Dental resin adhesive containing unsaturated fatty acid polyphenolamide derivatives

A technology of unsaturated fatty acids and resin adhesives, which is applied in dental preparations, dentistry, dental prostheses, etc., can solve problems such as the decrease in the bonding strength between resin adhesives and dentin, and achieve inhibition of metal matrix protease activity, adhesion High bonding strength and good stability

Active Publication Date: 2020-10-23
CHENGDU JIAODA MEDICAL SCI & TECH COMPANY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As the resin-bonded restoration is used in the oral cavity for a long time, the bonding strength of the resin cement to the dentin will decrease significantly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dental resin adhesive containing unsaturated fatty acid polyphenolamide derivatives
  • Dental resin adhesive containing unsaturated fatty acid polyphenolamide derivatives
  • Dental resin adhesive containing unsaturated fatty acid polyphenolamide derivatives

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A dental resin adhesive containing unsaturated fatty acid polyphenol amide derivatives is composed of core functional monomers, auxiliary functional monomers, an initiating system and a solvent.

[0024] The mass ratio of each component: 20 parts of core functional monomer, 50 parts of auxiliary functional monomer, 10 parts of initiating system, 20 parts of solvent;

[0025] The core functional monomer in this example is N-(3,4-dihydroxyphenethyl)methacryloyl;

[0026] The auxiliary functional monomer in this example is methacryloyloxyethyl phosphorylcholine;

[0027] The initiation system of this example is a mixture of camphorquinone and dimethylaminoethyl methacrylate, wherein the mass ratio of camphorquinone and dimethylaminoethyl methacrylate is 5:3.

[0028] The solvent in this example is a mixture of ethanol and water, wherein the volume ratio of ethanol and water is 9:1.

[0029] The core functional monomer, the auxiliary functional monomer and the initiator s...

Embodiment 2

[0037] A dental resin adhesive containing unsaturated fatty acid polyphenol amide derivatives is composed of core functional monomers, auxiliary functional monomers, an initiating system and a solvent.

[0038] The mass ratio of each component: 70 parts of core functional monomer, 20 parts of auxiliary functional monomer, 10 parts of initiating system, 25 parts of solvent;

[0039] The core functional monomer is N-(3,4-dihydroxyphenethyl)acrylamide.

[0040] The auxiliary functional monomer is methacryloyloxyethyl phosphorylcholine.

[0041] The initiation system of this example is a mixture of camphorquinone and dimethylaminoethyl methacrylate, wherein the mass ratio of camphorquinone and dimethylaminoethyl methacrylate is 5:3.

[0042] The solvent in this example is a mixture of ethanol and water, wherein the volume ratio of ethanol and water is 9:1.

[0043] The core functional monomer, the auxiliary functional monomer and the initiator system of this example are dissolve...

Embodiment 3

[0045]A dental resin adhesive containing unsaturated fatty acid polyphenol amide derivatives is composed of core functional monomers, auxiliary functional monomers, an initiating system and a solvent.

[0046] The mass ratio of each component: 20 parts of core functional monomer, 70 parts of auxiliary functional monomer, 15 parts of initiation system, and 15 parts of solvent;

[0047] The core functional monomer in this example is N-3,4-dihydroxybenzoyloxyethyl methacrylamide

[0048] The auxiliary functional monomer in this example is acryloyloxyethylphosphorylcholine.

[0049] The initiation system of this example is a mixture of camphorquinone and dimethylaminoethyl methacrylate, wherein the mass ratio of camphorquinone and dimethylaminoethyl methacrylate is 5:3.

[0050] The solvent in this example is a mixture of ethanol and water, wherein the volume ratio of ethanol and water is 9:1.

[0051] The core functional monomer, the auxiliary functional monomer and the initiat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a dental resin adhesive containing unsaturated fatty acid polyphenolic amide derivatives. The dental resin adhesive is prepared from 20-70 parts by mass of core functional monomers, 20-70 parts by mass of an auxiliary functional monomer, 10-30 parts by mass of an initiating system and a dissolved quantity of solvent, wherein the core functional monomers comprise N-(3,4-dihydroxyphenethyl) methacrylamide, N-(3,4-dihydroxyphenethyl) acrylamide, N-3,4-dihydroxybenzoyloxy ethyl methacrylamide, N-3,4-dihydroxybenzoyloxy ethyl acrylamide, N-3,4,5-trihydroxybenzyl methacrylamide, N-3,4,5-trihydroxybenzyl acrylamide, N-3,4,5-trihydroxybenzoyloxy methacrylamide and the like; the auxiliary functional monomer is methacryloyloxyethyl phosphorylcholine or acryloyloxyethyl phosphorylcholine. The dental resin adhesive is high in adhesion strength and good in stability.

Description

technical field [0001] The present invention relates to an adhesive, in particular to a dental resin adhesive. Background technique [0002] The minimally invasive restoration of tooth defects based on composite resin bonding is one of the characteristics of the development of modern dentistry. Composite resin not only has good wear resistance, but also has excellent color, which is close to the color of tooth tissue after curing; and has good immediate and short-term bonding effect; widely used in restoration. [0003] Dentin is composed of about 50% (volume fraction) of inorganic matter and 30% (volume fraction) of organic matter, and the organic matter mainly contains a large amount of type I collagen fibers. During resin bonding, the dentin is first removed to expose the collagen fiber network, and the resin penetrates into the collagen fiber network to solidify, that is, a "hybrid layer" is formed. This mechanical locking force is the main component of the bonding for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K6/887
CPCA61K6/887C08L33/26
Inventor 李全利赵元聪
Owner CHENGDU JIAODA MEDICAL SCI & TECH COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com