl solution with a concentration of 18-22 mg / L. The ...

Embodiment 1

[0051] A graphene-doped metal oxide electrode material provided in this embodiment is prepared according to the following steps:

[0052] (1) Insert the paired graphite electrodes into the 20mg / L NaCl electrolyte, energize for electrolysis, the energizing voltage is 10mv, the current is 0.03A, and the energizing time is 24h. After the electrolysis is completed, the extracted powder is cleaned with alcohol and put into a drying box Drying, the drying temperature is 80°C, drying for 0.5h, and the graphene is collected for use;

[0053] (2) Decompose ruthenium trichloride, tin chloride and cobalt chloride in alcohol according to the atomic ratio of Ru:Sn:Co of 4:3:3 to obtain a mixed metal salt solution;

[0054] (3) in mixed metal salt solution (the total amount of metal salt is 60mg), add 6mg graphene, after mixing, dry to obtain graphene-metal salt precursor;

[0055] (4) Keep the graphene-metal salt precursor at 230°C for 10 minutes, raise the temperature to 280°C and keep i...

Embodiment 2

[0057] A graphene-doped metal oxide electrode material provided in this embodiment is prepared according to the following steps:

[0058] (1) Insert the paired graphite electrodes into the 20mg / L NaCl electrolyte, energize for electrolysis, the energizing voltage is 10mv, the current is 0.03A, and the energizing time is 24h. After the electrolysis is completed, the extracted powder is cleaned with alcohol and put into a drying box Drying, the drying temperature is 80°C, drying for 0.5h, and the graphene is collected for use;

[0059] (2) dissolving ruthenium trichloride, tin chloride and cobalt chloride in alcohol according to the atomic ratio of Ru: Sn: Co is 4:3:3 to obtain a mixed metal salt solution;

[0060] (3) in mixed metal salt solution (the total amount of metal salt is 60mg), add 6mg graphene, after mixing, dry to obtain graphene-metal salt precursor;

[0061] (4) Keep the graphene-metal salt precursor at 230°C for 10 minutes, raise the temperature to 290°C and kee...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Login to View More

Abstract

The invention provides a graphene doped metallic oxide electrode material and a preparation method thereof, and relates to the technical field of electrochemical materials. According to the graphene doped metallic oxide electrode material, graphene is firstly prepared through an electrolysis method, then the graphene is mixed with a mixed salt solution of Ru, Sn and Co, and the mixture is calcinedat the temperature of 220 to 300 DEG C after drying, so that the graphene and metallic oxide composite electrode material is obtained. According to the graphene doped metallic oxide electrode material, metallic oxide and graphene are introduced for compounding, so that metal nanoparticles are embedded into adjacent graphene sheets, a double electric layer electrode material and a faradaic pseudocapacitance electrode material are reasonably compounded, and the material is good in electrical conductivity and chemical stability and has ideal specific capacitance.

Description

technical field [0001] The invention relates to the field of electrochemical materials, and in particular to a graphene-doped metal oxide electrode material and a preparation method thereof. Background technique [0002] Supercapacitors have high power density, short charging time, environmental protection and long cycle life, and have broad application prospects in electric vehicles, aerospace equipment, and consumer electronics. The performance of supercapacitors mainly depends on the choice of electrode materials. Metal oxides can obtain high pseudocapacitance based on their own redox reactions. Among them, ruthenium oxide has good stability and considerable pseudocapacitive characteristics, and is recognized as the best electrode material, but ruthenium is expensive, which limits its commercial applications. Reducing the raw material cost and manufacturing cost of ruthenium-containing electrodes is the key to realize its commercialization. By adding the second compone...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01G11/24H01G11/36H01G11/46B82Y30/00
CPCY02E60/13H01G11/24B82Y30/00H01G11/36H01G11/46
Inventor 麻季冬朱君秋连志翔张栋兴吴杭健张厚安
Owner XIAMEN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com