Electric vehicle light snoot coating paint and preparation method thereof

A technology for concentrators and electric vehicles, applied in primers, polyester coatings, coatings, etc., can solve the problems of low heat resistance, poor weather resistance, weak adhesion, etc., and achieve excellent performance and excellent performance. Adhesion, fast drying effect

Active Publication Date: 2019-02-12
肇庆市哈力化工有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has the advantages of high reactivity, many varieties, low VOC content, low energy consumption, etc., but generally speaking, the vacuum coating UV-curable coatings obtained by the prior art have low heat resistance, weak adhesion, and poor weather resistance. Waiting for the disadvantages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electric vehicle light snoot coating paint and preparation method thereof
  • Electric vehicle light snoot coating paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Embodiment 1 provides, on the one hand, a coating primer for the spotlight cover of an electric vehicle lamp, comprising the following raw materials in parts by weight: 30 parts of modified alkyd resin, 35 parts of modified phenolic resin, 33.38 parts of solvent, drying 1.41 parts of agent, 0.01 part of silicone oil, 0.2 parts of anti-skinning agent.

[0061] In this example, the modified alkyd resin is a mixture of medium-oil linseed oil-modified alkyd resin and short-oil linseed oil-modified alkyd resin, and the corresponding weight ratio is 23:7; the modified phenolic The resin is rosin modified phenolic resin; the solvent is 200# solvent and 120# solvent, and the corresponding weight ratio is 15:18.38; the drier is cobalt isooctanoate, zirconium isooctanoate, manganese isooctanoate, isooctanoate The calcium mixture has a corresponding weight ratio of 0.25:0.75:0.16:0.25; the silicone oil is polyether-modified polyorganosiloxane; and the anti-skinning agent is methyl...

Embodiment 2

[0068] Embodiment 2 provides on the one hand a kind of coating primer for the spotlight cover of electric vehicle lights, including the following raw materials in parts by weight: 10 parts of modified alkyd resin, 20 parts of modified phenolic resin, 20 parts of solvent, drying 0.8 part of agent, 0.005 part of silicone oil, 0.1 part of anti-skinning agent.

[0069] In this example, the modified alkyd resin is a mixture of medium-oil linseed oil-modified alkyd resin and short-oil linseed oil-modified alkyd resin, and the corresponding weight ratio is 23:7; the modified phenolic The resin is rosin modified phenolic resin; the solvent is 200# solvent and 120# solvent, and the corresponding weight ratio is 15:18.38; the drier is cobalt isooctanoate, zirconium isooctanoate, manganese isooctanoate, isooctanoate The calcium mixture has a corresponding weight ratio of 0.25:0.75:0.16:0.25; the silicone oil is polyether-modified polyorganosiloxane; and the anti-skinning agent is methyl ...

Embodiment 3

[0076] Embodiment 3 provides, on the one hand, a coating primer for the spotlight cover of an electric vehicle lamp, comprising the following raw materials in parts by weight: 50 parts of modified alkyd resin, 50 parts of modified phenolic resin, 40 parts of solvent, drying 3 parts of agent, 0.015 parts of silicone oil, 0.3 parts of anti-skinning agent.

[0077] In this example, the modified alkyd resin is a mixture of medium-oil linseed oil-modified alkyd resin and short-oil linseed oil-modified alkyd resin, and the corresponding weight ratio is 23:7; the modified phenolic The resin is rosin modified phenolic resin; the solvent is 200# solvent and 120# solvent, and the corresponding weight ratio is 15:18.38; the drier is cobalt isooctanoate, zirconium isooctanoate, manganese isooctanoate, isooctanoate The calcium mixture has a corresponding weight ratio of 0.25:0.75:0.16:0.25; the silicone oil is polyether-modified polyorganosiloxane; and the anti-skinning agent is methyl eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses electric vehicle light snoot coating primer which is prepared from the following raw materials in parts by weight: 10-50 parts of modified alkyd resin, 20-50 parts of modifiedphenolic resin, 20-40 parts of solvent, 0.8-3 parts of a dryer, 0.005-0.015 part of organic silicone oil and 0.1-0.3 part of an anti-skinning agent. The electric vehicle light snoot coating primer provided by the invention has the advantages of stable performance, no pollution, reasonable formula and good performance. The formula is selected while taking full account of factors such as leveling property and adhesion; two kinds of film forming resin, the modified alkyd resin and the modified phenolic resin, are adopted and compounded; the prepared primer has excellent leveling property and heatresistance as well as high drying speed, prevents the generation of shrinkage cavity and ripples and can ensure high gloss and refractive index of a metal coating. Through a synergistic effect of various kinds of components in the formula, a film has excellent adhesion to ABS base material and good film forming hardness while the phenomena of gloss loss and wrinkling of the coating are avoided.

Description

technical field [0001] The invention relates to the field of new paint materials, in particular to a coating paint for a condenser cover of an electric vehicle lamp and a preparation method thereof. Background technique [0002] In recent years, with the development of the economy, plastics (ABS, GRP, RIM, EPPM, polyurethane, nylon) as engineering decorative structural materials are widely used in industrial fields such as automobiles, household appliances, daily packaging and craft decoration. In the industry, vacuum evaporation plating and vacuum sputtering plating are usually used to form a bright metal film on the surface of the plastic substrate, that is, metallization of the plastic surface. Vacuum coating on plastic products can endow plastic products with metallic luster, increase the appearance aesthetics, and increase added value at the same time. This technology is widely used especially in the field of car lamp reflectors. [0003] The vacuum-plated metal thin f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D161/14C09D5/00C09D7/63
CPCC08K2201/014C08L2201/08C08L2205/03C09D5/002C09D5/18C09D161/14C09D167/08C09D7/63C08L67/08C08L83/12C08L83/04C08K5/098C08L61/14
Inventor 黄碧星
Owner 肇庆市哈力化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka