Check patentability & draft patents in minutes with Patsnap Eureka AI!

A kind of b/l acid-modified organosilicon ball catalyst and its preparation and application

A catalyst and organosilicon technology, applied in B/L acid-modified organosilicon ball catalyst and its preparation and application field

Active Publication Date: 2020-09-04
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no report on this type of catalyst and its application in the decomposition of cyclohexyl hydroperoxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of b/l acid-modified organosilicon ball catalyst and its preparation and application
  • A kind of b/l acid-modified organosilicon ball catalyst and its preparation and application
  • A kind of b/l acid-modified organosilicon ball catalyst and its preparation and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Catalyst M-S-BIM-SiO 2 preparation

[0016] The preparation of the organosilicon spheres modified by the B / L acid can be operated in the following steps:

[0017] First, add 100mL of methanol, 10mL of ammonia water with a mass fraction of 28% and 30mL of deionized water into a 250mL three-necked flask, stir mechanically for 30 minutes and mix them uniformly, then drop 3.36g of ethyl orthosilicate and 0.19g of 3-chloro The precursor of propyltriethoxysilane was stirred at 60°C for 3 hours, centrifuged and washed with water to prepare organosilicon spheres for catalysts. Suspend 2 g of the prepared silicone spheres in 30 mL of toluene solution, drop excess 0.2 g of diimidazopropane into it, reflux at 120° C. for 12 hours, centrifuge and wash with water to prepare bis-imidazolidinyl-modified silicone spheres. Suspend 2 g of the prepared bis-imidazolidinyl-modified silicone spheres in 50 mL of toluene solution, add 0.35 g of excess 1,4-butane sultone dropwise into the sus...

Embodiment 2

[0019] Catalyst Cu-S-BIM-SiO 2 preparation

[0020] Heterogeneous Catalyst Cu-S-BIM-SiO 2 The preparation method and M-S-BIM-SiO in Example 1 2 The preparation is the same, the difference is that the transition metal chloride salt used is CuCl 2 .

Embodiment 3

[0022] Catalyst Co-S-BIM-SiO 2 preparation

[0023] Heterogeneous Catalyst Co-S-BIM-SiO 2 The preparation method and M-S-BIM-SiO in Example 1 2 The preparation is the same, the difference is that the transition metal chloride salt used is CoCl 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the preparation and application of a B / L acid modified organosilicon sphere catalyst. According to the invention, a cyclohexane solution of cyclohexyl hydroperoxide is used asa raw material and a B / L acid-modified organosilicon sphere is used as a catalyst to achieve high-efficiency decomposition of cyclohexyl hydroperoxide under mild conditions, so cyclohexanol and cyclohexanone are produced. The catalyst has high selectivity to cyclohexanol and cyclohexanone, and can be recycled.

Description

technical field [0001] The invention relates to a method for preparing cyclohexanol and cyclohexanone by decomposing cyclohexyl hydroperoxide under alkali-free conditions using nanometer silicon balls wrapped with silicon source modified by Bronsted acid and Lewis acid as catalyst. Background technique [0002] The oxidation of cyclohexane to cyclohexanol and cyclohexanone (K / A oil) is an important petrochemical process. At present, cyclohexane oxidation mainly adopts a two-step method. First, cyclohexane is oxidized without catalyst under high temperature conditions to produce cyclohexyl hydroperoxide, and then, under the catalysis of sodium hydroxide and cobalt salt, it is decomposed to produce cyclohexanol and cyclohexanone. The sodium hydroxide added in this method generates a large amount of alkaline waste water to pollute the environment and cause corrosion to the equipment. It is of great scientific significance and application background to develop a new type of al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J31/02C07C27/00C07C35/08C07C45/53C07C49/303
CPCB01J31/0284C07C27/00C07C45/53C07C35/08C07C49/303
Inventor 郑玺徐杰孙志强高进杜文强石松
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com