A chitosan/styrene-acrylic emulsion surface sizing agent for papermaking

A technology of surface sizing agent and styrene-acrylic emulsion, which is used in papermaking, textiles, papermaking, paper coatings, etc., can solve the problems of low coating strength, poor film-forming property, poor erosion resistance, etc. Membrane properties and adhesive properties, the effect of improving environmental protection

Active Publication Date: 2021-04-02
襄阳市岩翔化工有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The quality of paper production requires good color retention and corrosion resistance. In the traditional production method, styrene-acrylic emulsion must be added to meet the above requirements. However, the existing styrene-acrylic emulsion is composed of three main types: styrene, acrylate, and acrylic acid. Material acquisition, and the sizing agent processed by these three main materials has problems such as poor film formation, low coating strength, poor coating water resistance, poor erosion resistance and poor light resistance, which directly affects the existing paper products. overall quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prescription material weight part is as follows:

[0025] Deionized water 1304Kg, chitosan 194 Kg, ammonium persulfate 10 Kg, ferrous sulfate 0.3 Kg, styrene 240Kg, butyl acrylate 164 Kg, methyl acrylate 8 Kg, compound emulsifier 114 Kg, hydrogen peroxide 40 Kg, disinfectant Foaming agent 0.4 Kg, glyoxal 84 Kg,

[0026] The preparation method is as follows:

[0027] Step 1, take 28 Kg of deionized water and ammonium persulfate and put it into a container, stir and mix evenly for later use;

[0028] Step 2, take 16 Kg of deionized water and put it into a container with ferrous sulfate, stir and mix evenly for later use;

[0029] Step 3. Put the four materials of styrene, butyl acrylate, methyl acrylate and compound emulsifier together into a container and stir evenly to make it a mixed monomer for use;

[0030] Step 4. Take 100 Kg of deionized water and put it into a container with hydrogen peroxide, stir and mix evenly for later use;

[0031] Step 5. Put the remaini...

Embodiment 2

[0042] Prescription material weight part is as follows:

[0043] Deionized water 1304Kg, chitosan 194 Kg, ammonium persulfate 10 Kg, ferrous sulfate 0.3 Kg, styrene 240Kg, butyl acrylate 164 Kg, methyl acrylate 8 Kg, compound emulsifier 114 Kg, hydrogen peroxide 40 Kg, disinfectant Foaming agent 0.4 Kg, glyoxal 84 Kg,

[0044] The preparation method is as follows:

[0045] Step 1, take 28 Kg of deionized water and ammonium persulfate and put it into a container, stir and mix evenly for later use;

[0046] Step 2, take 16 Kg of deionized water and put it into a container with ferrous sulfate, stir and mix evenly for later use;

[0047] Step 3. Put the four materials of styrene, butyl acrylate, methyl acrylate and compound emulsifier together into a container and stir evenly to make it a mixed monomer for use;

[0048] Step 4. Take 100 Kg of deionized water and put it into a container with hydrogen peroxide, stir and mix evenly for later use;

[0049] Step 5. Put the remaini...

Embodiment 3

[0060] Prescription material weight part is as follows:

[0061] Deionized water 1304Kg, chitosan 194 Kg, ammonium persulfate 10 Kg, ferrous sulfate 0.3 Kg, styrene 240Kg, butyl acrylate 164 Kg, methyl acrylate 8 Kg, compound emulsifier 114 Kg, hydrogen peroxide 40 Kg, disinfectant Foaming agent 0.4 Kg, glyoxal 84 Kg,

[0062] The preparation method is as follows:

[0063] Step 1, take 28 Kg of deionized water and ammonium persulfate and put it into a container, stir and mix evenly for later use;

[0064] Step 2, take 16 Kg of deionized water and put it into a container with ferrous sulfate, stir and mix evenly for later use;

[0065] Step 3. Put the four materials of styrene, butyl acrylate, methyl acrylate and compound emulsifier together into a container and stir evenly to make it a mixed monomer for use;

[0066] Step 4. Take 100 Kg of deionized water and put it into a container with hydrogen peroxide, stir and mix evenly for later use;

[0067] Step 5. Put the remaining...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a chitosan / styrene-acrylic emulsion surface sizing agent for papermaking. A formula of the chitosan / styrene-acrylic emulsion surface sizing agent comprises deionized water, chitosan, ammonium persulfate, ferrous sulfate, styrene, butyl acrylate, methyl acrylate, a composite emulsifier, hydrogen peroxide, a defoaming agent and glyoxal. A preparation method comprises the following steps: 1, stirring 28kg of deionized water and ammonium persulfate for standby use; 2, mixing 16kg of deionized water and ferrous sulfate for standby use; 3, stirring the styrene, butyl acrylate,methyl acrylate and the composite emulsifier for standby use; 4, mixing 100kg of deionized water and hydrogen peroxide for standby use; 5, adding the surplus water into chitosan, heating, and addingthe standby use material of step 1; 6, adding the standby use material of step 2, and preserving the heat for 10 minutes; 7, stirring 10 percent of to-be-used mixed monomer of step 3 and 10 percent ofstandby use material of step 4; 8, adding the remaining standby use materials of step 3 and 4; 9, cooling to 60 DEG C, adding the glyoxal, and stirring for 15 minutes; 10, adding the defoaming agent;and 11, filtering to remove impurities, thus obtaining a finished product. By adopting the sizing agent, the film forming performance, adhesion and paper surface strength of the paper product can beimproved, and the environment-friendly production can be facilitated.

Description

technical field [0001] The invention relates to a material for papermaking production, in particular to a chitosan / styrene-acrylic emulsion surface sizing agent for papermaking. Background technique [0002] The quality of paper production requires good color retention and corrosion resistance. In the traditional production method, styrene-acrylic emulsion must be added to meet the above requirements. However, the existing styrene-acrylic emulsion is composed of three main types: styrene, acrylate, and acrylic acid. Material acquisition, and the sizing agent processed by these three main materials has problems such as poor film formation, low coating strength, poor coating water resistance, poor erosion resistance and poor light resistance, which directly affects the existing paper products. overall quality. Contents of the invention [0003] The purpose of the present invention is to solve the above-mentioned existing problems, and to provide a chitosan / styrene-acrylic e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H21/16D21H19/20C08F251/00C08F212/08C08F220/18C08F220/14
CPCC08F251/00D21H19/20D21H21/16C08F220/1804
Inventor 李巍梁英陈振峰李祺祥
Owner 襄阳市岩翔化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com