Preparation method of fiber rubber type shock-absorbing material

A shock-absorbing material, rubber-type technology, applied in the field of shock-absorbing material preparation, can solve the problems of not meeting market requirements, poor impact resistance, poor shock absorption, etc., to suppress abnormal grain growth and improve impact resistance. , the effect of suppressing dislocation motion

Inactive Publication Date: 2018-11-20
吴伟华
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention: Aiming at the defects of poor impact resistance, poor shock absorption performance and poor heat dissipation in the current common shock absorbing materials, which cannot meet the market requirements, a preparation method of fiber rubber type shock absorbing materials is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Weigh 80-100g loofah pulp and put it into a beaker with 145-160mL deionized water and wash it for 10-12 minutes to remove impurities to obtain washed loofah pulp, then put the washed loofah pulp in an oven at a temperature of 85-90°C Dry for 21 to 24 minutes under certain conditions, grind and pulverize for 16 to 20 minutes after drying, and discharge to obtain loofah granules; according to the mass ratio of 1:3, mix and stir the loofah granules and sodium hydroxide solution with a mass fraction of 18% for 24 After ~32 minutes, take out the filtrate and remove the filtrate to obtain the filter residue, which is the modified loofah granule. Continue to put the modified loofah granule into the muffle furnace, and carbonize it at a temperature of 270-300°C under nitrogen protection for 45-55 minutes. Cool and discharge to obtain self-made activated carbon; mix and grind silicon carbide and silicon nitride for 10-12 minutes according to the mass ratio of 3:1 to obtain mixed ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a fiber rubber type shock-absorbing material and belongs to the technical field of preparation of shock-absorbing materials. The preparation method comprises the following steps: firstly, mixing and grinding silicon carbide and silicon nitride to obtain mixed powder; then melting and spinning the mixed powder to obtain self-made mixed fibers. As in asystem, the self-made mixed fibers are connected through staggered base material molecular chains, the surface of the vegetable sponge is modified by means of an alkaline solution, so that cutin andwax coats on the surfaces of cell walls of the vegetable sponge are removed favorably, and the extent of crystallization and polymerization of cellulose is reduced. In addition, the modified vegetablesponge particles are carbonized to prepare self-made activated carbon. Once being impacted by an external force, segmental motions of a base material are constrained by means of the self-made activated carbon. By adding trimethylolpropane trimethacrylate continuously and carrying out high-temperature irradiation crosslinking modification, twining and interaction among the molecular chains of thebase material are improved, so that the base material has higher cell density and more uniform pore distribution, and therefore, the heat dissipating property of the shock-absorbing material is further improved. The material has a wide application prospect.

Description

technical field [0001] The invention discloses a preparation method of a fiber rubber type shock absorbing material, which belongs to the technical field of shock absorbing material preparation. Background technique [0002] With the rapid development of modern industry, vibration and noise have become serious problems in various fields, which will reduce the operating accuracy, affect product quality, shorten product life, make high-precision instruments not work normally, endanger safety, and make equipment or construction Early destruction of objects, environmental pollution and impact on human health. In order to prevent the noise and vibration produced by automobiles, home appliances and other vehicles and industrial machinery, in addition to reducing or eliminating the vibration of the vibration source, it is more practical to develop and utilize various shock-absorbing products, among which rubber shock-absorbing products are particularly important. Part. The elasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L23/06C08K7/10C08K3/04C08J3/28C08J3/24
CPCC08L9/06C08J3/24C08J3/28C08J2309/06C08J2423/06C08L23/06C08K7/10C08K3/04
Inventor 吴伟华赵必花朱彩娣
Owner 吴伟华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products