Waterproof self-cleaning silicone resin coating and preparation method thereof

A technology of resin coating and silicone, which is applied in the field of coatings, can solve the problems that the protection cannot meet people's requirements, and achieve the effect of good waterproof effect, good elasticity and high curing density

Inactive Publication Date: 2018-10-16
TONGCHENG HUIQI IND & TRADE
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of industry, the variety of coatings is increasing, and the quality and performance are constantly improving. The simple protection of coatings can no longer meet people's requirements. Especially in people's daily life, waterproof and moisture-proof are getting more and more attention.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A waterproof self-cleaning silicone resin coating, made of the following raw materials in parts by weight: 20 parts of polymethylphenyl silicone resin, 15 parts of fluorosilane, 5 parts of silane coupling agent, 2 parts of nano titanium dioxide, palygorskite 6 parts, 8 parts of carbon fiber, 8 parts of nano-calcium carbonate, 10 parts of kaolinite, 3 parts of carbon nanotubes, 25 parts of demineralized water, 2 parts of thickener, 2 parts of dispersant, 2 parts of hydrophobic agent, film-forming aid 1 serving.

[0022] The particle size of the palygorskite and kaolinite is 500-100 mesh.

[0023] The dispersant is prepared by mixing zinc EDTA and dodecafluoroheptyl methacrylate in a mass ratio of 2:1.

[0024] The film-forming aid is propylene glycol methyl ether acetate.

[0025] The hydrophobic agent is polysiloxane-polyalkoxy ether copolymer or silicone resin.

[0026] The waterproof self-cleaning silicone resin coating is prepared by the following steps:

[0027]...

Embodiment 2

[0031] A waterproof self-cleaning silicone resin coating, made of the following raw materials in parts by weight: 30 parts of polymethylphenyl silicone resin, 18 parts of fluorosilane, 7 parts of silane coupling agent, 7 parts of nano titanium dioxide, palygorskite 10 parts, 12 parts of carbon fiber, 12 parts of nano-calcium carbonate, 15 parts of kaolinite, 8 parts of carbon nanotube, 35 parts of demineralized water, 5 parts of thickener, 7 parts of dispersant, 6 parts of hydrophobic agent, film-forming aid 3 copies.

[0032] The particle size of the palygorskite and kaolinite is 500-100 mesh.

[0033] The dispersant is prepared by mixing zinc EDTA and dodecafluoroheptyl methacrylate in a mass ratio of 2:1.

[0034] The film-forming aid is propylene glycol methyl ether acetate.

[0035] The hydrophobic agent is polysiloxane-polyalkoxy ether copolymer or silicone resin.

[0036] The waterproof self-cleaning silicone resin coating is prepared by the following steps:

[0037...

Embodiment 3

[0041] A waterproof self-cleaning silicone resin coating, made of the following raw materials in parts by weight: 25 parts of polymethylphenyl silicone resin, 16 parts of fluorosilane, 6 parts of silane coupling agent, 4.5 parts of nano titanium dioxide, palygorskite 8 parts, 10 parts of carbon fiber, 10 parts of nano calcium carbonate, 13 parts of kaolinite, 5.5 parts of carbon nanotube, 30 parts of demineralized water, 3.5 parts of thickener, 5 parts of dispersant, 4 parts of hydrophobic agent, film-forming aid 2 servings.

[0042] The particle size of the palygorskite and kaolinite is 500-100 mesh.

[0043] The dispersant is prepared by mixing zinc EDTA and dodecafluoroheptyl methacrylate in a mass ratio of 2:1.

[0044] The film-forming aid is propylene glycol methyl ether acetate.

[0045] The hydrophobic agent is polysiloxane-polyalkoxy ether copolymer or silicone resin.

[0046] The waterproof self-cleaning silicone resin coating is prepared by the following steps: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses waterproof self-cleaning silicone resin coating. The coating is prepared from the following raw materials in parts by weight: 20 to 30 parts of polymethylphenyl organic siliconresin, 15 to 18 parts of fluoroalkyl silane, 5 to 7 parts of a silane coupling agent, 2 to 7 parts of nanometer titania, 6 to 10 parts of palygorskite, 8 to 12 parts of carbon fiber, 8 to 12 parts ofnanometer calcium carbonate, 10 to 15 parts of kaolinite, 3 to 8 parts of carbon nanometer tube, 25 to 35 parts of softened water, 2 to 5 parts of a thickening agent, 2 to 7 parts of a dispersing agent, 2 to 6 parts of a water repellent agent, and 1 to 3 parts of a coalescing agent. The coating formed by the polymethylphenyl organic silicon resin, the fluoroalkyl silane and the silane coupling agent is good in waterproof effect. The added nanometer titania ensures that the coating has a self-cleaning function, and meanwhile is matched with the palygorskite, carbon fiber, nanometer calcium carbonate and kaolinite, the curing density is extremely high, the surface smoothness is extremely high, dust in the air cannot be adhered to the surface of the coating, and the aesthetic degree is good.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a waterproof self-cleaning silicone resin coating and a preparation method thereof. Background technique [0002] Paint is a kind of liquid or fixed material that is coated on the surface of an object and forms a thin film under certain conditions to play a protective, decorative and specific role. It has been widely used in daily life. With the development of industry, the variety of coatings is increasing day by day, and the quality and performance are constantly improving. The simple protection of coatings can no longer meet people's requirements. Especially in people's daily life, waterproof and moisture-proof are getting more and more attention. [0003] Waterproof coating refers to a kind of coating that the coating film formed by coating can prevent rainwater or groundwater from seeping. The waterproof film formed after the waterproof coating is cured has certain extensibility, e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D5/16C09D5/14C09D7/61C09D7/63C09D7/65
CPCC09D4/06C09D5/14C09D5/1675C09D5/1687
Inventor 王宇
Owner TONGCHENG HUIQI IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com