Rapid assembly turbocharging hose and preparation method thereof

A turbocharged and fast technology, applied in the automotive field, can solve the problems of insufficient thermal stability to meet demand, poor flame retardant effect, etc., and achieve the effects of low cost, good flame retardant and lubricating effect, and high degree of dispersion

Inactive Publication Date: 2019-02-12
ANHUI ZHONGDING HOSE PROD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the rapid assembly turbo tube in the market is mainly made of acrylic rubber material, which has good oil resistance, high shock absorption performance, excellent water resistance, weather resistance and low compression deformation performance, but has poor flame retardancy and thermal stability. Sex doesn't satisfy needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid assembly turbocharging hose and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A quick assembly turbo tube, its raw materials include: acrylate rubber 80g, plasticizer TP759 15g, stearic acid 0.2g, filling reinforcing agent 100g, coupling agent 1g, anti-aging agent 445 2.5g, ARMEEN18D 0.8g , lubricant VAM 3g, vulcanizing agent DIAK#1 1g, vulcanization accelerator XLA-60 6g.

[0020] The filling and reinforcing agent is composed of carbon black N-550, polyethylene glycol compound, nano talcum powder, medical stone powder, and precipitated barium sulfate in a weight ratio of 60:12:12:8:10. The polyethylene glycol complex is prepared by the following process: mix 18g of phosphomolybdic acid, 1g of ammonium chloride, and 1.4g of polyethylene glycol, then add 50g of 42wt% ethanol aqueous solution, heat up to 54°C for 2 hours, filter, and dry Obtain polyethylene glycol complex.

[0021] The preparation method of the above-mentioned rapid assembly turbocharger tube includes the following steps: adding acrylate rubber, plasticizer TP759, stearic acid, fi...

Embodiment 2

[0023] A quick assembly turbocharger tube, its raw materials include: acrylate rubber 120g, plasticizer TP759 5g, stearic acid 1.5g, filling reinforcing agent 80g, coupling agent 3g, anti-aging agent 445 0.5g, ARMEEN18D 1.2g , lubricant VAM 1g, vulcanizing agent DIAK#1 1.8g, vulcanization accelerator XLA-60 2g.

[0024] The filling and reinforcing agent is composed of carbon black N-550, polyethylene glycol compound, nano talcum powder, medical stone powder, and precipitated barium sulfate in a weight ratio of 70:4:18:4:17. The polyethylene glycol complex is prepared by the following process: mix 12g of phosphomolybdic acid, 1.8g of ammonium chloride, and 0.5g of polyethylene glycol, then add 80g of 35wt% ethanol aqueous solution, heat up to 58°C for 1 hour, filter, Dry to obtain polyethylene glycol complex.

[0025] The preparation method of the above-mentioned rapid assembly turbocharger tube includes the following steps: adding acrylate rubber, plasticizer TP759, stearic a...

Embodiment 3

[0027] A quick assembly turbocharger tube, its raw materials include: 90g of acrylic rubber, 12g of plasticizer TP759, 0.6g of stearic acid, 95g of filling and reinforcing agent, 1.5g of coupling agent, 2g of anti-aging agent 445, 0.9g of ARMEEN18D , lubricant VAM 2.5g, vulcanizing agent DIAK#1 1.2g, vulcanization accelerator XLA-60 5g.

[0028] The filling and reinforcing agent is composed of carbon black N-550, polyethylene glycol compound, nano talcum powder, medical stone powder, and precipitated barium sulfate in a weight ratio of 64:10:14:7:12. The polyethylene glycol complex is prepared by the following process: mix 16g of phosphomolybdic acid, 1.2g of ammonium chloride, and 1.2g of polyethylene glycol, then add 60g of 40wt% ethanol aqueous solution, heat up to 55°C for 1.7h, filter , and dry to obtain the polyethylene glycol complex.

[0029] The preparation method of the above-mentioned rapid assembly turbocharger tube includes the following steps: adding acrylate ru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rapid assembly turbocharging hose. The rapid assembly turbocharging hose is prepared from the following raw materials in parts by weight: 80 to 120 parts of acrylate rubber,5 to 15 parts of a plasticizer TP759, 0.2 to 1.5 parts of stearic acid, 80 to 100 parts of a filling fortifier, 1 to 3 parts of a coupling agent, 0.5 to 2.5 parts of an anti-aging agent 445, 0.8 to 1.2 parts of ARMEEN 18D, 1 to 3 parts of a lubricant VAM, 1 to 1.8 parts of a vulcanizing agent DIAK No.1 and 2 to 6 parts of a vulcanizing accelerator XLA-60. The invention discloses a preparation method of the rapid assembly turbocharging hose. The preparation method comprises the following steps: uniformly mixing the acrylate rubber, the plasticizer TP759, the stearic acid, the filling fortifier,the coupling agent, the anti-aging agent 445, the ARMEEN 18D, the lubricant VAM, the vulcanizing agent DIAK No.1 and the vulcanizing accelerator XLA-60, extruding, vulcanizing and forming to obtain the rapid assembly turbocharging hose.

Description

technical field [0001] The invention relates to the technical field of automobiles, in particular to a rapid assembly turbocharger tube and a preparation method thereof. Background technique [0002] At present, automobiles generally adopt turbocharging devices to increase the power of automobile engines. The advantages of turbocharging are obvious. It can greatly increase power and torque without increasing engine displacement. After an engine is equipped with a turbocharger, its maximum output power can be increased by about 40% or more compared with that without a supercharger. [0003] At present, the rapid assembly turbo tube in the market is mainly made of acrylic rubber material, which has good oil resistance, high shock absorption performance, excellent water resistance, weather resistance and low compression deformation performance, but has poor flame retardancy and thermal stability. Sex does not satisfy needs. Contents of the invention [0004] Based on the t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/04C08L71/02C08K13/02C08K5/09C08K3/04C08K3/34C08K3/30C08K5/5425C08K5/544
CPCC08K2003/3045C08K2201/011C08L33/04C08L2201/02C08L2201/08C08L2201/22C08L2203/18C08L71/02C08K13/02C08K5/09C08K3/04C08K3/34C08K3/30C08K5/5425C08K5/544
Inventor 陈兴华杨显峰鲍仁德郑海波符王超刘鎏耿本星
Owner ANHUI ZHONGDING HOSE PROD