Special titanium dioxide for color masterbatch

A technology of titanium dioxide and color masterbatch, which is applied in the direction of titanium dioxide, titanium oxide/hydroxide, etc.

Inactive Publication Date: 2019-06-21
GUANGXI JINMAO TITANIUM
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The masterbatch titanium dioxide is located in the core layer of the masterbatch, so the requirements for whiteness, dispersibility, hiding power, processing torque performance, etc. are relatively high. The titanium dioxide obtained by the traditional process is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] 7) Hydrolysis

[0062] The purpose of hydrolysis is to obtain metatitanic acid, and its basic process includes the formation of crystallization centers, the growth of crystal nuclei and the formation of precipitates, the aggregation and precipitation of metatitanic acid particles and the change of solution composition. Anatase seeds need to be added during hydrolysis.

[0063] The specific process of hydrolysis is as follows:

[0064] 7.1) Measure the titanium solution prepared according to the process requirements and put it into the hydrolysis preheating pot and the seed titanium liquid tank respectively. When the liquid level reaches the stirring paddle, start the preheating pot to stir, and measure the ammonia water with a good concentration. Squeeze into the seed crystal ammonia water tank for standby;

[0065] 7.2) Wait for the seed crystal to be added after the material is finished. Start the stirring of the seed crystal production tank, open the discharge val...

Embodiment 2

[0069] 7) Hydrolysis

[0070] The purpose of hydrolysis is to obtain metatitanic acid, and its basic process includes the formation of crystallization centers, the growth of crystal nuclei and the formation of precipitates, the aggregation and precipitation of metatitanic acid particles and the change of solution composition. Anatase seeds need to be added during hydrolysis.

[0071] The specific process of hydrolysis is as follows:

[0072] 7.1) Measure the titanium liquid prepared according to the process requirements and pour it into the hydrolysis preheating pot and the seed titanium liquid tank respectively. When the liquid level reaches the stirring paddle, start the preheating pot to stir, and measure the ammonia water with a good concentration Squeeze into the seed crystal ammonia water tank for standby;

[0073]7.2) Wait for the seed crystal to be added after the material is finished. Start the stirring of the seed crystal production tank, open the discharge valve ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to special titanium dioxide for color masterbatch, wherein the content of titanium dioxide TiO2 is 95-97%, the rutile content is not less than 99.7%, the S element content is notmore than 3 ppm, the specific surface area is 350-370 m<2>/g, the agglomeration particle size D50 is 0.10-0.20 [mu]m, the agglomeration particle size D90 is less than or equal to 0.5 [mu]m, the volatile matter (105 DEG C, 2 h) is less than or equal to 1.5%, the burning loss (the sample is burned for 1 h after drying for 2 h at a temperature of 105 DEG C) is less than or equal to 8%, the pH valueof the aqueous suspension is 6.5-7.5, the water absorption is (30-35) g/50 g, the 45 [mu]m sieve residue is less than or equal to 0.04%, the oil absorption is 23-25 (g/100 g), Fe2O3 is less than or equal to 0.005%, and (K2O+Na2O) is less than or equal to 0.008%.

Description

technical field [0001] The invention belongs to the field of titanium dioxide production, and in particular relates to a preparation process of titanium dioxide specially used for producing plastic color masterbatches. Background technique [0002] Titanium dioxide scientific name titanium dioxide (TiO 2 ), there are mainly two crystal forms of rutile and anatase. Because of its superior whiteness, tinting strength, hiding power and other advantages, it has the highest refractive index among all white pigments, and is considered to be the best white pigment, so it is widely used in coatings, plastics, printing and rubber industries. As the second largest user of titanium dioxide, plastics can not only use its high hiding power, high tinting power and other pigment properties, but also improve the heat resistance, light resistance and weather resistance of plastic products. The masterbatch titanium dioxide is located in the core layer of the masterbatch, so the requirements...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01G23/053
Inventor 柴春旺
Owner GUANGXI JINMAO TITANIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products