Alkaline residue cement superfine powder and preparation method thereof

A technology of ultra-fine powder and cement, applied in the field of cement ultra-fine powder, which can solve the problems of polluting groundwater resources and achieve the effects of improving cement quality, reducing water consumption, and increasing production

Inactive Publication Date: 2018-11-23
淮安市水泥厂有限公司 +1
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Purpose of the invention: The purpose of the invention is to solve the problems of stacking and landfilling a large number of salt chemical waste residues and alkali residues, seriously polluting groundwater resources, etc., and provide a cement super-combined powder with low production cost and good product performance and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Superfine cement powder, calculated by mass percentage, 98% of the waste residue and alkali slag discharged after the production of industrial lime by salt chemical industry, calculated by mass percentage as dechlorination agent, 2% is 100% as raw material, after mixing and stirring evenly, it is made into micro The fine particles are 1-2mm, stacked and solidified, sent to the drying kiln to dry at 100 degrees to remove free water and crystal water, that is, the cement superfine powder product, and finally the specific surface area is greater than 400-500㎡ / kg of cement superfine powder, used to replace 40-50% of cement products, can advance the setting time of cement products by 20-40 minutes, increase the hydration strength of cement products by 8-12mpa, and increase the specific surface area of ​​cement products by 100-150㎡ / kg , can reduce the water consumption of cement products by 15-30%, improve the wear resistance of cement products by 10-15 times, increase the co...

Embodiment 2

[0017] Cement superfine powder, calculated by mass percentage, is 99% of waste residue and alkali slag discharged after the production of industrial lime by salt chemical industry, calculated by mass percentage as dechlorination agent, 1% is 100% as raw material, after mixing and stirring evenly, it is made into micro fine powder The particles are 1-2mm, stacked and solidified, sent to the drying kiln to dry at 100 degrees to remove free water and crystal water, and then get superfine cement powder products, and finally grind to make the specific surface area greater than 400-500㎡ / kg cement superfine powder. Used to replace 40-50% of cement products, it can advance the setting time of cement products by 20-40 minutes, increase the hydration strength of cement products by 8-12mpa, increase the specific surface area of ​​cement products by 100-150㎡ / kg, and reduce the water consumption of cement products 15-30%, improve the wear resistance of cement products by 10-15 times, incre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses alkaline residue cement superfine powder. The alkaline residue cement superfine powder is prepared by the following steps: uniformly mixing 98 to 99 percent by mass of waste alkaline residue discharged after production of industrial crystal soda in salt chemical industry and 1 to 2 percent by mass of chlorine remover with stirring; curing and drying at 100 DEG C; grinding the mixture into cement superfine powder with a specific surface area of greater than 400 to 500m<2> / kg. The alkaline residue cement superfine powder can replace 40 to 50 percent of cement products, improves the performance of cement products, can advance the setting time of cement by 20 to 40 minutes, increases the hydration strength of cement by 8 to 12mpa, increases the specific surface area by100 to 150m<2> / kg, reduces the water consumption of cement by 15 to 30 percent, increases the wear resistance of cement by 10 to 15 times, increase the compatibility of cement products by 100mm, increases the hourly output of a cement table by 20 to 30 tons, directly lowers the cost of cement by 80 yuan / ton, and protects the environment from secondary pollution.

Description

technical field [0001] The invention belongs to the technical field of environmentally friendly cement production, and in particular relates to a superfine cement powder prepared from industrial waste slag and alkali slag. Background technique [0002] With the continuous development of my country's economic reform and opening up, especially the new technology of the salt chemical industry is advancing by leaps and bounds, resulting in the consumption of a large amount of natural mineral resources such as limestone, and also causing the problem of environmental pollution. Waste slag is difficult to handle and can only be piled up and landfilled, resulting in secondary pollution of groundwater resources. Alkali slag contains a large amount of calcium oxide, calcium chloride and other components, and the water content is about 50%. In order to turn waste into treasure, we turn industrial waste Alkali slag, a kind of ultra-fine powder produced by a specific process, is used to re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/24
CPCC04B7/24Y02P40/10
Inventor 谭纪林华玉海华建军曹敏谭伟张会明牛成徐学成陈阳
Owner 淮安市水泥厂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products