Oil well cement slurry convenient to use

A technology of oil well cement slurry and parts by weight, applied in the field of oil well cement slurry, can solve the problems of poor performance of oil well cement slurry, ineffective use of high temperature and high pressure, etc., and achieves the effect of good finished product, good performance and easy long-term use.

Inactive Publication Date: 2019-03-01
泸州高智知识产权运营有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is that the existing oil well cement slurry has poor performance and cannot be effectively used in high temperature, high pressure, and harsh environment oil exploitation. The purpose is to provide easy-to-use oil well cement slurry and solve the problem of using oil well cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The easy-to-use oil well cement slurry of the present invention comprises the following components in parts by weight: 35-48 parts of limestone, 24-31 parts of sandstone, 17-26 parts of converter slag, 13-23 parts of spheroidized silicon powder, and 8 parts of ordinary silicon powder ~17 parts, 39~48 parts of water, 23~36 parts of polyurethane elastomer, 19~26 parts of polyisocyanate, 13~24 parts of bentonite, 11~23 parts of biopolymer, 9~17 parts of high molecular weight fiber derivatives, organic 11-25 parts of phosphate, 34-47 parts of gypsum.

[0022] The easy-to-use oil well cement slurry includes the following components in parts by weight: 39-44 parts of limestone, 29-31 parts of sandstone, 19-25 parts of converter slag, 18-22 parts of spheroidized silicon powder, and 10-15 parts of ordinary silicon powder 41-46 parts of water, 25-33 parts of polyurethane elastomer, 21-25 parts of polyisocyanate, 15-22 parts of bentonite, 13-20 parts of biopolymer, 10-15 parts of...

Embodiment 2

[0025] The present invention comprises the following steps:

[0026] (1) mixing limestone, sandstone, converter slag with water, and grinding to make a slurry, stirring evenly at 50-60°C to make a slurry with a water content of 45-56%;

[0027] (2) dehydrating the slurry through a vacuum suction filter to form a filter cake with 12% to 15% moisture;

[0028] (3) Add filter cake, bentonite, spheroidized silicon powder, and ordinary silicon powder into the drying crusher, and after crushing, dry it into raw meal powder with a water content of 1 to 3%;

[0029] (4) Feed the raw meal powder into the rotary kiln after preheating and decomposing, and add polyurethane elastomer, polyisocyanate, biopolymer, high molecular weight fiber derivatives, organic phosphate and water, and use the kiln head burner to calcinate it into Oil well cement clinker;

[0030] (5) The oil well cement clinker and gypsum are mixed and ground, and the specific surface area is 260-285m 2 / kg to get the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses oil well cement slurry convenient to use. The oil well cement slurry comprises, by weight, 35-48 parts of limestone, 24-31 parts of sandstone, 17-26 parts of converter slag, 13-23 parts of nodularized silicon powder, 8-17 parts of ordinary silicon powder, 39-48 parts of water, 23-36 parts of polyurethane elastomers, 19-26 parts of polyisocyanate, 13-24 parts of bentonite, 11-23 parts of biopolymers, 9-17 parts of fiber derivatives with high molecular weights, 11-25 parts of organic phosphate and 34-47 parts of gypsum. The oil well cement slurry has the advantages of good performance and applicability to high-temperature and high-pressure severe environments.

Description

technical field [0001] The invention relates to the petroleum field, in particular to an easy-to-use oil well cement slurry. Background technique [0002] With the continuous deepening of petroleum exploration and development, the number of wells with special requirements is gradually increasing, and the requirements for cementing are getting higher and higher. Only using conventional cement slurry systems can not only meet the cementing requirements of special wells such as gas storages, but also cannot solve various complex conditions encountered in the cementing process. The development of cement slurry systems with better comprehensive performance can effectively promote the cementing technology. development of. [0003] Gas well annulus under pressure is becoming more and more common, and the anti-gas channeling ability of cement slurry and the sealing quality and durability of cement sheath are getting more and more attention in the industry. For the current high tem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/21C09K8/467
CPCC04B7/21C09K8/467Y02P40/10
Inventor 赖惠蓉
Owner 泸州高智知识产权运营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap