A kind of metal substrate graphene modified long-term anti-corrosion paint and preparation method thereof

A graphene modification, long-term anti-corrosion technology, applied in anti-corrosion coatings, radiation-absorbing coatings, coatings, etc., can solve the problems of loss of anti-corrosion function, chemical bond breakage, short anti-corrosion period, etc., and achieve super corrosion resistance for outdoor use. The effect of life, strong complexing ability and short curing time

Active Publication Date: 2020-08-25
广东绿色大地化工有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current anti-corrosion coatings, because the main chain in the film-forming material is composed of C-C bonds, are prone to breakage of chemical bonds under the irradiation of ultraviolet light, thus losing the anti-corrosion function, resulting in a short anti-corrosion life; therefore, the development of long-term High-efficiency anti-corrosion coatings have become an important direction of current coatings research, the key is to prepare high-performance resins and high-performance long-term anti-corrosion additives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of metal substrate graphene modified long-term anti-corrosion paint and preparation method thereof
  • A kind of metal substrate graphene modified long-term anti-corrosion paint and preparation method thereof
  • A kind of metal substrate graphene modified long-term anti-corrosion paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A metal substrate graphene modified long-acting anti-corrosion paint, it is made up of A, B two components, and the weight ratio of described A component and B component is 100:30;

[0044] Wherein, described component A is made up of following raw material by weight:

[0045] 45 parts of epoxy resin with an epoxy value of 0.35, 15 parts of modified graphene, 15 parts of rutile titanium dioxide with a fineness of 50nm, 20 parts of cyclohexanone, and 0.5 parts of defoamer BYK066N, selected from BYK Chemicals Company, leveling agent EFKA3777 0.5 parts, selected from Ciba Company, anti-settling agent 6900-20X 0.8 parts, selected from Disparon Company, dispersant TEGO Dispers 685 0.8 parts, selected from Tego Company;

[0046] Described B component is made up of following raw material by weight:

[0047] Methylated amino resin and isobutanol etherified amino resin are composed of 55 parts of etherified amino resin, 30 parts of phenalkamine and 30 parts of cyclohexanone by ...

Embodiment 2

[0062] A metal substrate graphene modified long-acting anti-corrosion paint, it is made up of A, B two components, and the weight ratio of described A component and B component is 100:35;

[0063] Wherein, described component A is made up of following raw material by weight:

[0064] 40 parts of epoxy resin with an epoxy value of 0.56, 10 parts of modified graphene, 18 parts of phthalocyanine blue with a fineness of 100nm, 18 parts of butanol, and 0.8 parts of defoamer BYK066N, selected from BYK Chemical Company, flow 0.3 part of leveling agent EFKA3777, selected from Ciba Company, 1 part of anti-settling agent 6900-20X, selected from Disparon Company, 1 part of dispersant TEGO Dispers 685, selected from Tego Company;

[0065] Described B component is made up of following raw material by weight:

[0066] Methylated amino resin and isobutanol etherified amino resin are composed of 60 parts of etherified amino resin, 25 parts of phenalkamine and 25 parts of butanol by mass 3:1;...

Embodiment 3

[0081] A metal substrate graphene modified long-acting anti-corrosion paint, it is made up of A, B two components, and the weight ratio of described A component and B component is 100:25;

[0082] Wherein, described component A is made up of following raw material by weight:

[0083] 50 parts of epoxy resin with an epoxy value of 0.20, 20 parts of modified graphene, 20 parts of high-pigment carbon black with a fineness of 200nm, 15 parts of isopropanol, and 0.3 parts of defoamer BYK066N, selected from BYK Chemicals 0.8 part of leveling agent EFKA3777, selected from Ciba Company, 0.5 part of anti-settling agent 6900-20X, selected from Disparon Company, 1 part of dispersant TEGO Dispers 685, selected from Tego Company;

[0084] Described B component is made up of following raw material by weight:

[0085] Methylated amino resin and isobutanol etherified amino resin are composed of 50 parts of etherified amino resin, 35 parts of phenalkamine, and 30 parts of isopropanol by mass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
Login to View More

Abstract

Belonging to the technical field of anticorrosive paint, the invention in particular relates to a metal substrate graphene modified long-acting anticorrosive paint and a preparation method thereof. The metal substrate graphene modified long-acting anticorrosive paint consists of a component A and a component B. The component A is composed of the following raw materials by weight: 40-50 parts of epoxy resin, 10-20 parts of modified graphene, 15-20 parts of pigment, 15-20 parts of a cosolvent, 0.3-0.8 part of a defoamer, 0.3-0.8 part of a leveling agent, 0.5-1 part of an anti-settling agent and0.5-1 part of a dispersant; the component B is composed of the following components by weight: 50-60 parts of etherified amino resin, 25-35 parts of phenolic aldehyde amine, and 20-30 parts of a cosolvent. The metal substrate graphene modified long-acting anticorrosive paint provided by the invention has the advantages of long-lasting and excellent anticorrosive performance, strong substrate adhesion, high mechanical strength, excellent friction resistance, excellent salt fog resistance, good water resistance, chemical resistance, oil resistance and impact resistance, strong construction adaptability, etc. The operation method is simple and is easy to operate, is low in raw material and energy consumption cost, and is environment-friendly and pollution-free, the coating film dries quickly,and the construction period is short.

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, and in particular relates to a graphene-modified long-acting anti-corrosion coating for metal substrates and a preparation method thereof. Background technique [0002] Corrosion of metal is a phenomenon in which metal is destroyed by chemical or electrochemical action of environmental medium. The corrosion of metals spreads all over the national economy and brings huge losses to the national economy. In industrially developed countries, the direct economic loss caused by corrosion accounts for 1% to 4% of the total output value of the national economy, the annual corroded and rusted steel accounts for about 20% of the output, and about 30% of the equipment is scrapped due to corrosion. In China, the economic loss caused by metal corrosion is as high as 30 billion yuan per year, accounting for 4% of the gross national product. For a long time, people have used a variety of techn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D5/08C09D5/32C09D7/62C08G59/50
CPCC08G59/50C09D5/08C09D5/32C09D7/62C09D163/00C08K9/02C08K9/06C08K3/042C08K13/06
Inventor 肖洪健谢秋梅
Owner 广东绿色大地化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products