Washing-resistant rubber lining for cyclone and preparation method thereof

A kind of erosion-resistant, cyclone technology, applied in the direction of the cyclone device, the device in which the axial direction of the cyclone can be reversed, etc. Effect

Inactive Publication Date: 2018-06-12
北京中选耐磨设备有限公司平顶山分公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem in the prior art that the inner wall of the cyclone is easily worn due to erosion, the invention provides a scour-resistant rubber lining for the cyclone and a preparation method thereof, the rubber lining is arranged on the inner wall of the cyclone , so that the pulp directly impacts on the rubber lining, which protects the inner wall of the cyclone, and the rubber lining is easy to replace after damage, which greatly prolongs the service life of the cyclone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An erosion-resistant rubber lining for a cyclone. According to the weight ratio, the rubber lining is based on 85 parts of nitrile rubber and 50 parts of butadiene rubber, and 5 parts of polyurethane fiber filaments, 6 parts of carbon fiber and 8 parts of polyester Amide fiber is the skeleton fiber, with 10 parts of sepiolite powder, 4 parts of carbon black, 6 parts of nano-alumina powder as filler, 5 parts of aluminate coupling agent, 1 part of liquid coumarone and 3 parts 1 part of modified additive is used as an admixture, and mixed with 12 parts of wear-resistant auxiliary agent, 2 parts of vulcanizing agent BPO and 2 parts of accelerator DM. Among them, the wear-resistant auxiliary agent is composed of nitrile rubber powder, phthalate Dioctyl formate, aluminum oxide, succinic acid and KH580 are mixed in a weight ratio of 16:0.8:2:4:1; the modified additives are KH570, nano-aluminum hydroxide, acetone and barium hydroxide according to 3 :0.8:3:0.5 weight ratio mixed...

Embodiment 2

[0052] An erosion-resistant rubber lining for a cyclone. According to the weight ratio, the rubber lining is based on 90 parts of nitrile rubber and 60 parts of butadiene rubber, and 7 parts of polyurethane fiber filaments, 8 parts of carbon fiber and 12 parts of polyester Amide fiber is the skeleton fiber, with 12 parts of sepiolite powder, 5 parts of carbon black, 8 parts of nano-alumina powder as filler, 8 parts of aluminate coupling agent, 3 parts of liquid coumarone and 4 parts The modification additive of one part is used as an admixture, and mixed with 16 parts of wear-resistant auxiliary agent, 4 parts of vulcanizing agent BPO and 3 parts of accelerator DM, wherein, the wear-resistant auxiliary agent is composed of nitrile rubber powder, phthalate Dioctyl formate, aluminum oxide, succinic acid and KH580 are mixed in a weight ratio of 20:1.2:3:6:2; the modified additives are KH570, nano-aluminum hydroxide, acetone and barium hydroxide according to 4 :1:4:0.6 weight rati...

Embodiment 3

[0071] An erosion-resistant rubber lining for a cyclone. According to the weight ratio, the rubber lining is based on 88 parts of nitrile rubber and 55 parts of butadiene rubber, and 6 parts of polyurethane fiber filaments, 7 parts of carbon fiber and 10 parts of polyester Amide fiber is the skeleton fiber, with 11 parts of sepiolite powder, 4.5 parts of carbon black, 7 parts of nano-alumina powder as filler, 6.5 parts of aluminate coupling agent, 2 parts of liquid coumarone and 3.5 parts The modified additive of one part is used as an admixture, and mixed with 14 parts of wear-resistant auxiliary agent, 3 parts of vulcanizing agent BPO and 2.5 parts of accelerator DM, wherein, the wear-resistant auxiliary agent is composed of nitrile rubber powder, phthalate Dioctyl formate, aluminum oxide, succinic acid and KH580 are mixed in a weight ratio of 18:1:2.5:5:1.5; the modified additives are KH570, nano-aluminum hydroxide, acetone and barium hydroxide according to 3.5 :0.9:3.5:0.5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a washing-resistant rubber lining for a cyclone and a preparation method thereof. The rubber lining is prepared by taking the nitrile rubber and butadiene rubber as matrix, taking polyurethane cellosilk, carbon fiber and polyamide fiber as the skeleton fiber, taking the sepiolite powder, carbon black and nano-aluminum oxide powder as filler, taking a aluminic ester couplingagent, liquid coumarone resin and modifying additive as the additive, and mixing the raw materials with anti-wearing auxiliary, a sulfurizing agent BPO and DM, wherein the anti-wearing auxiliary is prepared by mixing nitrile rubber powder, dioctyl phthalate, aluminium oxide, succinic acid and KH580; the modifying additive is prepared by mixing KH570, nanometer aluminum hydroxide, acetone and barium hydroxide. By arranging the rubber lining on the inner wall of the cyclone, thus the ore pulp directly impacts on the rubber lining, and the aim of protecting the inner wall of the cyclone is achieved; the rubber lining is easy to change after being damaged, and the service life of the cyclone is greatly prolonged.

Description

technical field [0001] The invention relates to a cyclone used in the mineral processing field, in particular to a scour-resistant rubber lining for a cyclone and a preparation method thereof. Background technique [0002] The cyclone is a common separation and classification equipment, and the principle of centrifugal sedimentation is commonly used. When the two-phase mixed liquid to be separated enters the cyclone tangentially from the periphery of the cyclone at a certain pressure, a strong three-dimensional elliptical strong rotational shear turbulent movement is generated. Due to the difference in particle size between coarse particles and fine particles, they are subjected to centrifugal force, centripetal buoyancy, fluid drag, etc., and are subjected to centrifugal sedimentation. Most of the coarse particles are discharged through the bottom flow port of the cyclone, while most of the fine particles are discharged from The overflow pipe is discharged, so as to achiev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L9/00C08L75/04C08L77/00C08L45/02C08L63/00C08L3/02C08K13/06C08K9/06C08K9/04C08K9/02C08K9/10C08K7/26C08K3/04C08K3/22C08K5/12C08K7/28C08K3/36B04C5/085B29B7/28
Inventor 王畅杜刚刚肖敏宋鹏远高明帅
Owner 北京中选耐磨设备有限公司平顶山分公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products