Catalyst for methane oxyhalogenation as well as preparation method and application of catalyst

A technology for methane halide oxidation and catalyst, which is applied in the field of methane halide oxidation catalyst and its preparation, and can solve the problems of low yield of halogenated methane and reduced selectivity of halogenated methane, etc.

Active Publication Date: 2018-05-25
FUSHUN RES INST OF PETROLEUM & PETROCHEMICALS SINOPEC CORP +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The methane halogen oxidation reaction in the prior art has the following technical problems. High temperature is beneficial to improve the conversion rate of methane, but it will cause deep oxidation of the generated methyl halides, especially monohalomethanes, to generate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for methane oxyhalogenation as well as preparation method and application of catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prepare aluminum hydroxide slurry by hydrolysis of aluminum isopropoxide: mix water and aluminum isopropoxide at a molar ratio of 120:1, control the hydrolysis temperature at 80°C-85°C, hydrolyze aluminum isopropoxide for 1.5h, and then carry out aging , the aging temperature was controlled at 90°C-95°C, the aging time was 18h, and an aluminum hydroxide slurry with a solid content of 21.3wt% was obtained.

[0025] Preparation of zinc-loaded alumina: use equal volume impregnation method on alumina (commercially available, the properties are as follows: L acid content is 0.2mmol g -1 ; BET specific surface is 200; pore volume is 0.3ml / g) impregnated with zinc nitrate solution, dried and roasted after impregnation, the drying time is 2h, and the drying temperature is 130°C; the roasting time is 4h, and the temperature is 400°C , the zinc-loaded alumina is spherical, and the equivalent diameter of the zinc-loaded alumina is 2 mm;

[0026] Spray immersion process: mix appro...

Embodiment 2

[0030] Prepare aluminum hydroxide slurry by hydrolysis of aluminum isopropoxide: mix water and aluminum isopropoxide at a molar ratio of 120:1, control the hydrolysis temperature at 80°C-85°C, hydrolyze aluminum isopropoxide for 1.5h, and then carry out aging , the aging temperature was controlled at 90°C-95°C, the aging time was 18h, and an aluminum hydroxide slurry with a solid content of 21.3wt% was obtained.

[0031] Preparation of zinc-loaded alumina: use equal volume impregnation method on alumina (commercially available, L acid content is 0.1mmol g -1 ;BET specific surface is 300m 2 / g; the pore volume is 0.5ml / g) impregnated with zinc sulfate solution, dried and roasted after immersion, the drying time is 3h, and the drying temperature is 120°C; the roasting time is 5h, the temperature is 450°C, the load Zinc alumina is spherical, and the equivalent diameter of zinc-loaded alumina is 2mm;

[0032] Spray immersion process: mix appropriate amount of zirconium sulfate s...

Embodiment 3

[0036] Prepare aluminum hydroxide slurry by hydrolysis of aluminum isopropoxide: mix water and aluminum isopropoxide at a molar ratio of 120:1, control the hydrolysis temperature at 80°C-85°C, hydrolyze aluminum isopropoxide for 1.5h, and then carry out aging , the aging temperature was controlled at 90°C-95°C, the aging time was 18h, and an aluminum hydroxide slurry with a solid content of 21.3wt% was obtained.

[0037] Preparation of zinc-loaded alumina: using equal volume impregnation method on alumina (commercially available, the properties are as follows: L acid content is 0.05 mmol g -1 ;BET specific surface is 250m 2 / g; pore volume is 0.3 ~ 0.6ml / g, preferably 0.4ml / g,) impregnated with zinc bromide solution, dried and roasted after impregnated, the drying time is 4h, and the drying temperature is 100°C; The calcination time is 4 hours, the temperature is 500°C, the zinc-loaded alumina is spherical, and the equivalent diameter of the zinc-loaded alumina is 3mm;

[0038...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Equivalent diameteraaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a catalyst for methane oxyhalogenation as well as a preparation method and an application of the catalyst. The core of the catalyst is zinc supported alumina, wherein content of alumina L acid is smaller than 0.2 mmol.g<-1>; BET specific surface area is 200-350m<2>/g; pore volume is 0.3-0.6 ml/g; the shell is alumina containing zirconium sulfate solid acid and a molecular sieve, and the molecular sieve is at least one of a 5A molecular sieve, a 13X molecular sieve and a mordenite molecular sieve; the weight ratio of zinc supported alumina to alumina containing zirconiumsulfate solid acid and the molecular sieve is 10:1-2:1; based on the weight of alumina containing zirconium sulfate solid acid and the molecular sieve as the baseline, the weight content of zirconiumsulfate solid acid is 8wt%-15wt%, and the content of the molecular sieve is 3wt%-7wt%; based on the weight of zinc supported alumina as the baseline, content of zinc in terms of oxide is 5wt%-30wt%.The catalyst has the advantages that methane conversion rate and selectivity of halomethane as a target product are increased simultaneously, deep oxidation of halomethane is inhibited, and yield of halomethane is increased obviously.

Description

technical field [0001] The invention relates to a methane halogen oxidation catalyst and its preparation method and application, in particular to a low-temperature high-activity, selective methane halogen oxidation conversion catalyst and its preparation method and application. Background technique [0002] Methane does not directly react with halogen, but uses HCl, HBr or metal halide as a halogen source, and the process of reacting with the participation of oxygen to form halide is called halogen oxidation reaction. This method was first applied to the industrial production of chlorine by catalytic oxidation of HCl, known as the Deacon process. [0003] The early methane halogen oxidation reaction mainly used HCl as the halogen source, and the catalyst mainly used CuCl 2 As the active component, Bromhead et al. (Bromhead J, Font-Freide J J, Westlake D J. Process for the production of methyl or ethyl mono-chloride or bromide. EP. Patent, 0117731.1984-09-05) loaded CuCl on ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J29/08B01J29/18B01J29/70C07C17/154C07C19/075
CPCB01J29/087B01J29/185B01J29/7053B01J35/0073C07C17/154C07C19/075
Inventor 张信伟李杰尹泽群刘全杰倪向前
Owner FUSHUN RES INST OF PETROLEUM & PETROCHEMICALS SINOPEC CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap