Degradable sanitary brush bristle and production method thereof

A production method and sanitation technology, applied in the manufacture of rayon, conjugated rayon, conjugated synthetic polymer rayon, etc., can solve the problems of waste of energy resources, environment, pollution, environmental and health hazards, and achieve easy Oxidative degradation, low price, effect of improving mechanical properties and thermal properties

Inactive Publication Date: 2018-11-02
安徽古皖刷业有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to excessive use and inadequate recycling and other reasons, worn-out sanitation brush filaments will cause serious waste of energy resources and environmental pollution, and bring great harm to people's living environment and health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A degradable sanitation brush filament of the present invention is made of the following raw materials in parts by weight:

[0023] 85-95 parts of polyethylene, 15-20 parts of plant fiber, 0.4-0.8 parts of lubricant, 0.1-0.5 parts of coupling agent, and 1-5 parts of additives; the additives include foaming agent masterbatch.

[0024] Further, the foaming agent masterbatch includes the following raw materials in parts by weight: 90 parts of polypropylene and 5-10 parts of foaming agent.

[0025] Further, the foaming agent is selected from one or more of azodicarbonamide, azobisisobutyronitrile and p-toluenesulfonylsemicarbazide.

[0026] The above-mentioned production method of a degradable sanitation brush filament comprises the following steps:

[0027] a Weighing the raw materials of the above-mentioned proportioning;

[0028] b Mix polyethylene, plant fiber, lubricant, coupling agent and foaming agent masterbatch, melt the mixed raw materials, and spin through an e...

Embodiment 2

[0038] A degradable sanitation brush filament of the present invention is made of the following raw materials in parts by weight:

[0039] 85 parts of polyethylene, 15 parts of plant fiber, 0.4 part of lubricant, 0.1 part of coupling agent, and 1 part of additive; the additive includes foaming agent masterbatch.

[0040] Further, the foaming agent masterbatch includes the following raw materials in parts by weight: 90 parts of polypropylene and 5 parts of foaming agent.

[0041] Further, the foaming agent is selected from one or more of azodicarbonamide, azobisisobutyronitrile and p-toluenesulfonylsemicarbazide.

[0042] The above-mentioned production method of a degradable sanitation brush filament comprises the following steps:

[0043] a Weighing the raw materials of the above-mentioned proportioning;

[0044] b Mix polyethylene, plant fiber, lubricant, coupling agent and foaming agent masterbatch, melt the mixed raw materials, and spin through an extruder;

[0045] c li...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a degradable sanitary brush bristle. The degradable sanitary brush bristle is prepared from the following raw materials in parts by weight: 85-95 parts of polyethylene, 15-20 parts of plant fiber, 0.4-0.8 part of a lubricant, 0.1-0.5 part of a coupling agent and 1-5 parts of an additive, wherein the additive comprises a foaming agent masterbatch. Through addition of the foaming agent masterbatch into polypropylene, the degradable sanitary brush bristle is good in heat stability, relatively high in tensile strength and impact strength and excellent in microwave adaptability, has the advantages of light weight, heat insulation, cushioning, anticorrosion, high specific strength, low price and the like, and has greatly improved mechanical properties and heat performance; the added coupling agent is easily oxidatively degraded, so that the degradable sanitary brush bristle has a fully-degradable function; through addition of the plant fiber, the degradable sanitary brush bristle has a good environment-friendly effect. The invention further discloses a production method of the degradable sanitary brush bristle.

Description

technical field [0001] The invention relates to the technical field of sanitation brush filaments, in particular to a degradable sanitation brush filament and a production method thereof. Background technique [0002] Sanitation brushes are brushes used for cleaning, mainly disc brushes or steel wire disc brushes, which are most commonly seen on street sweepers. With the vigorous development of urban cleaning work in our country, sanitation brushes have sprung up like mushrooms after rain. At present, the filaments of most sanitation brushes on the market are made of nylon, polyester, and polyolefin, which have a wide range of raw materials and high cost performance. After the sanitation brush is worn out, it is generally necessary to replace it with a new sanitation brush. Due to reasons such as excessive use and inadequate recycling, worn-out sanitation brush filaments will cause serious waste of energy resources and environmental pollution, and bring great harm to peopl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F8/06D01F8/18D01F1/10
CPCD01F1/10D01F8/06D01F8/18
Inventor 阮德旭阮德全黄光源
Owner 安徽古皖刷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products