A technology for volleyball leather and astringency is applied in the field of high-astringency volleyball leather and its preparation, which can solve the problems of stiff hand, high production cost, complicated process and the like, and achieves simple and controllable method, long service life and good repeatability. Effect

Inactive Publication Date: 2018-11-16
HUALUN LEATHER & PLASTIC SUZHOU
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

They have sulfides, chlorides, chromium compounds, phthalates, DMF waste water and waste gas emissions in the production process. Although people have been recycling them, it is difficult to meet the requirements of environmental protection and cause great harm to people.
Moreover, volleyball leather usually has high production cost, complicated process, and is difficult to process. At present, volleyball leather is made by embossing the surface of ordinary PU leather. slips off easily after volleyball

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for preparing volleyball leather with high astringency, comprising the steps of:

[0023] 1) According to parts by weight PU: 80 parts; wood flour: 1 part; color paste: 5 parts; stabilizer: 0.5 parts; After stirring evenly, apply it evenly on the base cloth at a speed of 9 m / min and a coating thickness of 1.05 mm. After solidification, wash with water and dry. The solidification time is 10 minutes, and the drying temperature is 150°C. Prepare the PU layer;

[0024] 2) Mix the astringent surface treatment agent and butanone at a weight ratio of 1:1, stir evenly, and use a roller coater to roll-coat the above liquid on the PU layer. The speed is controlled at 8 m / min. ℃ drying, drying time is 2 minutes, coiling after drying to make semi-finished volleyball leather;

[0025] 3) Mix 8 parts by weight of astringent surface treatment agent, 1 part by weight of methyl ethyl ketone, and 3 parts by weight of color paste, stir evenly, and use a printing machine to prin...

Embodiment 2

[0027] A method for preparing volleyball leather with high astringency, comprising the steps of:

[0028] 1) According to parts by weight PU: 95 parts; wood powder: 3 parts; color paste: 9 parts; stabilizer: 1 part; After stirring evenly, apply it evenly on the base cloth, the speed is 11 m / min, the coating thickness is 1.15mm, after solidification, wash with water and dry, the solidification time is 15 minutes, and the drying temperature is 100°C. Prepare the PU layer;

[0029] 2) Mix the astringent surface treatment agent and butanone at a weight ratio of 1:1, stir evenly, and use a roller coater to roll coat the above liquid on the PU layer. The speed is controlled at 10 m / min. ℃ drying, drying time is 3 minutes, coiling after drying, made into semi-finished volleyball leather;

[0030] 3) Mix 12 parts by weight of astringent surface treatment agent, 2 parts by weight of methyl ethyl ketone, and 5 parts by weight of color paste, stir evenly, and use a printing machine to ...

Embodiment 3

[0032] A method for preparing volleyball leather with high astringency, comprising the steps of:

[0033] 1) According to parts by weight PU: 100 parts; wood flour: 6 parts; color paste: 10 parts; After stirring evenly, apply it evenly on the base cloth at a speed of 10 m / min and a coating thickness of 1 mm. After solidification, wash with water and dry. The solidification time is 12 minutes, and the drying temperature is 130°C. Prepare the PU layer;

[0034] 2) Mix the astringent surface treatment agent and butanone at a weight ratio of 1:1, stir evenly, and use a roller coater to roll coat the above liquid on the PU layer. The speed is controlled at 12 m / min. ℃ drying, drying time is 2 minutes, coiling after drying to make semi-finished volleyball leather;

[0035] 3) Mix 10 parts by weight of astringent surface treatment agent, 1 part by weight of methyl ethyl ketone, and 2 parts by weight of color paste, stir evenly, and use a printing machine to print the above liquid o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-acerbity volleyball leather and a preparation method thereof. The volleyball leather sequentially comprises: a base cloth; a PU layer comprising, by weight, 80-100 partsof PU, 1-6 parts of wood powder, 5-10 parts of a color paste, 0.5-3 parts of a stabilizer and 40-55 parts of a solvent; and an acerbic finishing layer from bottom to top. The preparation method of thehigh-acerbity volleyball leather has the advantages of simplicity, controllability, good repeatability, and obtaining of a volleyball leather material with excellent performances, and the volleyballleather product prepared through the method has the advantages of soft surface, high acerbity, excellent elasticity, good hand feeling, good wearing resistance and long service life.

Description

technical field [0001] The invention relates to the technical field of preparation of synthetic leather, in particular to a volleyball leather with high astringency and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, the improvement of physical fitness is closely linked with health, and various sports are entering people's lives, which puts forward higher requirements for the quality of sports balls. Because of its simplicity and convenience, volleyball has become more and more popular among people. At present, the materials of volleyball include genuine leather and imitation leather, and the ball leather made of polyvinyl chloride (PVC) and polyurethane (PU) is widely used in the market. They have sulfides, chlorides, chromium compounds, phthalates, and DMF wastewater and waste gas emissions during the production process. Although people have already recycled them, it is difficult to meet the requirements of en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/14D06N3/00
CPCD06N3/0056D06N3/0059D06N3/0061D06N3/0063D06N3/0077D06N3/0088D06N3/14D06N2209/1635D06N2209/1685D06N2211/28
Inventor 吕培军高金岗高国华张卫松
Owner HUALUN LEATHER & PLASTIC SUZHOU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap