Near-infrared fluorescent powder as well preparation method and application thereof

A fluorescent powder and near-infrared technology, which is applied in the direction of fluorescence/phosphorescence, chemical instruments and methods, luminescent materials, etc., can solve the problem that the emission spectrum cannot meet the use requirements, etc., and achieves the convenience of large-scale production and popularization and application, and the preparation time is short , the effect of long excitation wavelength

Active Publication Date: 2018-09-14
HEBEI UNIVERSITY
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the new broadband infrared LED launched by Osram Opto Semiconductors applied phosphor technology to infrared emitters for the first time, created infrared spectroscopy technology suitable for the consumer market, and applied it to the food industry, agriculture and other industries to measure moisture in food , fat, carbohydrate, sugar or protein content, etc.; however, this technology relies on near-infrared phosphors that can emit a broad spectrum, and most of the emission spectra of current near-infrared phosphors do not meet the requirements for their use. Therefore, the industry's It is necessary for R&D personnel to develop more near-infrared phosphors with a wide emission spectrum, to provide more material options for near-infrared phosphors required by Osram light beads, and to provide near-infrared phosphors for food detection, biological detection, and biological imaging. More options

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Near-infrared fluorescent powder as well preparation method and application thereof
  • Near-infrared fluorescent powder as well preparation method and application thereof
  • Near-infrared fluorescent powder as well preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Weigh the raw materials according to the following weights: Weigh 0.8047g of magnesium oxide (MgO), gallium oxide (Ga 2 O 3 ) 1.2496g, chromium trioxide (Cr 2 O 3 )0.0025g and germanium oxide (Ge 2 O 3 ) 0.6976g, mix evenly, place it in an agate mortar and grind it for 30 minutes to obtain a mixture;

[0026] (2) Place the ground mixture powder in a small crucible, heat up to 1260°C at a heating rate of 5°C / min, sinter at this temperature for 4 hours, and cool to room temperature naturally to obtain a sintered body;

[0027] (3) The obtained sintered body is cooled to room temperature and then fully polished to obtain a chemical formula of Mg 2.995 Ga 2 Cr 0.005 GeO 8 Of near-infrared phosphors.

Embodiment 2

[0029] (1) Weigh the raw materials according to the following weights: Weigh 0.8033g magnesium oxide (MgO), gallium oxide (Ga 2 O 3 ) 1.2496g, chromium trioxide (Cr 2 O 3 ) 0.0051g and germanium oxide (Ge 2 O 3 ) 0.6976g, mix evenly, place it in an agate mortar and grind it for 30 minutes to obtain a mixture;

[0030] (2) Place the ground mixture powder in a small crucible, heat up to 1260°C at a heating rate of 5°C / min, sinter at this temperature for 4 hours, and cool to room temperature naturally to obtain a sintered body;

[0031] (3) The obtained sintered body is cooled to room temperature and then fully polished to obtain a chemical formula of Mg 2.99 Ga 2 Cr 0.01 GeO 8 Of near-infrared phosphors.

Embodiment 3

[0033] (1) Weigh the raw materials according to the following weights: respectively weigh 0.7979g of magnesium oxide (MgO), gallium oxide (Ga 2 O 3 ) 1.2496g, chromium trioxide (Cr 2 O 3 ) 0.0152g and germanium oxide (Ge 2 O 3 ) 0.6976g, mix evenly, place it in an agate mortar and grind it for 30 minutes to obtain a mixture;

[0034] (2) Place the ground mixture powder in a small crucible, heat up to 1260°C at a heating rate of 5°C / min, sinter at this temperature for 4 hours, and cool to room temperature naturally to obtain a sintered body;

[0035] (3) The obtained sintered body is cooled to room temperature and then fully polished to obtain a chemical formula of Mg 2.97 Ga 2 Cr 0.03 GeO 8 Of near-infrared phosphors.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses near-infrared fluorescent powder. A chemical general formula of the near-infrared fluorescent powder is Mg(3-x)Ga2CrxGeO8, wherein x is greater than 0 and is smaller than or equal to 0.1. The invention also discloses a preparation method of the near-infrared fluorescent powder. The preparation method comprises the following steps: weighing oxide or carbonate containing elements of Mg, Ga, Cr and Ge according to molar proportions of all elements in the chemical general formula Mg(3-x)Ga2CrxGeO8 of the near-infrared fluorescent powder, mixing, and grinding, thus obtaininga mixture; heating the mixture to 1200 to 1300 DEG C, and roasting for 3 to 4 hours, thus obtaining a sintered body; cooling the sintered body to room temperature, and fully grinding, thus obtainingthe near-infrared fluorescent powder. Meanwhile, the invention discloses application of the near-infrared fluorescent powder. The near-infrared fluorescent powder provided by the invention has longerexcitation wavelength and cannot be easily absorbed by a living body, an emission spectrum is in wide spectrum emission, the wavelength covers 700 to 1200nm which can cover one part of a first windowand a second window of a body biological window, the luminous strength is high, the stability is high, the preparation technology of the near-infrared fluorescent powder is simple, operation and control are easy, the safety is high, the preparation time is short, and the near-infrared fluorescent powder is convenient for large-scale production as well as popularization and application.

Description

Technical field [0001] The invention relates to a luminescent material and a preparation method and application thereof, in particular to a near-infrared phosphor and a preparation method and application thereof. Background technique [0002] The near-infrared light region is a non-visible light region that people discovered earlier. Due to the low level of early technology, the spectrum overlap and the analysis are complicated due to the influence of frequency multiplication and frequency combination, which leads to certain restrictions on the research and application of near-infrared light. Until the 1960s, the emergence of commercial instruments and the large amount of work done by Norris et al. put forward the theory that the content of the substance is linearly related to the absorption peaks of multiple different wavelength points in the near-infrared region, and uses NIR diffuse reflection technology The determination of moisture, protein, fat and other components in agric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/68F21V9/40G01N21/64
CPCC09K11/681F21V9/40G01N21/64
Inventor 戴丹婕李盼来王志军杨志平
Owner HEBEI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com