Quick-drying environmental-protection ink preparation method
A fast-drying, environmentally friendly technology, applied in ink, household utensils, applications, etc., can solve the problems of UV gravure ink easy to precipitate, not resistant to strong acid etching, slow printing speed, etc., to achieve no ink residue, clean ink residue, The effect of increasing temperature
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0019] Mix 10 parts of C9 petroleum hydrocarbon resin, 0.1 part of polymerization inhibitor ST-1 and 15 parts of tripropylene glycol acrylate, and heat to 140°C to dissolve. Then add 15 parts of Cytec EB168 acrylic prepolymer, 0.2 parts of tert-butylcatechol, 4 parts of 4-phenylbenzophenone, 4 parts of 2-methyl-2-(4-morpholinyl)-1- [4-(methylthio)phenyl]-1-propanone, 10 parts of B-15:3 phthalocyanine blue, 2 parts of polymer dispersant BYK-163, stirred at 1000 rpm / min for 30 minutes. Pour the slurry into the bead ink machine, heat it to 60°C and grind it, grind it fully until the slurry fineness is less than 5 μm, add 20 parts of β-carboxyethyl acrylate, 20 parts of 1,6-hexanediol dipropylene Stir the ester evenly to get quick-drying environmental protection ink.
Embodiment 2
[0021] Mix 10 parts of C5 / C9 copolymer resin, 0.1 part of inhibitor ST-1 and 15 parts of tripropylene glycol acrylate, and heat to 140°C to dissolve. Then add 15 parts of Cytec EB168 acrylic prepolymer, 0.2 parts of tert-butylcatechol, 4 parts of 4-phenylbenzophenone, 4 parts of 2-methyl-2-(4-morpholinyl)-1- [4-(methylthio)phenyl]-1-propanone, 3 parts of B-15:3 phthalocyanine blue, 2 parts of polymer dispersant BYK-163, stirred at 1000rpm / min for 30 minutes. Pour the slurry into the bead ink machine, heat it to 60°C and grind it, grind it fully until the slurry fineness is less than 5 μm, add 23 parts of β-carboxyethyl acrylate, 24 parts of 1,6-hexanediol dipropylene Stir the ester evenly to get quick-drying environmental protection ink.
Embodiment 3
[0023] Mix 10 parts of C5 terpene-modified C5 resin, 0.1 part of polymerization inhibitor ST-1 and 15 parts of tripropylene glycol acrylate, and heat to 140°C to dissolve. Then add 15 parts of Cytec EB168 acrylic prepolymer, 0.2 parts of tert-butylcatechol, 4 parts of 4-phenylbenzophenone, 4 parts of 2-methyl-2-(4-morpholinyl)-1- [4-(methylthio)phenyl]-1-propanone, 6 parts of B-15:3 phthalocyanine blue, 2 parts of polymer dispersant BYK-163, stirred at 1000rpm / min for 30 minutes. Pour the slurry into the bead ink machine, heat it to 60°C and grind it, grind it fully until the slurry fineness is less than 5 μm, add 22 parts of β-carboxyethyl acrylate, 22 parts of 1,6-hexanediol dipropylene Stir the ester evenly to get quick-drying environmental protection ink.
PUM
Property | Measurement | Unit |
---|---|---|
softening point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com