Easy-to-pull tape and preparation method and use thereof

An easy-pull tape and tape technology, which is applied in the directions of adhesives, monocarboxylic acid ester copolymer adhesives, adhesive types, etc., can solve the problems of light and thin electronic products, large thickness, and many layers of easy-pull tapes. , to achieve the effect of easy stretching and removal, low thickness and less space occupied

Active Publication Date: 2019-08-30
东莞市古川胶带有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, at present, miniaturization and high integration are the mainstream trends in the development of electronic products. The pull-up tape with the above structure has the disadvantages of many layers and high thickness, which is not conducive to the thinning of electronic products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easy-to-pull tape and preparation method and use thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] This embodiment provides an easy-to-pull adhesive tape, comprising a double-sided release film and an adhesive layer arranged on one side of the double-sided release film;

[0051] The adhesive layer includes the following raw material components in weight percentage: 45% of EVA elastomer, 30% of acrylonitrile-butadiene-acrylate block copolymer, 10% of hyperbranched polyurethane, 10% of rosin resin, 3% of titanium dioxide % and isocyanate curing agent 2%;

[0052] Wherein, the weight-average molecular weight of the hyperbranched polyurethane is 3000; the content of the VA unit in the EVA elastomer is 60wt%, and the weight-average molecular weight is 12000; the weight-average molecular weight of the acrylonitrile-butadiene-acrylate block copolymer is 10000; The particle size of titanium dioxide is 10-20 μm.

[0053] The preparation method of above-mentioned easy-to-pull adhesive tape is as follows:

[0054] (1) Add EVA elastomer, acrylonitrile-butadiene-acrylate block ...

Embodiment 2

[0057] This embodiment provides an easy-to-pull adhesive tape, comprising a double-sided release film and an adhesive layer arranged on one side of the double-sided release film;

[0058] The adhesive layer includes the following raw material components in percentage by weight: 25% of EVA elastomer, 25% of acrylonitrile-butadiene-acrylate block copolymer, 20% of hyperbranched polyurethane, 8% of rosin resin, 5% of titanium dioxide %, unsaturated polycarboxylic acid polymer dispersant 5%, polyoxypropylene glyceryl ether 5%, acrylate film-forming agent 5% and isocyanate curing agent 2%;

[0059] Wherein, the weight-average molecular weight of the hyperbranched polyurethane is 5000; the content of the VA unit in the EVA elastomer is 50wt%, and the weight-average molecular weight is 8000; the weight-average molecular weight of the acrylonitrile-butadiene-acrylate block copolymer is 10000; The particle size of titanium dioxide is 1-5 μm.

[0060] The preparation method of above-me...

Embodiment 3

[0064] This embodiment provides an easy-to-pull adhesive tape, comprising a double-sided release film and an adhesive layer arranged on one side of the double-sided release film;

[0065] The adhesive layer includes the following raw material components in weight percentage: 25% of EVA elastomer, 45% of acrylonitrile-butadiene-acrylate block copolymer, 10% of hyperbranched polyurethane, 6% of terpene phenolic resin, titanium White powder 4%, unsaturated polycarboxylic acid polymer dispersant 4%, polyoxypropylene glyceryl ether 2%, acrylate film forming agent 2% and isocyanate curing agent 2%;

[0066] Wherein, the weight-average molecular weight of the hyperbranched polyurethane is 3000; the content of the VA unit in the EVA elastomer is 50wt%, and the weight-average molecular weight is 8000; the weight-average molecular weight of the acrylonitrile-butadiene-acrylate block copolymer is 15000; The particle size of titanium dioxide is 1-5 μm.

[0067] The preparation method of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides an easy-to-pull tape and a preparation method and use thereof. The easy-to-pull tape comprises a double-sided release film and an adhesive layer arranged on one side of the double-sided release film, wherein the adhesive layer comprises the following raw material component in percent by weight: 25-45% of an EVA elastomer, 25-45% of acrylonitrile-butadiene-acrylate block copolymer, 10-25% of hyperbranched polyurethane, 5-10% of tackifying resin, 2-5% of titanium dioxide and 1-5% of a curing agent. The easy-to-pull tape is prepared by a method of dissolving and dispersingthe raw material component of the adhesive layer in an organic solvent, performing coating on the double-sided release film, and performing heating, solidifying and drying. The provided easy-to-pull tape has good bonding performance, relatively high tensile strength and elongation at break, and is easily removed by stretching; and the easy-to-pull tape does not have a base film, the thickness is relatively low, the occupied space is relatively small, and thus the easy-to-pull tape is conducive to lightness and thinness of electronic products.

Description

technical field [0001] The invention belongs to the technical field of adhesive materials, and in particular relates to an easy-to-pull adhesive tape, a preparation method and application thereof. Background technique [0002] With the rapid development of electronics and communication technologies, electronic products such as smart phones and tablet computers have become an indispensable part of people's work and life. Most of these electronic products use fixed batteries. In order to securely fix the batteries, adhesives are used to fix the batteries on the motherboard. However, this will make it difficult to disassemble the components of electronic products, and it will be difficult to clean up the residual adhesive, which will bring difficulties to product maintenance and battery recycling. [0003] In this context, the easy-to-pull tape came into being. The easy-to-pull tape can realize the firm bonding of the battery and the motherboard in the direction perpendicular...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/10C09J131/04C09J153/00C09J175/04C09J11/04C09J11/08
CPCC08K2003/2241C08L2205/035C09J11/04C09J11/08C09J131/04C09J153/00C09J2431/00C09J2453/00C09J7/10C09J2301/308C08L53/00C08L75/04C08L93/04C08K3/22C08L31/04C08L61/14
Inventor 王建义徐宏飞王博文周雄安汪刘兵
Owner 东莞市古川胶带有限公司