Coating composition containing acrylic acid body hybrid emulsion

A composition, acrylic technology, applied in the field of coatings, can solve the problems of marine biological variation, huge damage to the marine environment, etc., and achieve the effect of preventing adhesion

Inactive Publication Date: 2018-09-21
深圳市前海星火同为科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Then, toxic substances such as organotin can easily cause marine organisms to mutate, which is extremely harmful to the marine environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] (1) Put xylene accounting for 50% of the total amount into a four-necked reaction flask equipped with a dropping funnel, a spherical condenser, a water separator and a thermometer, and heat up to reflux;

[0035] (2) After mixing all the monomers evenly, put them in the dropping funnel, dissolve 20% of the total amount of azobisisobutyronitrile in xylene and mix them evenly;

[0036] (3) After the normal reflux of xylene for 10 minutes, add the mixed monomers and azobisisobutyronitrile (30% of the total) dropwise, and finish dropping within 3 hours;

[0037] (4) After refluxing for 2 hours, add the remaining azobisisobutyronitrile;

[0038] (5) Continue reflux and heat preservation for 2 hours, measure the technical control index of the resin, when the acid value is less than or equal to 10mgKOH / g, distill part of the xylene and release it from the water separator;

[0039] (6) Add butyl acetate, modifier and fluorine-containing ternary copolymer resin, continue to hea...

Embodiment 2

[0054] Method is with embodiment 1, and the parts by weight of each raw material are as follows:

[0055] Styrene 1 Azobisisobutyronitrile 0.5

[0056] Acrylic butyric acid 10 Modifier 0.5

[0057] Methacrylic acid 0.2 Fluorinated ternary copolymer resin 10

[0058] Methyl methacrylate 15 Hydroxyethyl methacrylate 5

[0059] Titanium dioxide 15 UV absorber 5060 0.1

[0060] Butyl acetate 2 Xylene 2

[0061] Iron red 5 Aluminum tripolyphosphate 10

[0062] Modified zinc phosphate 10 Defoamer 0.1

[0063] Dispersant 0.1 1250 mica powder 15.

Embodiment 3

[0065] Method is with embodiment 1, and the parts by weight of each raw material are as follows:

[0066] Styrene 5 Azobisisobutyronitrile 2

[0067] Acrylic Butyric Acid 12 Modifier 2

[0068] Methacrylic acid 2 Fluorinated ternary copolymer resin 20

[0069] Methyl methacrylate 20 Hydroxyethyl methacrylate 15

[0070] Titanium dioxide 25 UV absorber 5060 0.4

[0071] Butyl acetate 4 Xylene 6

[0072] Iron red 15 Aluminum tripolyphosphate 15

[0073] Modified Zinc Phosphate 20 Defoamer 1

[0074] Dispersant 2 1250 mica powder 20.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
adhesivityaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of coatings, and particularly relates to a coating composition containing an acrylic acid body hybrid emulsion. The coating composition is prepared from styrene, azobisisobutyronitrile, acrylic acid butyric acid, a modifier, methyl methacrylate, methacrylic acid, fluorine-containing ternary copolymer resin, hydroxyethyl methacrylate, titanium dioxide, an ultraviolet light absorber 5060, butyl acetate, xylene, iron oxide red, aluminum tripolyphosphate, modified zinc phosphate, an antifoaming agent, a dispersant and 1250 mica powder. The coating composition has the advantages that by means of the coating, marine organisms can be effectively prevented from adhering to the bottom of a ship, the variation cannot be caused to the marine organisms, andthe damage cannot be caused to the marine environment.

Description

technical field [0001] The invention belongs to the technical field of coatings, in particular to a coating composition containing an acrylic bulk hybrid emulsion. Background technique [0002] Marine biofouling is becoming more and more serious. However, marine biofouling has not yet been resolved. The fouling of attached organisms mainly refers to the attachment of organisms, mainly algae and shellfish, to the surface of marine facilities, affecting the normal operation of equipment. Taking ships as an example, marine organisms attach to the bottom of the ship, causing huge resistance when the ship is running, reducing the speed of the ship, and consuming a lot of energy at the same time. The study found that for the 10,000-ton ship, the fouling of the ship's bottom reached about 5%, and the fuel consumption increased by about 10%, which caused huge economic losses due to the adhesion of marine organisms to the bottom of the ship. [0003] In order to prevent the attach...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D127/12C09D5/16C09D7/61C08F220/14C08F220/20C08F220/18C08F220/06C08F212/08
CPCC08F220/14C08K2003/2241C08K2003/327C09D5/1662C09D5/1687C09D133/066C08L27/12C08K3/22C08K3/32C08K3/34C08F220/20C08F220/1804C08F220/06C08F212/08
Inventor 车春玲
Owner 深圳市前海星火同为科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com