Catalyst carrier and supported catalyst, preparation method and application thereof, and method for producing hydrogen by steam reforming of methane

A catalyst carrier and carrier technology, which is applied in the direction of catalyst activation/preparation, catalyst carrier, chemical instruments and methods, etc., can solve the problem of poor carbon deposition resistance of catalysts, improve mechanical strength and hydration resistance, increase diffusion speed and The effect of relative adsorption capacity and strong anti-carbon performance

Active Publication Date: 2022-04-12
CHINA PETROLEUM & CHEM CORP +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the defect of poor anti-coking performance of the catalyst under low water-to-carbon ratio operating conditions in the hydrogen production process of methane steam reforming in the prior art, and to provide a catalyst carrier and its preparation method, a Supported catalyst and preparation method thereof, application of said support and supported catalyst in methane steam reforming reaction, and method for hydrogen production by methane steam reforming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst carrier and supported catalyst, preparation method and application thereof, and method for producing hydrogen by steam reforming of methane
  • Catalyst carrier and supported catalyst, preparation method and application thereof, and method for producing hydrogen by steam reforming of methane
  • Catalyst carrier and supported catalyst, preparation method and application thereof, and method for producing hydrogen by steam reforming of methane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0033] According to a preferred embodiment of the present invention, in the La modified alumina, La 2 o 3 The content is 0.1-6% by weight, preferably 0.5-3% by weight, more preferably 1.5-2.5% by weight.

[0034] The carrier that satisfies the aforementioned requirements of the present invention can realize the object of the present invention, and the present invention has no special requirements for its preparation method. For the present invention, the carrier described in the present invention is preferably prepared according to the following steps: the aluminum oxide containing La modified, CaCO 3 The mixture of , MgO, binder and pore-forming agent is ball-milled, then shaped and fired.

[0035] In the present invention, La-modified alumina, CaCO 3 , MgO, a binder and a pore-forming agent are ball-milled together, and then calcined to obtain a carrier with pores larger than 100 nm, and the pore volume of the pores larger than 100 nm accounts for 75-95% of the total pore...

Embodiment 1

[0097] (1) Preparation of La-modified alumina

[0098] 11.4g of La(NO 3 ) 2 9H 2 O was dissolved in 210mL of deionized water and stirred to dissolve, and 300g of pseudoboehmite was impregnated with it as the impregnating solution. After standing for 2 hours, the water was evaporated to dryness, and then calcined at 1200°C for 2 hours to obtain La-Al 2 o 3 -1. Among them, the content of La is 2% by weight, and the specific surface area is 71.4m 2 / g, the pore volume is 0.212cm 3 / g.

[0099] (2) Preparation of catalyst carrier

[0100] Weigh 130g of La-Al 2 o 3 -1, 30g of MgO, 18g of CaCO 3 , 1.05g magnesium stearate, 0.4g charcoal powder and 6mL carboxymethyl cellulose were mixed and ball milled for 20 hours to 100 mesh-150 mesh. Put the compressed pellet (diameter 1cm, thickness 3mm) into a muffle furnace and bake at 1200°C for 5 hours at a high temperature to obtain a catalyst carrier. The obtained support is denoted as LAMC-1, wherein the content of La modified ...

Embodiment 2

[0115] (1) Preparation of La-modified alumina

[0116] 8.4g of La(NO 3 ) 2 9H 2 O was dissolved in 210mL of deionized water and stirred to dissolve, and 300g of pseudo-boehmite was impregnated with it as the impregnating solution. After standing for 2 hours, the water was evaporated to dryness, and then calcined at 1300°C for 1 hour to obtain La-Al 2 o 3 -2. Among them, the content of La is 1.5% by weight, and the specific surface area is 64.5m 2 / g, the pore volume is 0.203cm 3 / g.

[0117] (2) Preparation of catalyst carrier

[0118] Weigh 120g of La-Al 2 o 3 -2, 28g of MgO, 22g of CaCO 3 , 1.05g magnesium stearate, 0.4g charcoal powder and 6mL carboxymethyl cellulose were mixed and ball-milled for 30 hours to below 100 mesh-150 mesh, and then poured into a mold for tableting after mixing and ball-milling evenly. The tablet molding pressure was 15MPa, and then Then put the compressed pellet (diameter 1cm, thickness 3mm) into a muffle furnace and bake at 1300°C for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of catalyst preparation, and discloses a catalyst carrier, a supported catalyst, a preparation method and application thereof, and a method for producing hydrogen by steam reforming of methane. The carrier includes La-modified alumina, CaO and MgO, and the carrier has Pores larger than 100 nm, and the pore volume of the pores larger than 100 nm accounts for 75-95% of the total pore volume of the carrier. The carrier provided by the invention has high strength and high hydrothermal stability. When the carrier provided by the invention is used to prepare a methane steam reforming catalyst, the dispersion degree of the active metal, the activity of the catalyst, the anti-coking performance and the structural stability can be significantly improved .

Description

technical field [0001] The invention relates to the field of catalyst preparation, in particular to a catalyst carrier, a method for preparing a catalyst carrier, a catalyst carrier prepared by the method, a supported catalyst, a method for preparing a supported catalyst, and a catalyst carrier prepared by the method. The obtained supported catalyst, the application of the carrier and the supported catalyst in methane steam reforming reaction and a method for producing hydrogen by methane steam reforming. Background technique [0002] In the chemical industry, the largest amount of hydrogen is used in synthetic ammonia and petroleum refining. In other fields, such as metallurgy, electronics, glass, medicine, food, aerospace, energy, etc., hydrogen is needed. In recent years, with the development of hydroreforming and hydrocracking in the refining process, the demand for hydrogen is increasing, and the demand for hydrogen in petrochemical industries such as synthetic ammonia,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J32/00B01J23/83B01J35/10B01J37/02B01J37/08C01B3/40
CPCY02P20/52
Inventor 张荣俊夏国富李明丰吴玉晋超孙霞侯朝鹏阎振楠
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com