High-intensity waterproof underground pipe culvert and production method thereof

A high-strength, pipe-culvert technology, applied in the field of concrete pipe culverts, can solve the problems affecting the durability, impermeability and crack resistance of concrete pipes and steel cylinder concrete pipes, poor compactness and flexibility, poor impact resistance, and bending resistance. Low tensile strength and deformation ability, etc., to achieve high impregnation efficiency, excellent mechanical properties, and good durability

Inactive Publication Date: 2018-09-28
ANHUI YUTE CONCRETE STRUCTURE TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary pipe culverts are made of cement concrete. Cement concrete is a typical brittle material with low bending and tensile strength and deformation capacity, and weak fatigue and external erosion resistance. The pipe culvert made of cement concrete has the internal There will be more void structures. After the pipe culvert is in a humid environment for a long time, the internal void structure will increase, and even cracks will appear. Alkaline liquid corrosion, in this environment for a long time, will cause the mechanical strength of the pipe culvert to plummet, and then lead to water seepage in the underground pipe culvert
Therefore, there are great requirements for the strength and waterproof performance of underground pipe culverts, and in the prior art, the waterproof performance of underground pipe culverts is relatively poor
[0003] At present, the production of concrete pipe culverts is to use a certain proportion of ordinary Portland cement as the cementitious material, and coarse and fine aggregates such as sand and stone, add an appropriate amount of water reducing agent, and add water to stir in a mixer to form ordinary concrete. Concrete pipes and steel cylinder concrete pipes, due to the brittleness of ordinary concrete, have poor compactness, flexibility, and impact resistance under external forces, and are prone to inner wall cracks, which affect the durability of concrete pipes and steel cylinder concrete pipes resistance, impermeability and crack resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A high-strength waterproof underground pipe culvert in this embodiment is made of the following raw materials in parts by weight: 10 parts of modified carbon fiber, 30 parts of wollastonite, 8 parts of mineral fiber, 15 parts of barium sulfate, 30 parts of talcum powder, 3 parts of salicylic acid, 3 parts of dimethylformamide, 2 parts of toughening agent, 80 parts of water;

[0022] Among them, the particle size of talcum powder and barium sulfate is 2000 mesh; the mineral fiber is magnesium sulfate whisker with a diameter of 10um; Carbon fiber, polytetrafluoroethylene / polyvinylidene fluoride dispersion is a colloidal solution formed by mixing polytetrafluoroethylene resin and polyvinylidene fluoride resin with an average particle size of 0.4 μm and suspending them in liquid water according to a mass ratio of 1:1. And the viscosity of the colloidal solution is 0.04Pas, the concentration is 55wt%, and the pH value is 9; the relative molecular weight of polytetrafluoroeth...

Embodiment 2

[0025] A high-strength waterproof underground pipe culvert in this embodiment is made of the following raw materials in parts by weight: 20 parts of modified carbon fiber, 60 parts of wollastonite, 16 parts of mineral fiber, 35 parts of barium sulfate, 50 parts of talcum powder, 10 parts of salicylic acid, 7 parts of dimethylformamide, 5 parts of toughening agent, 180 parts of water;

[0026] Among them, the particle size of talcum powder and barium sulfate is 3000 mesh; the mineral fiber is aluminum borate whisker with a diameter of 16um; Carbon fiber, polytetrafluoroethylene / polyvinylidene fluoride dispersion is a colloidal solution formed by mixing polytetrafluoroethylene resin and polyvinylidene fluoride resin with an average particle size of 0.5 μm and suspending them in liquid water according to a mass ratio of 1:1. And the viscosity of the colloidal solution is 0.04Pas, the concentration is 55wt%, and the pH value is 10; the relative molecular weight of polytetrafluoroe...

Embodiment 3

[0029] A high-strength waterproof underground pipe culvert in this embodiment is made of the following raw materials in parts by weight: 15 parts of modified carbon fiber, 45 parts of wollastonite, 12 parts of mineral fiber, 25 parts of barium sulfate, 40 parts of talcum powder, 6 parts of salicylic acid, 5 parts of dimethylformamide, 3.5 parts of toughening agent, 130 parts of water;

[0030] Among them, the particle size of talcum powder and barium sulfate is 2500 mesh; the mineral fiber is a mixture of magnesium sulfate whisker, silicon oxide whisker, aluminum borate whisker and glass fiber with a diameter of 13um; the modified carbon fiber is carbon fiber through polytetrafluoroethylene Modified carbon fibers obtained after impregnating the vinyl fluoride / polyvinylidene fluoride dispersion, the average particle size of the polytetrafluoroethylene / polyvinylidene fluoride dispersion is

[0031] 0.4-0.5μm polytetrafluoroethylene resin and polyvinylidene fluoride resin are mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
crystallinityaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-intensity waterproof underground pipe culvert and a production method thereof, and relates to the technical field of concrete pipe culverts. The high-intensity waterproofunderground pipe culvert is made of the following raw materials: modified carbon fibers, wollastonite, mineral fibers, barium sulfate, talcum powder, sulfosalicylic acid, dimethylformamide, a flexibilizer and water. The high-intensity waterproof underground pipe culvert is high in mechanical performance, and high in tensile intensity and folding resistance, and is capable of inhibiting visible cracks, caused by shrinkage of the pipe culvert, in the inner wall; the pipe culvert is high in permeating resistance, high in cracking resistance, high in durability, and long in service life; the modified carbon fibers are uniform to disperse in a substrate; the produced pipe culvert is obviously high in abrasion resistance and remains outstanding in mechanical performance.

Description

technical field [0001] The invention relates to the technical field of concrete pipe culverts, in particular to a high-strength waterproof underground pipe culvert and a preparation method thereof. Background technique [0002] Culvert refers to a culvert constructed with reinforced concrete box-shaped pipe joints. Underground pipe culvert refers to a pipe buried below the surface, which is cast with reinforced concrete, commonly known as cement pipe, and is generally used as a water diversion pipe under a cofferdam dam. Ordinary pipe culverts are made of cement concrete. Cement concrete is a typical brittle material with low bending and tensile strength and deformation capacity, and weak fatigue and external erosion resistance. The pipe culvert made of cement concrete has the internal There will be more void structures. After the pipe culvert is in a humid environment for a long time, the internal void structure will increase, and even cracks will appear. Alkaline liquid ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/18C04B20/10
CPCC04B28/188C04B20/1033C04B14/386C04B14/383C04B14/368C04B14/042C04B24/16C04B24/124C04B22/002C04B2103/0068C04B14/42
Inventor 肖吕阳
Owner ANHUI YUTE CONCRETE STRUCTURE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products