Heat-resistant wear-resistant steel plate and production method thereof

A production method and steel plate technology, applied in the field of metal materials, can solve problems such as lack of heat resistance and wear resistance, inability to carry out continuous casting production, and difficult quality assurance, and achieve the effects of low internal stress, convenient cost, and low cost

Inactive Publication Date: 2018-08-14
ANGANG STEEL CO LTD
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] This type of heat-resistant and wear-resistant steel plate has formed multiple patents at home and abroad, such as CN1026901C, CN104611641ACN103205650A, CN101746089A, CN103342020A, EP3015561 A, US2015 / 0184270 A1, etc.; And Ni, W, Mo and other alloys have high content, high cost and cannot be produced by continuous casting; 2. It needs to be produced by specific production methods such as bimetallic casting, vacuum composite or surfacing welding. The process is complicated, special production equipment is required, and the quality is not easy Guarantee; 3. The residual internal stress of the steel plate after quenching is prone to cracks; 4. The hardness decreases after high temperature tempering, and it does not have heat resistance and wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistant wear-resistant steel plate and production method thereof
  • Heat-resistant wear-resistant steel plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention will be further described below in conjunction with specific examples.

[0032] According to chemical composition of the present invention and production technology, the actual chemical composition of smelting steel grade of the present invention is as table 1, and the actual rolling process parameter of steel example of the present invention is as table 2, and the hot-rolled state of steel example of the present invention and in 250~500 See Table 3 for the actual hardness at °C.

[0033] The smelting composition example of the steel grade of the present invention of table 1, Wt%

[0034]

[0035] P≤0.015%, S≤0.005%

[0036] The actual rolling process parameter of table 2 steel example of the present invention

[0037]

[0038] Table 3 The hardness of steel embodiment of the present invention

[0039] serial number

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a heat-resistant wear-resistant steel plate and a production method thereof. The heat-resistant wear-resistant steel plate consists of the following components in percentage byweight: 0.33%-0.40% of C, 0.2%-0.4% of Si, 0.80%-1.00% of Mn, 0.5-0.7% of Cr, 0.2-0.4% of Mo, 0.015%-0.03% of Nb, 0.0005-0.0022% of B, 0.10%-0.20% of Ti, 0.015%-0.045% of Als and the balance of Fe and inevitable impurities; and impurity elements in steel are controlled as follows: less than or equal to 0.015% of P, less than or equal to 0.005% of S, less than or equal to 0.0040% of [N] and less than or equal to 0.0020% of [O]. According to the heat-resistant wear-resistant steel plate and the production method thereof provided by the invention, the steel plate has surface hardness greater than HB400 after being tempered at a temperature lower than 500 DEG C; the production method is simple, and does not need special compound equipment; and residual stress is low, cracks are not liable togenerate, components are simple and common, and the cost is low.

Description

technical field [0001] The invention belongs to the field of metal materials, and relates to a heat-resistant and wear-resistant steel plate and a production method thereof, which can be used in the manufacture of wear-resistant equipment or components whose ambient temperature is not higher than 500°C. Background technique [0002] In recent years, low and medium alloy wear-resistant steels have achieved rapid development due to their simpler production process, better wear resistance and economical characteristics. This type of wear-resistant steel is mainly produced by quenching or quenching plus low-temperature tempering The heat treatment process obtains low-carbon martensite or its low-temperature tempered structure, which ensures that the steel plate has good wear resistance. In terms of composition design, a certain carbon content is generally used to ensure the hardenability of the steel plate. At the same time, an appropriate amount of chromium, molybdenum, and Nic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/22C22C38/26C22C38/32C22C38/28C22C38/06C21D8/02
CPCC21D8/0226C21D8/0263C21D2211/008C22C38/02C22C38/04C22C38/06C22C38/22C22C38/26C22C38/28C22C38/32
Inventor 张涛侯华兴林田子杨颖张哲
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products