A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide and its products and applications

A nickel hydroxide, in-situ preparation technology, applied in metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, catalyst activation/preparation and other directions, can solve problems such as expensive equipment, achieve low cost, The structure is stable and the effect of avoiding the use of adhesives

Active Publication Date: 2021-02-09
CHONGQING UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ex-situ bonding presents problems with bond firmness, while vapor deposition requires expensive equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide and its products and applications
  • A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide and its products and applications
  • A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide and its products and applications

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide, comprising the steps of:

[0032] (1) Preparation of multilevel carbon-based acicular nanowire / needle arrays:

[0033] a. Put the cut carbon cloth in acetone, sonicate it for 15 minutes, and put it in alcohol for 15 minutes to remove impurities on the surface of the commercial carbon cloth, and rinse it with deionized water until the carbon cloth becomes super hydrophilic and obtains a hydrophilic water carbon cloth;

[0034] b. 6.5g disodium hydrogen phosphate (Na 2 HPO 4 ) and 5.8g sodium dihydrogen phosphate (NaH 2 PO 4 ) was dissolved in 200mL deionized water to obtain a phosphate buffer solution;

[0035] c. Add 1.4 mL of pyrrole to the phosphate buffer solution prepared in step b, and then ultrasonically treat the solution to fully disperse the pyrrole in the solution to obtain an electrodeposition electrolyte;

[0036] d. use the hydrophilic carbon cloth obtained in step...

Embodiment 2

[0041] A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide, comprising the steps of:

[0042] (1) Preparation of polypyrrole nanowires on carbon cloth:

[0043] a. Put the cut carbon cloth in acetone, sonicate it for 15 minutes, and put it in alcohol for 15 minutes to remove impurities on the surface of the commercial carbon cloth, and rinse it with deionized water until the carbon cloth becomes super hydrophilic and obtains a hydrophilic water carbon cloth;

[0044] b. 6.5g disodium hydrogen phosphate (Na 2 HPO 4 ) and 5.8g sodium dihydrogen phosphate (NaH 2 PO 4 ) was dissolved in 200mL deionized water to obtain a phosphate buffer solution;

[0045] c. Add 1.4 mL of pyrrole to the phosphate buffer solution in step b, and then ultrasonically treat the solution to fully disperse the pyrrole in the solution to obtain an electrodeposition electrolyte;

[0046]d. the hydrophilic carbon cloth processed with step a is used as a working elect...

Embodiment 3

[0051] A kind of in-situ preparation method of multi-level carbon-based iron-nickel hydroxide, comprising the steps of:

[0052] (1) Preparation of polypyrrole nanowires on carbon cloth:

[0053] a. Put the cut carbon cloth in acetone, sonicate it for 15 minutes, and put it in alcohol for 15 minutes to remove impurities on the surface of the commercial carbon cloth, and rinse it with deionized water until the carbon cloth becomes super hydrophilic and obtains a hydrophilic water carbon cloth;

[0054] b. 6.5g disodium hydrogen phosphate (Na 2 HPO 4 ) and 5.8g sodium dihydrogen phosphate (NaH 2 PO 4 ) was dissolved in 200mL deionized water to obtain a phosphate buffer solution;

[0055] c. Add 1.4 mL of pyrrole to the phosphate buffer solution in step b, and then ultrasonically treat the solution to fully disperse the pyrrole in the solution to obtain an electrodeposition electrolyte;

[0056] d. the hydrophilic carbon cloth processed with step a is used as a working elec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
electric potential / voltageaaaaaaaaaa
electric potential / voltageaaaaaaaaaa
Login to View More

Abstract

The invention relates to an in-situ preparation method of multi-level carbon-based iron-nickel hydroxide and its products and applications. The method uses an electrochemical method to in-situ grow polypyrrole nanowire / needle arrays on carbon cloth, and heat treatment to obtain carbon The multilevel carbon-based acicular nanowire / needle array as the substrate is then loaded with iron-nickel hydroxide in situ; the method is simple and low in cost, and the prepared multilevel carbon-based nanoneedle / wire array has a large specific surface area, The morphology is controllable, the oxygen evolution catalytic performance is good, and it can be widely used in the field of energy storage and conversion.

Description

technical field [0001] The invention belongs to the field of self-supporting catalytic materials, and relates to an in-situ preparation method of multi-level carbon-based iron-nickel hydroxide; it also relates to products and applications prepared by the method. Background technique [0002] In order to improve the conductivity of catalytic materials and increase the number of loading sites, some micro-nano-sized carbon materials (such as carbon nanotubes, graphene, carbon microspheres, etc.) are mixed with catalysts and then bonded with large-scale substrate materials. Non-in-situ growth methods, such as Park first loading graphene oxide on the melamine foam frame, high-temperature carbonization, and then supporting catalysts; there are also some in-situ growth methods using chemical vapor deposition, such as Ekspong, nitrogen-doped carbon nanotubes through Catalytic chemical vapor deposition directly grown on carbon fiber paper for catalyst loading. Ex-situ bonding has is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/755B01J35/06B01J37/08B01J37/10B01J37/34H01M4/90
CPCH01M4/9083B01J23/755B01J37/084B01J37/10B01J37/348B01J35/58B01J35/33Y02E60/50
Inventor 李猛张立阳邹婧王佳程孙宽周永利
Owner CHONGQING UNIV