High-compression-resistant and long-life water-permeable plate and preparation method thereof

A long-life, water-permeable board technology, applied in the field of water-permeable boards, can solve the problems of compressive strength, low flexural strength, fracturing, crushing, short service life, etc. The effect of reducing cost

Active Publication Date: 2019-02-15
柳晶(长春)环保科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing permeable panels are made of ordinary permeable materials, and the compressive strength and flexural strength are relatively low, and they are prone to fracturing and collapse when driving on the road, resulting in a short service life and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A high-pressure-resistant and long-life permeable board, including the following raw material components in parts by weight: 100 parts of waste ash, 80 parts of waste residue, 10 parts of polymer fiber, 8 parts of zirconia fiber, 4 parts of polyether polyamine, and nano-silica powder 10 parts, 8 parts of nano-calcium carbonate, 3 parts of nano-titanium dioxide and 4 parts of reinforcing agent, of which:

[0029] The reinforcing agent is composed of phenolic resin, polyanionic cellulose, sodium carboxymethyl cellulose CMC-LV, graphite powder, glass microspheres, oxidation Calcium, calcium carbonate whiskers, polyacrylamide.

[0030] The preparation method of the high-compression and long-life permeable plate of this embodiment includes the following steps:

[0031] (1) Raw material mixing and ball milling: first mix waste ash, waste slag, polymer fibers, and zirconia fibers according to the raw material components, and then add them to a ball mill for ball milling to ob...

Embodiment 2

[0037] A high-compression-resistant and long-life permeable board, including the following raw material components in parts by weight: 200 parts of waste ash, 120 parts of waste residue, 20 parts of polymer fiber, 18 parts of zirconia fiber, 10 parts of polyether polyamine, nano silicon powder 20 parts, 14 parts of nano-calcium carbonate, 9 parts of nano-titanium dioxide and 8 parts of reinforcing agent, of which:

[0038] The reinforcing agent is composed of phenolic resin, polyanionic cellulose, sodium carboxymethyl cellulose CMC-LV, graphite powder, glass microspheres, oxidation Calcium, calcium carbonate whiskers, polyacrylamide.

[0039] The preparation method of the high-compression and long-life permeable plate of this embodiment includes the following steps:

[0040] (1) Raw material mixing and ball milling: first mix waste ash, waste slag, polymer fibers, and zirconia fibers according to the raw material components, and then add them to a ball mill for ball milling t...

Embodiment 3

[0046] A high-pressure-resistant and long-life permeable board, including the following raw material components in parts by weight: 120 parts of waste ash, 90 parts of waste residue, 12 parts of polymer fiber, 10 parts of zirconia fiber, 5 parts of polyether polyamine, and nano-silica powder 12 parts, 9 parts of nano-calcium carbonate, 4 parts of nano-titanium dioxide and 5 parts of reinforcing agent, of which:

[0047] The strengthening agent is composed of phenolic resin, polyanionic cellulose, sodium carboxymethyl cellulose CMC-LV, graphite powder, glass microspheres, oxidation Calcium, calcium carbonate whiskers, polyacrylamide.

[0048] The preparation method of the high-compression and long-life permeable plate of this embodiment includes the following steps:

[0049] (1) Raw material mixing and ball milling: first mix waste ash, waste slag, polymer fibers, and zirconia fibers according to the raw material components, and then add them to a ball mill for ball milling to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of water-permeable plates, in particular to a high-compression-resistant and long-life water-permeable plate and a preparation method thereof. The high-compression-resistant and long-life water-permeable plate comprises the following components as raw materials in parts by weight: 100-200 parts of waste ash, 80-120 parts of waste slag, 10-20 parts of polymer fiber, 8-18 parts of zirconium oxide fiber, 4-10 parts of polyether polyamine, 10-20 parts of nanometer silicon micropowder, 8-14 parts of nanometer calcium carbonate, 3-9 parts of nanometer titanium dioxide and 4-8 parts of a reinforcing agent. The preparation method of the high-compression-resistant long-life water-permeable plate comprises the following steps: performing mixed ball milling on the raw materials, mixing powder, adding the reinforcing agent, preparing a blank plate and polishing to obtain a finished product. The water-permeable plate has relatively high compressive strength and flexural strength; in addition, by the preparation method, a preparation technology is simple, and various technological parameters are strictly controlled according to the properties of the raw materials, so that the quality of the finished water-permeable plate product is guaranteed.

Description

technical field [0001] The invention relates to the technical field of permeable panels, in particular to a high-pressure-resistant and long-life permeable panel and a preparation method thereof. Background technique [0002] Water-permeable material is a kind of porous material, which realizes the transfer of water and gas inside the material through the pore channels inside the material. It is widely used in construction, environmental protection, chemical industry, water treatment, catalysis and other fields. For example, permeable panels used for drainage on urban roads, catalyst carriers in the catalytic field, filter materials used in water treatment processes, filter materials used in chemical production and separation processes, and mold materials for grouting molding used in the ceramic industry are all water-permeable materials. It can be seen that the application of permeable materials is very extensive, especially the market prospect of permeable panels is extrem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/10B29C67/24
CPCB29C67/243C04B26/10C04B2111/00284C04B2201/50C04B18/08C04B18/0409C04B18/12C04B14/22C04B18/0427C04B18/16C04B16/06C04B14/4637C04B14/06C04B14/28C04B14/305C04B24/302C04B24/383C04B14/024C04B22/064C04B14/383C04B24/2652
Inventor 任文强
Owner 柳晶(长春)环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com