A kind of aqueous PVDF-coated lithium-ion battery diaphragm and preparation method thereof

A lithium-ion battery, water-based technology, applied in the preparation of lithium-ion battery diaphragm, the field of water-based PVDF-coated lithium-ion battery diaphragm, can solve the problem of poor adhesion, uneven island size, easy to block ion channels, etc. Problems, to achieve the effect of improving process capability, increasing air permeability, and improving the positive and negative interface of the battery cell

Active Publication Date: 2021-05-25
JIANGSU QINGTAO ENERGY TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating of the microgravure preparation process is relatively dense, which is easy to block the ion channel
The coating prepared by the spraying process is distributed in a discrete island shape, with uneven thickness, uneven island size, and poor final adhesion effect
Acrylic glue and polyacrylonitrile polymer, due to the large swelling, should strictly control the shape distribution, which will easily lead to blockage of ion channels, so it is rarely used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aqueous PVDF-coated lithium-ion battery diaphragm and preparation method thereof
  • A kind of aqueous PVDF-coated lithium-ion battery diaphragm and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A lithium-ion battery diaphragm coated with water-based PVDF of the present invention is composed of a lithium-ion battery base film and a coating on one or both sides of the base film, the coating is composed of PVDF slurry, and the PVDF slurry The composition and mass parts are: PVDF is 9 parts of polyvinylidene fluoride copolymer; water-based UV curable resin is preferably 15 parts of UP resin; water-based binder is preferably 4 parts of acrylic polymer; thickener is carboxymethyl Base cellulose is preferably 0.6 parts; water is 63 parts; photoinitiator is preferably benzophenone, preferably 7 parts; auxiliary agent is 0.09 parts of dispersant, and 1 part of polymerization inhibitor.

[0025] Among them, the polyvinylidene fluoride copolymer of PVDF has a molecular weight of 500,000-800,000 and a particle size of 150nm-300nm.

[0026] The lithium-ion battery base film is a polyethylene film with a thickness of 5um and a porosity of 36%.

[0027] A preparation method...

Embodiment 2

[0032] A lithium-ion battery diaphragm coated with water-based PVDF of the present invention is composed of a lithium-ion battery base film and a coating on one or both sides of the base film, the coating is composed of PVDF slurry, and the PVDF slurry The composition and mass parts are: PVDF is 8 parts of polyvinylidene fluoride copolymer; the water-based UV curable resin is preferably 17 parts of PUA resin; the water-based binder is preferably 5 parts of acrylic polymer; the thickener is methylol The base cellulose is preferably 0.8 parts; the water is 60 parts; the photoinitiator is preferably a carbonyl compound, preferably 8 parts; the auxiliary agent is 0.09 parts of a dispersant, and the polymerization inhibitor is 2 parts.

[0033] The PVDF is a polyvinylidene fluoride copolymer with a molecular weight of 500,000-800,000 and a particle size of 150nm-300nm.

[0034] The lithium ion battery base film is a polypropylene film with a thickness of 15um and a porosity of 40%....

Embodiment 3

[0040] A lithium-ion battery diaphragm coated with water-based PVDF of the present invention is composed of a lithium-ion battery base film and a coating on one or both sides of the base film, the coating is composed of PVDF slurry, and the PVDF slurry The composition and mass parts are: PVDF is polyvinylidene fluoride copolymer, 6 parts; water-based UV curing resin is EA resin, preferably 15 parts; water-based binder is acrylic polymer, preferably 2 parts; thickener is attapulgite Clay is preferably 1 part; water is 65 parts; photoinitiator is preferably azo compound, preferably 6 parts; auxiliary agent is 0.09 parts of dispersant, and polymerization inhibitor is 2.5 parts.

[0041] The lithium-ion battery base film is a polyimide film with a thickness of 25um and a porosity of 45%.

[0042] A preparation method of a water-based PVDF-coated lithium-ion battery diaphragm, the preparation steps of which are: a. Add the dispersant and attapulgite clay in the auxiliary agent to 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
porosityaaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a water-based PVDF-coated lithium-ion battery diaphragm. The preparation steps are: adding a dispersant and a thickener to water, stirring evenly, adding PVDF, and merging the PVDF into water to prepare a suspension Add water-based UV resin, water-based binder, photoinitiator, polymerization inhibitor to the remaining water, disperse evenly, then import PVDF suspension, disperse evenly to prepare PVDF slurry; PVDF slurry is coated on corona One or both sides of the treated lithium-ion battery base film form a dot-matrix distributed coating, and cure the finished product. The advantages are: using water-based UV light curing technology, the coating can be dried immediately, with lower energy consumption, and there is no need to worry about the deformation of the diaphragm due to heat and tension. The drying time of the diaphragm coating can be reduced to 8‑15s, which is conducive to continuous and stable mass production.

Description

technical field [0001] The invention relates to the technical field of lithium-ion batteries, in particular to an aqueous PVDF-coated lithium-ion battery diaphragm, and to a preparation method of the aqueous PVDF-coated lithium-ion battery diaphragm. Background technique [0002] Compared with steel-shell and aluminum-shell batteries, lithium-ion soft-pack batteries have the advantages of light weight, large capacity, small internal resistance, flexible design, and safety. They are widely used in 3C consumer electronics and power battery products. However, there is no hard shell on the interface between the positive and negative electrodes of the battery. During the charge and discharge process, due to the expansion of graphite, deformation is easy to occur. When deformation occurs, the interface between the positive and negative electrodes is likely to be unstable, resulting in poor battery performance. [0003] At present, in order to improve the interface between the posi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M50/449H01M50/403H01M10/0525
CPCH01M10/0525H01M50/403H01M50/409Y02E60/10
Inventor 李峥冯玉川席健陈雷杨帆南策文
Owner JIANGSU QINGTAO ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More