Circulating utilizing method of using biomass ash and slag to modify converter steelmaking slag to remove phosphorous

A biomass ash, converter steel slag technology, applied in recycling technology, application, phosphate fertilizer and other directions, to achieve the effects of easy absorption, important economic and environmental benefits, and simple operation

Active Publication Date: 2019-01-15
ANHUI UNIVERSITY OF TECHNOLOGY
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the problems existing in the current steel slag treatment and utilization process, the present invention provides a recycling method for dephosphorization of converter steel slag modified by biomass ash and slag, which promotes 2CaO·SiO 2 -2CaO·K 2 O·P 2

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Circulating utilizing method of using biomass ash and slag to modify converter steelmaking slag to remove phosphorous
  • Circulating utilizing method of using biomass ash and slag to modify converter steelmaking slag to remove phosphorous
  • Circulating utilizing method of using biomass ash and slag to modify converter steelmaking slag to remove phosphorous

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Select the converter steel slag produced by the converter duplex process of producing automobile plates in a steel factory, and the recycling method of biomass ash slag modification converter steel slag dephosphorization in this embodiment, its flow chart is as follows figure 1 As shown, it specifically includes the following steps:

[0043] (1) Add rice straw ash under 200 mesh sieves to molten steel slag when slag removal, the ash amount is 5mass%;

[0044] (2) insulation reaction at 1723K for 90min;

[0045] (3) Control the cooling rate to be 5K / min, and slowly drop to room temperature;

[0046] (4) The slag sample particle size of the cooled modified steel slag crushed, ground and screened is 75-150 μm, and the chemical composition of the dephosphorized slag is detected by an X-ray fluorescence spectrometer, and the results are shown in Table 2;

[0047] (5) Prepare 400 mL of citric acid solution with a pH value of 5 and add it to the beaker, and control the acid...

Embodiment 2

[0058] Select the converter steel slag produced by the converter duplex process of producing automobile plates in a steel factory, and the recycling method of the biomass ash slag modification converter steel slag dephosphorization of the present embodiment specifically includes the following steps:

[0059] (1) Add the sugarcane ash under the 200 mesh sieve to the molten steel slag when the slag is discharged, and the ash amount is 8mass%;

[0060] (2) insulation reaction at 1823K for 60 minutes;

[0061] (3) Control the cooling rate to be 4K / min, and slowly drop to room temperature;

[0062] (4) The slag sample particle size of the cooled modified steel slag crushed, ground and screened is 45-48 μm, and the chemical composition of the dephosphorized slag is detected by an X-ray fluorescence spectrometer, and the results are shown in Table 3;

[0063] (5) Prepare 400 mL of citric acid solution with a pH value of 6 and add it to the beaker, and control the acidity and alkalin...

Embodiment 3

[0074] Select the converter steel slag produced by the converter double slag process of producing pipeline steel in a steel factory, and the recycling method of biomass ash slag modification converter steel slag dephosphorization in this embodiment specifically includes the following steps:

[0075] (1) Add rice straw and sawdust ash (mass ratio is 1:1) under 200 mesh sieves to the molten steel slag during slag removal, and the ash amount is 8mass%;

[0076] (2) insulation reaction at 1783K for 80min;

[0077] (3) Control the cooling rate to be 3K / min, and slowly drop to room temperature;

[0078] (4) The slag sample particle size of the cooled modified steel slag crushed, ground and screened is 45-48 μm, and the chemical composition of the dephosphorized slag is detected by an X-ray fluorescence spectrometer, and the results are shown in Table 4;

[0079] (5) citric acid solution 400mL that the preparation pH value is 7 joins in the beaker, controls solution acidity and alka...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a circulating utilizing method of using biomass ash and slag to modify converter steelmaking slag to remove phosphorous, and belongs to the technical field of resource reuse inmetallurgy. According to the method, biomass ash and slag is used to modify molten converter steelmaking slag; then modified converter steelmaking slag is finely grinded; finely grinded converter steelmaking slag is added into a critic acid solution; under the stirring of an electric stirrer, phosphorus in converter steelmaking slag is dissolved out, phosphorus containing filtrate and phosphorusfree steel slag are obtained; the phosphorus containing organic acid solution can be used to produce a liquid phosphorus fertilizer; and the phosphorus free steel slag is dried and then applied to metallurgy. The dissolution rate of phosphorus in steel slag can reach 90%; the dissolution rate of iron is lower than 10%, the iron loss is effectively avoided; the critic acid has weak acidity, the equipment requirements of leaching treatment are low, compared with a strong acid treatment, the processing cost is reduced, and environmental pollution is avoided.

Description

technical field [0001] The invention belongs to the technical field of metallurgical resource reuse, and relates to a recycling method for removing phosphorus from modified converter steel slag with biomass ash and slag, and more specifically, to a method for recycling phosphorus in modified converter steel slag by using citric acid. Background technique [0002] Steel slag is a solid waste produced in the steelmaking process, and its output is about 10-20% of crude steel output. Due to the phosphorus element and high free calcium oxide in steel slag, its use in steel plants and cement concrete is limited. Effective use of building materials in the field. For example, in 2017, my country's crude steel output was about 800 million tons, and the discharge of steel slag was close to 100 million tons, and its comprehensive utilization rate was only 25-30%. At present, most of the steel slag is discarded or landfilled after iron selection, which not only occupies the abandoned l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21B3/06C22B1/11C05G1/00
CPCC05B13/00C05G5/20C21B3/06C22B1/11C05F11/00Y02P10/20Y02W30/50
Inventor 吕宁宁杨金星苏畅杜传明桂德培王海川孔辉
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap