Solvent-free polyurethane-acrylate floor material

A technology of polyurethane acrylic and floor materials, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve problems such as ecological environmental pollution and threats, and achieve strong decoration, high tensile bond strength, and good temperature denaturation resistance Effect

Inactive Publication Date: 2019-04-02
FUZHOU ROYAL FLOOR
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional solvent-based floor materials contain about 50% organic solvents. During the manufacturing, processing, drying and curing of coatings, a large amount of volatile organic compounds (VOC) are released into the atmosphere, which has a negative impact on the human ecological environment. cause great pollution and threats

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvent-free polyurethane-acrylate floor material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Solvent-free polyurethane acrylic floor material, the floor material includes A component and B component, the raw material composition of the A component is calculated in parts by weight: 20 parts of 2,2-dimethylol butanol, 55 parts of 2,2,4-trimethylhexamethylene diisocyanate, 13 parts of dipropylene glycol methyl ether acetate, 18 parts of color paste, 13 parts of kaolin, 40 parts of talcum powder, 13 parts of precipitated barium sulfate, N,N-dimethyl 3.0 parts of cyclohexylamine, 0.6 parts of BYK-358N, 0.2 parts of BYK-066N, 0.3 parts of BYK-163; Alcohol 8 parts, dibutyltin diacetate 1.4 parts.

Embodiment 2

[0015] Solvent-free polyurethane acrylic floor material, the floor material includes A component and B component, the raw material composition of the A component is calculated in parts by weight: 30 parts of 2,2-dimethylol butanol, 60 parts of 2,2,4-trimethylhexamethylene diisocyanate, 15 parts of dipropylene glycol methyl ether acetate, 20 parts of color paste, 15 parts of kaolin, 45 parts of talcum powder, 15 parts of precipitated barium sulfate, N,N-dimethyl 3.0 parts of cyclohexylamine, 0.7 parts of BYK-358N, 0.3 parts of BYK-066N, 0.4 parts of BYK-163; Alcohol 10 parts, dibutyltin diacetate 1.5 parts.

Embodiment 3

[0017] Solvent-free polyurethane acrylic floor material, the floor material includes A component and B component, the raw material composition of the A component is by weight: 10 parts of 2,2-dimethylol butanol, 50 parts of 2,2,4-trimethylhexamethylene diisocyanate, 12 parts of dipropylene glycol methyl ether acetate, 14 parts of color paste, 10 parts of kaolin, 30 parts of talcum powder, 10 parts of precipitated barium sulfate, N,N-dimethyl 2.5 parts of cyclohexylamine, 0.5 parts of BYK-358N, 0.1 parts of BYK-066N, 0.2 parts of BYK-163; Alcohol 5 parts, dibutyltin diacetate 1.0 parts.

[0018] The solvent-free polyurethane acrylic floor material of embodiment 1-3 is made according to following production method:

[0019] (1) First add 2,2-dimethylol butanol and 2,2,4-trimethylhexamethylene diisocyanate in component A into the reaction kettle in proportion, and stir the reaction at 110°C at 2600r / min 1.5h, after cooling to 75°C, add other raw materials of component A, and st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a solvent-free polyurethane-acrylate floor material, comprising assemblys A and B, the raw material compositions of the assembly A comprise trimethylol propane, 2,2,4-trimethylhexamethylene diisocyanate, di(propylene glycol) methyl ether acetate, color paste, kaolin, talc powder, precipitated barium sulfate, N,N-dimethylcyclohexylamine, BYK-358N, BYK-066N and BYK-163; and the raw material compositions of the assembly B comprise acrylic resin, diethylene glycol and dibutyltin diacetate. The solvent-free polyurethane-acrylate floor material of the invention is green and friendly to environment, is applicable to various fields, is suitable for indoor and outdoor application, has high decorative property, good weather resistance, good wear resistance, good impact resistance, good hardness, good anti-slip property, good temperature-change resistance, and good adhesion even without a grounding primer, and can be combined with epoxy, cement, polyurethane and other foundations for use with high gloss.

Description

technical field [0001] The invention belongs to the field of floor materials, and in particular relates to a solvent-free polyurethane acrylic floor material. Background technique [0002] The floor refers to the use of specific materials and processes to carry out construction treatment on the original ground and present a certain decorative and functional ground. It is suitable for some places that require relatively high sanitary conditions, such as hospital floors, food factory workshop floors, and pharmaceuticals. The floor of the workshop, the floor of the laboratory building, the floor of the machine room, etc.; with the improvement of people's living standards, the requirements for the floor have become higher, in addition to requiring a certain strength, stiffness, waterproof, moisture-proof, warm, wear-resistant, durable In addition to corrosion and other performance, in some places (such as track and field, sports field, etc.), the floor is also required to have t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/04C09D7/61C08G18/73C08G18/32
CPCC08G18/3206C08G18/73C08K2003/3045C09D7/61C09D175/04C08K13/02C08K3/34C08K3/346C08K3/30
Inventor 陈军军陈亮谢桂秀陈遵厚
Owner FUZHOU ROYAL FLOOR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com