Assembly-type double-sided partition wall production process

A production process and technology for partition walls, which are applied in the field of production technology of prefabricated double-sided partition walls, can solve the problems of low wear resistance of partition walls, and achieve good wear resistance, high temperature resistance and insulation performance, and convenient assembly process. Effect

Inactive Publication Date: 2018-12-25
安徽省浦菲尔建材有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the disadvantage of low wear resistance of the partition wall in the prior art, and propose a production process for an assembled double-sided partition wall

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: A production process for an assembled double-sided partition wall, comprising the following steps:

[0021] S1. Weigh the following slab raw materials in parts by weight: 100 parts of polyvinyl chloride resin, 12 parts of talcum powder, 11 parts of calcium carbonate, 7 parts of toughened aluminum oxide (toughened aluminum oxide is alumina and zirconia mixture, and the ratio of alumina and zirconia in toughened alumina is 1:1), 5 parts of dioctyl phthalate, 6 parts of azodicarbonamide, 3 parts of silicon dioxide, three 5 parts of propylene oxide propyl ether, 10 parts of mica powder and 1 part of methyl endomethylene tetrahydrophthalic anhydride;

[0022] S2. Pulverize the slab raw material in an ultrafine pulverizer, mix it uniformly and heat it to a molten state, and extrude the molten mixture through an extruder to form a slab;

[0023] S3. Weigh the following wear-resistant paint raw materials in parts by weight: 100 parts of epoxy resin, 12 parts of c...

Embodiment 2

[0026] Embodiment 2: A production process for an assembled double-sided partition wall, comprising the following steps:

[0027] S1. Weigh the following slab raw materials in parts by weight: 110 parts of polyvinyl chloride resin, 13 parts of talcum powder, 12 parts of calcium carbonate, 8 parts of toughened aluminum oxide (toughened aluminum oxide is alumina and zirconia mixture, and the ratio of alumina and zirconia in the toughened alumina is 1:1), 6 parts of dioctyl phthalate, 7 parts of azodicarbonamide, 4 parts of silicon dioxide, three 7 parts of propylene oxide propyl ether, 11 parts of mica powder and 1 part of methyltetrahydrophthalic anhydride;

[0028] S2. Pulverize the slab raw material in an ultrafine pulverizer, mix it uniformly and heat it to a molten state, and extrude the molten mixture through an extruder to form a slab;

[0029] S3, take the following parts by weight of the wear-resistant paint raw material: 110 parts of epoxy resin, 14 parts of corundum, ...

Embodiment 3

[0032] Embodiment 3: A production process for an assembled double-sided partition wall, comprising the following steps:

[0033] S1. Weigh the following slab raw materials in parts by weight: 110 parts of polyvinyl chloride resin, 13 parts of talcum powder, 12 parts of calcium carbonate, 8 parts of toughened aluminum oxide (toughened aluminum oxide is alumina and zirconia mixture, and the ratio of alumina and zirconia in the toughened alumina is 1:1), 6 parts of dioctyl phthalate, 7 parts of azodicarbonamide, 4 parts of silicon dioxide, three 7 parts of propylene oxide propyl ether, 11 parts of mica powder and 1 part of methyltetrahydrophthalic anhydride;

[0034] S2. Pulverize the slab raw material in an ultrafine pulverizer, mix it uniformly and heat it to a molten state, and extrude the molten mixture through an extruder to form a slab;

[0035] S3, take the following parts by weight of the wear-resistant paint raw material: 110 parts of epoxy resin, 14 parts of corundum, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an assembly-type double-sided partition wall production process. The assembly-type double-sided partition wall production process includes the steps of S1), weighing a slab material; S2), crushing the slab material and extruding the mixture in the molten state into shape by an extruder to form a slab blank; S3), weighing a wear-resisting paint raw material; S4), dispersingthe wear-resisting paint raw material with ultrasonic wave prior to filtering the same to obtain wear-resisting paint, and painting the wear-resisting paint to the periphery of the slab blank to obtain a slab after natural airing; S5, designing a three-dimensional diagram of the partition wall according to decoration requirements, determining the length, width and height of each component of the partition wall, cutting the slab and glass according to the three-dimensional diagram of the partition wall, and assembling the glass onto the slab by using glass cement to obtain the assembly-type double-sided partition wall after airing of the glass cement. The application of filler during processing of the slab can reduce production cost during the production of the slab, the addition of toughened alumina can improve the abrasion resistance of the slab, and the addition of mica powder makes the slab have high temperature resistance and good insulation performance.

Description

technical field [0001] The invention relates to the technical field of interior decoration, in particular to a production process for an assembled double-sided partition wall. Background technique [0002] Partition walls are also called high partitions, high partitions, high partition walls, and some people even call them office screens. They are mainly used in office spaces. It is this feature that makes partition walls different from sanitary partitions. Partition walls originated in the United States and developed in the 1950s and 1960s. In the 1980s, due to the high degree of specialization, commercialization and socialization of building materials and components in these countries, the industrialization of decoration has matured so far. The industrialization of partition walls has entered the Chinese market in the past few years. The utilization rate is 2%, and the user group is only limited to office buildings. We can clearly foresee the future of China's decoration i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K13/02C08K3/34C08K3/26C08K3/22C08K5/12C09D163/00C09D5/24C09D7/61C09D7/63C09D7/65H01B3/44E04B2/74
CPCC08K3/22C08K3/26C08K3/34C08K5/12C08K13/02C08K2003/2227C08K2003/2244C08K2003/265C08K2201/014C08K2201/017C08L2201/08C09D5/24C09D7/61C09D7/63C09D7/65C09D7/70C09D163/00E04B2/74H01B3/443C08L27/06C08L83/12C08K13/04C08K7/12C08K5/1515
Inventor 段承连陈小军陈林
Owner 安徽省浦菲尔建材有限公司