A kind of preparation method of coated composite iron phosphide

An iron phosphide and coated technology, which is applied in the direction of chemical instruments and methods, chemical/physical processes, physical/chemical process catalysts, etc., can solve the problems of complex and cumbersome steps, strict equipment, high cost, etc., and achieve uniform particle size distribution, The effect of simple process and low cost

Active Publication Date: 2021-11-19
鲍君杰
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the current methods all have high cost, strict equipment, complicated and cumbersome steps, dangerous or expensive reaction raw materials, polluting by-products, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of coated composite iron phosphide
  • A kind of preparation method of coated composite iron phosphide
  • A kind of preparation method of coated composite iron phosphide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method of coated composite ferric phosphide, characterized in that it comprises the following steps:

[0038] (1) Add iron oxide red to citric acid and polyethylene glycol. After mixing, add pure water and add water to stir for slurry, then add phosphoric acid and cobalt acetate, stir to dissolve, and then use a jar mill to grind to a particle size of 0.7 μm ;

[0039] (2) Spray-dry the finely ground slurry in a spray dryer until the moisture content of the dried material is lower than 1%;

[0040] (3) Put the dry material into the rotary furnace, feed nitrogen gas at the same time, react at a temperature of 880°C for 4.2 hours, then cool to a temperature lower than 120°C, and then undergo airflow crushing, then classify in the classification chamber, after classification The material is screened to obtain coated composite iron phosphide.

[0041] In the step (1), the grinding balls in the pot mill are zirconia, alumina or stainless steel balls with a di...

Embodiment 2

[0053] A preparation method of coated composite ferric phosphide, characterized in that it comprises the following steps:

[0054] (1) Add iron oxide red to citric acid and polyethylene glycol. After mixing, add pure water and add water to stir for slurry, then add phosphoric acid and cobalt acetate, stir to dissolve, and then use a jar mill to grind to a particle size of 0.65 μm ;

[0055] (2) Spray-dry the finely ground slurry in a spray dryer until the moisture content of the dried material is lower than 1%;

[0056] (3) Put the dry material into the rotary furnace, feed nitrogen gas at the same time, react at a temperature of 865°C for 4.5 hours, then cool to a temperature lower than 120°C, and then undergo airflow crushing, then classify in the classification chamber, after classification The material is screened to obtain coated composite iron phosphide.

[0057] In the step (1), the grinding balls in the pot mill are zirconia, alumina or stainless steel balls with a d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of coated composite iron phosphide. Add iron oxide red to citric acid and polyethylene glycol. After mixing, add pure water and water to stir for slurry, then add phosphoric acid and cobalt acetate, stir to dissolve, and then use a tank mill to grind to a particle size of 0.5-0.8 μm; The finely ground slurry is spray-dried in a spray dryer until the moisture content of the dried material is lower than 1%; the dried material is put into a rotary kiln, and nitrogen is introduced at the same time, at a temperature of 850-900°C React for 3-5 hours, then cool to a temperature lower than 120°C, and then classify in a classifying chamber after jet crushing, and the classified materials are screened to obtain coated composite iron phosphide. The invention has simple process and low cost, and the obtained coated composite iron phosphide has uniform particle size distribution and high activity.

Description

technical field [0001] The invention relates to a method for preparing coated composite iron phosphide, which belongs to the field of waste recycling. Background technique [0002] Petroleum is processed to obtain abundant petroleum products, such as fuel, solvent, chemical raw material, etc., which are applied to various industries in the national economy. Among them, hydrofining is a very important process in reducing the sulfur content of heavy oil catalytic cracking gasoline. In order to realize clean oil production, it has become a research hotspot to develop and develop high-performance hydrodesulfurization catalysts. In addition to transition metal carbides and nitrides with excellent catalytic properties, transition metal phosphides are also considered to have the same properties. [0003] In previous studies, the effective methods to solve the heavy and inferior quality of petroleum are mainly hydrodesulfurization (HDS) and hydrodenitrogenation (HDN). However, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine