Carrier for hydrogenation protection agent, and preparation method thereof, and catalyst

A technology for hydrogenation protection and catalyst, which is applied in catalyst carriers, chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, etc., can solve problems such as unfavorable precipitation and removal, and achieve large pore volume and Simple, efficient mass transfer and diffusion

Active Publication Date: 2019-05-07
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the content of pores with a pore diameter of more than 1000nm is low, which is not conducive to the precipitation and removal of iron, calcium, nickel and vanadium in residual oil

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carrier for hydrogenation protection agent, and preparation method thereof, and catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Weigh 500 grams of pseudoboehmite A1 (produced by Wenzhou Jingjing Alumina Co., Ltd., with a weight content of 70% on a dry basis) and roast at 470°C for 5 hours to prepare alumina.

[0038] Weigh 50 grams of the above-mentioned alumina and place it in 300 grams of 10% ammonium bicarbonate aqueous solution, transfer the mixed material into an autoclave, seal it, heat it at 150°C for 4 hours, and then dry the carrier at 100°C for 8 hours. The aluminum oxide was submerged in a 40% polyethylene glycol-6000 (molecular weight: 6000) solution for 1.5 hours, and then the carrier was dried at 100°C for 8 hours to obtain rod-shaped alumina clusters.

[0039] Weigh 85 grams of pseudo-boehmite A1 (manufactured by Wenzhou Jingjing Alumina Co., Ltd., with a weight content of 70% on a dry basis), 50 grams of the above-mentioned rod-shaped alumina clusters, and 1.5 grams of scallop powder, and mix the above-mentioned materials evenly , adding an appropriate amount of aqueous solution ...

Embodiment 2

[0042] Same as Example 1, except that the calcination temperature of pseudo-boehmite A1 is 530°C. The consumption of ammonium bicarbonate solution is 400 grams, and the mass concentration of solution is 12%. The heat treatment temperature is 170° C., and the treatment time is 4 hours. The polyethylene glycol-6000 solution was changed to polyethylene glycol-2000 (that is, the molecular weight is 2000) solution, and the mass concentration was 50%. The amount of rod-shaped alumina clusters added was 56 grams, and alumina carrier Z2 and hydrogenation protection catalyst C2 were obtained. The properties of alumina carrier Z2 are shown in Table 1.

Embodiment 3

[0044] Same as Example 1, except that the calcination temperature of pseudo-boehmite A1 is 490°C. The consumption of ammonium bicarbonate solution is 500 grams, and the mass concentration of solution is 13%. The heat treatment temperature is 150° C., and the treatment time is 8 hours. The polyethylene glycol-6000 solution was changed to polyethylene glycol-12000 (that is, the molecular weight is 12000) solution, and the mass concentration was 30%. The amount of rod-shaped alumina clusters added was 45 grams, and alumina carrier Z3 and hydrogenation protection catalyst C3 were obtained. The properties of alumina carrier Z3 are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a carrier for a hydrogenation protection agent, and a preparation method thereof, and a catalyst. The carrier is an alumina carrier, which contains a rod-like alumina cluster,wherein the rod-like alumina has a length of 2-6 [mu]m and a diameter of 100-300 nm, and the rod-like alumina cluster has an outer diameter of 8-25 [mu]m, and accounts for 35-49% of the weight of thealumina carrier. The preparation method of the carrier comprises: calcining pseudo-boehmite A to obtain alumina; immersing the alumina in an ammonium bicarbonate aqueous solution, carrying out sealingheat treatment, drying, soaking with a polyethylene glycol solution, and drying the soaked material to obtain a rod-like alumina cluster; and carrying out mixing kneading molding on pseudo-boehmite Band the rod-like alumina cluster, drying the molded material, and calcining to obtain the carrier. According to the present invention, with the application of the carrier as the residue oil hydrogenation protection catalyst, the characteristics of good macromolecular diffusion performance, strong impurity tolerance, high demetallization activity and the like can be achieved; and the carrier is particularly suitable for residue oil hydrotreating processes.

Description

technical field [0001] The invention relates to an alumina carrier, a catalyst and a preparation method thereof, in particular to a carrier, a catalyst and a preparation method thereof for a residual oil hydrogenation protecting agent. Background technique [0002] At present, hydroprocessing is still the most important means to produce high-quality, environment-friendly petroleum products. The core of hydroprocessing technology is the catalyst. For the hydroprocessing of heavy components of petroleum (such as VGO, especially residual oil), the pore size and pore volume of the catalyst will directly affect the activity of the catalyst. [0003] The main function of the residual oil hydrogenation protection catalyst is to remove iron, calcium, nickel and vanadium in the residual oil. The carrier materials used in the existing residual oil hydrogenation protection catalysts are generally macroporous alumina and its modified products. The commonly used preparation methods of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J21/04B01J32/00B01J23/882B01J23/883B01J23/888C10G45/08
Inventor 隋宝宽季洪海彭冲吕振辉关月明佟佳
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com