A kind of method of carbon-coated waste lithium battery anode material

A technology for waste lithium batteries and anode materials, which is applied in battery recycling, regeneration of useful parts, recycling by waste collectors, etc. It can solve the problems of graphite material price rise, low density, and small thermal expansion coefficient, etc., and achieve charge retention High, high specific capacity, stable graphite structure effect

Active Publication Date: 2021-08-27
浙江卡波恩新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As an important source of energy for personal mobile devices, medical devices, and the automotive industry, commercial lithium batteries have grown rapidly in market size in the past two decades. Behind the huge market demand, there is a huge pressure on resource recovery, and carbon is currently commercialized. The most commonly used negative electrode material has the characteristics of good thermal conductivity and electrical conductivity, low density, small thermal expansion coefficient, corrosion resistance, small elasticity, non-toxic safety, simple preparation, low cost and high purity. According to the survey, there will be 52 million The kilograms of lithium battery anode materials have not been recycled, which will also lead to an increase in the price of graphite materials
[0003] In the prior art, lithium battery anode materials are recovered by using electrolysis method, ultrasonic stripping method, etc., but there is still room for further improvement in the effect of the recovered anode material, and the electrical conductivity of the material can be improved, thereby further improving the capacity and discharge performance of waste batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method of carbon-coated waste lithium battery anode material
  • A kind of method of carbon-coated waste lithium battery anode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Put the waste lithium battery into the electric tank and soak it for 100 minutes to dry, then disassemble the packaged waste lithium battery by combining manual and machine methods, and disassemble the rolled lithium battery negative electrode material into strips of carbon-coated copper Foil, put the carbon-coated copper foil into a temperature-controlled water washing pool with a stirring device, pour clean water into the pool until all the copper foil is submerged, heat the water in the pool to 70°C, and wait until the carbon powder is completely removed from the copper foil Stop stirring after washing, take out the copper foil without carbon powder attached after wet separation from the washing tank, dry and pack to complete the recovery of metal copper, at this time, the remaining material in the temperature-controlled washing tank is carbon powder ;

[0017] The above carbon powder was reflux treated with 3 mol / L nitric acid at 60°C for 8 hours, and washed with wa...

Embodiment 2

[0021] Put the waste lithium battery into the electric tank and soak it for 100 minutes to dry, then disassemble the packaged waste lithium battery by combining manual and machine methods, and disassemble the rolled lithium battery negative electrode material into strips of carbon-coated copper Foil, put the carbon-coated copper foil into a temperature-controlled water washing pool with a stirring device, pour clean water into the pool until all the copper foil is submerged, heat the water in the pool to 70°C, and wait until the carbon powder is completely removed from the copper foil Stop stirring after washing, take out the copper foil without carbon powder attached after wet separation from the washing tank, dry and pack to complete the recovery of metal copper, at this time, the remaining material in the temperature-controlled washing tank is carbon powder ;

[0022] The above carbon powder was reflux treated with 3 M nitric acid at 80°C for 10 h, and washed with water sev...

Embodiment 3

[0026] Put the waste lithium battery into the electric tank and soak it for 100 minutes to dry, then disassemble the packaged waste lithium battery by combining manual and machine methods, and disassemble the rolled lithium battery negative electrode material into strips of carbon-coated copper Foil, put the carbon-coated copper foil into a temperature-controlled water washing pool with a stirring device, pour clean water into the pool until all the copper foil is submerged, heat the water in the pool to 70°C, and wait until the carbon powder is completely removed from the copper foil Stop stirring after washing, take out the copper foil without carbon powder attached after wet separation from the washing tank, dry and pack to complete the recovery of metal copper, at this time, the remaining material in the temperature-controlled washing tank is carbon powder ;

[0027]The above carbon powder was reflux treated with 3 mol / L nitric acid at 70°C for 10 h, and washed with water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for coating the negative electrode material of a waste lithium battery with carbon, comprising the following steps: (1) dismantling and cleaning the waste battery, and treating the surface with carboxylated nano-graphite; (2) mixing nano-silicon powder with 3 ‑Aminopropyltriethoxysilane reaction to obtain surface aminated nano-silicon powder; (3) ball milling surface carboxylated nano-graphite sheet and surface-aminated nano-silicon powder mixture to obtain silicon-graphite sheet composite material; (4 ) using hexuronic acid as the coating carbon source, and adopting the liquid phase impregnation method to obtain the coated sample; (5) placing the coated sample in a tube furnace at 300-400°C for carbonization and heat preservation; (6) ball milling and sieving step (5) The obtained product is the carbon-coated silicon-based graphite sheet negative electrode material. The coated negative electrode material has a high charge retention rate and good cycle performance. The decommissioned negative electrode material can be reapplied to lithium batteries.

Description

technical field [0001] The invention relates to the field of lithium batteries, in particular to a method for carbon-coating anode materials of waste lithium batteries. Background technique [0002] As an important source of energy for personal mobile devices, medical devices, and the automotive industry, commercial lithium batteries have grown rapidly in market size in the past two decades. Behind the huge market demand, there is a huge pressure on resource recovery, and carbon is currently commercialized. The most commonly used negative electrode material has the characteristics of good thermal conductivity and electrical conductivity, low density, small thermal expansion coefficient, corrosion resistance, small elasticity, non-toxic safety, simple preparation, low cost and high purity. According to the survey, there will be 52 million The kilograms of lithium battery anode materials have not been recycled, which will also lead to an increase in the price of graphite mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/54H01M6/52
CPCH01M6/52H01M10/54Y02W30/84
Inventor 李建平朴良德
Owner 浙江卡波恩新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com