Firework decoration glaze and firework glaze jun porcelain and production method thereof

A technique for patterned glaze and fireworks, applied in the field of glaze, can solve the problems of fragile thermal stability, immature preparation method, not as good as one piece of Jun porcelain, etc., and achieves the effect of high hardness, smooth surface and thin glaze layer

Inactive Publication Date: 2019-08-23
大宋官窑股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Jun porcelain is one of the five famous porcelains of the Song Dynasty in my country. It is famous for its unique kiln transformation art. The unique national treasure porcelain in Shenhou Town, Zhouzhou City, with its simple shape, exquisite craftsmanship, and complex glaze matching, can achieve the magical kiln transformation of "one color in the kiln, and a variety of colors in the kiln". The infinitely changing graphic colors and wonderful flavors of fish, etc., are known as China's "Five Famous Porcelains". The preparation methods of Lihua glaze and Lihua glazed Jun porcelain in the prior art are not yet mature, and the surface is rough, easily broken and thermally stable. Therefore, it is very necessary to provide a kind of ceremony pattern glaze with simple process, smooth surface, high hardness and good thermal stability, ceremony flower glaze Jun porcelain and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A ceremony pattern glaze, a ceremony flower glaze, which is prepared from the following raw materials in parts by weight: 10-12 parts of quartz, 50-60 parts of feldspar, 5-6 parts of clay, 10-15 parts of crystals, and 20 parts of iron oxide -25 parts, 2-4 parts of zinc salt and 70-75 parts of solvent, etc.

[0020] A kind of ceremony pattern glaze, ceremony flower glaze Jun porcelain and preparation method thereof, comprising the following steps:

[0021] Step 1: Grinding and mixing quartz, feldspar and clay, then adding iron oxide, zinc salt and solvent for mixing and stirring; Step 2: Grinding the mixture of step 1 quartz, feldspar and clay, adding crystals, zinc salt and solvent Mixing and stirring; step 3: glaze the Jun porcelain obtained in step 1, and heat and fire; firing;

[0022] The volatile zinc salt used in the present invention reacts chemically with the surface of the green body to form a bright glaze layer. The prepared Lihua glaze Jun porcelain has a t...

Embodiment 2

[0024] A ceremony pattern glaze, a ceremony flower glaze, which is prepared from the following raw materials in parts by weight: 10-12 parts of quartz, 50-60 parts of feldspar, 5-6 parts of clay, 10-15 parts of crystals, and 20 parts of iron oxide -25 parts, 2-4 parts of zinc salt and 70-75 parts of solvent, etc.

[0025] A kind of ceremony pattern glaze, ceremony flower glaze Jun porcelain and preparation method thereof, comprising the following steps:

[0026] Step 1: Grinding and mixing quartz, feldspar and clay, then adding iron oxide, zinc salt and solvent for mixing and stirring; Step 2: Grinding the mixture of step 1 quartz, feldspar and clay, adding crystals, zinc salt and solvent Mixing and stirring; step 3: glaze the Jun porcelain obtained in step 1, and heat and fire; firing;

[0027] The crystallized product adopts zinc silicate, and the crystal diameter reaches 12mm; the described crystal product adopts manganese-cobalt, titanium silicate, silicon-zinc-titanium,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to firework decoration glaze and firework glaze jun porcelain and a production method thereof. Firework decoration glaze and firework glaze are produced from the following raw materials in parts by weight: 10-12 parts of quartz, 50-60 parts of feldspar, 5-6 parts of clay, 10-15 parts of crystals, 20-25 parts of ferric oxide, 2-4 parts of a zinc salt, 70-75 parts of a solventand the like. The production method comprises the following steps of (1) crushing and mixing the quartz, the feldspar and the clay, and then adding the ferric oxide, the zinc salt and the solvent formixing and stirring; (2) adding the crystals, the zinc salt and the solvent into a crushed mixture, in the step (1), of the quartz, the feldspar and the clay for mixing and stirring; (3) applying glaze obtained in the step (1) onto jun porcelain, and conducting heating and firing; and (4) conducting secondary glazing on the jun porcelain obtained in the step (3), and conducting heating and firing,wherein applied glaze is glaze obtained in the step (2). The firework decoration glaze and firework glaze jun porcelain and the production method thereof have the advantages that the technology is simple, the surface is smooth, the hardness is high, and the thermal stability is good.

Description

technical field [0001] The invention belongs to the technical field of glazes, and in particular relates to a ceremony pattern glaze, a ceremony flower glaze Jun porcelain and a preparation method thereof. Background technique [0002] Jun porcelain is one of the five famous porcelains of the Song Dynasty in my country. It is famous for its unique kiln transformation art. The unique national treasure porcelain in Shenhou Town, Zhouzhou City, with its simple shape, exquisite craftsmanship, and complex glaze matching, can achieve the magical kiln transformation of "one color in the kiln, and a variety of colors in the kiln". The infinitely changing graphic colors and wonderful flavors of fish, etc., are known as China's "Five Famous Porcelains". The preparation methods of Lihua glaze and Lihua glazed Jun porcelain in the prior art are not yet mature, and the surface is rough, easily broken and thermally stable. Therefore, it is very necessary to provide a kind of ceremony patter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86
Inventor 张怀强
Owner 大宋官窑股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap