Super-tough polyketone (POK) material and preparation method thereof

A polyketone, super-tough technology, used in the chemical field, can solve the problems of low impact strength and low flexural modulus, and achieve the effects of low specific gravity, high toughness and excellent environmental friendliness.

Active Publication Date: 2019-01-29
SHANGHAI GAOXINKE PLASTIC PROD
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to improve a kind of super-tough POK polyketone material and preparation method thereof, described this super-tough POK polyketone material and preparation method thereof will solve the low flexural modulus of POK polyketone material in Greek technology , The technical problem of low impact strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-tough polyketone (POK) material and preparation method thereof
  • Super-tough polyketone (POK) material and preparation method thereof
  • Super-tough polyketone (POK) material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 94.4 parts by weight of polyketone (M630A, Korea Hyosung), 5 parts by weight of impact modifier hydrogenated styrene-butadiene-urethane copolymer (ESBU) (Kuramiron U, TU-S5265, Kuraray Co. , Ltd.), 0.2 parts by weight of organic carboxylate nucleating agent, 0.1 parts by weight of lubricant (ethylene bis stearamide EBS), 0.1 parts by weight of heat stabilizer (zinc stearate), 0.1 parts by weight Add hindered phenolic antioxidant (BASF antioxidant 1076) and 0.1 weight part of phosphite antioxidant (BASF antioxidant 168) into a high-speed mixer and stir and mix. The mixing temperature is not higher than 80 ° C. Mix After 20 minutes, the uniformly stirred material was added to the hopper of a co-rotating twin-screw extruder with an aspect ratio L / D of 42:1 and a screw diameter of 40mm, and then melted, kneaded, and extruded by the twin-screw machine. After being cooled in a water tank and air-dried, it enters a granulator for granulation and packaging, and the super-tough ...

Embodiment 2

[0030] 89.4 parts by weight of polyketone (M630A, Korea Hyosung), 10 parts by weight of impact modifier hydrogenated styrene-butadiene-urethane copolymer (ESBU) (Kuramiron U, TU-S5265, Kuraray Co. , Ltd.), 0.2 parts by weight of organic carboxylate nucleating agent, 0.1 parts by weight of lubricant (ethylene bis stearamide EBS), 0.1 parts by weight of heat stabilizer (zinc stearate), 0.1 parts by weight Add hindered phenolic antioxidant (BASF antioxidant 1076) and 0.1 weight part of phosphite antioxidant (BASF antioxidant 168) into a high-speed mixer and stir and mix. The mixing temperature is not higher than 80 ° C. Mix After 20 minutes, the uniformly stirred material was added to the hopper of a co-rotating twin-screw extruder with an aspect ratio L / D of 42:1 and a screw diameter of 40mm, and then melted, kneaded, and extruded by the twin-screw machine. After being cooled in a water tank and air-dried, it enters a granulator for granulation and packaging, and the super-tough...

Embodiment 3

[0034] 84.4 parts by weight of polyketone (M630A, Korea Hyosung), 15 parts by weight of impact modifier hydrogenated styrene-butadiene-urethane copolymer (ESBU) (Kuramiron U, TU-S5265, Kuraray Co. , Ltd.), 0.2 parts by weight of organic carboxylate nucleating agent, 0.1 parts by weight of lubricant (ethylene bis stearamide EBS), 0.1 parts by weight of heat stabilizer (zinc stearate), 0.1 parts by weight Add hindered phenolic antioxidant (BASF antioxidant 1076) and 0.1 weight part of phosphite antioxidant (BASF antioxidant 168) into a high-speed mixer and stir and mix. The mixing temperature is not higher than 80 ° C. Mix After 20 minutes, the uniformly stirred material was added to the hopper of a co-rotating twin-screw extruder with an aspect ratio L / D of 42:1 and a screw diameter of 40mm, and then melted, kneaded, and extruded by the twin-screw machine. After being cooled in a water tank and air-dried, it enters a granulator for granulation and packaging, and the super-tough...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention provides a super-tough polyketone (POK) material. The super-tough POK material is prepared from the following components in parts by weight: 70-90 parts of POK, 5-25 parts of an impact modifier, 0.05-0.5 part of a nucleating agent, 0.05-1 part of a lubricant, 0.05-0.2 part of a heat stabilizer, 0.05-0.2 part of a main antioxidant and 0.05-0.2 part of an auxiliary antioxidant. The invention further provides a preparation method of the super-tough POK material. The preparation method comprises the following steps: mixing the raw materials according to the weight parts, and then carrying out melt extrusion granulation by using a double-screw extruder to prepare the super-tough POK material. The super-tough POK material provided by the invention has the characteristics of low specific gravity, high wear resistance, ultrahigh toughness, environmental friendliness and the like, and can be applied to the fields of toy dolls, automobiles, electronics and the like.

Description

technical field [0001] The invention relates to the field of chemistry, in particular to polymer material technology, in particular to a POK polyketone material, in particular to a super-tough POK polyketone material and a preparation method thereof. Background technique [0002] POK is a kind of engineering plastic with extremely excellent comprehensive properties. It belongs to polyketone materials. It is a new type of green polymer material formed by coordination polymerization of CO, ethylene and propylene. Self-lubricating, impact resistance and many other excellent properties, compared with polyoxymethylene (POM) material, this material has the characteristics of low specific gravity, higher impact resistance toughness, green environmental protection and so on. The wear resistance of POK is 14 times that of POM, which is the best wear-resistant material at present, and it can be used almost permanently without change. Usually PA66 has high tensile strength, but low im...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/02C08L51/08C08K5/00C08K5/098C08K5/20
CPCC08K2201/014C08L61/02C08L2201/08C08L2205/06C08L2205/24C08L51/08C08K5/00C08K5/098C08K5/20
Inventor 郑晓清李文国周扬波黄锦河陈建和
Owner SHANGHAI GAOXINKE PLASTIC PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com