Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Method for producing carved magnetic wood board porcelain tile

A porcelain tile, Jingdiao technology, applied in the field of preparation of Jingdiao magnetic wood large-slab porcelain tiles, can solve the problems of immature technology and complicated process requirements, and achieve the effects of protecting natural resources, reducing felling, and high hardness

Inactive Publication Date: 2019-09-13
广东冠星陶瓷企业有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional ceramic enterprises all produce porcelain tiles of regular size, and the process requirements for producing large-sized porcelain tiles are relatively complicated. Therefore, there are relatively few processes for producing large-sized porcelain tiles on the market, and the technology is not yet mature. , so the present invention proposes a preparation method of finely carved magnetic wood slab porcelain tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation method of a kind of finely carved magnetic wood slab porcelain brick of the present invention comprises the following steps:

[0027] S1: Put the purchased raw materials and 28% of the total amount of water into the ball mill in the raw material workshop for ball milling to form a slurry. The ball mill grinds the raw materials to a particle size of 80 μm, pump the slurry to the spray tower for powder making, and enter the powder bin After being stale and qualified, it is sent to the press workshop for use. The raw materials are made of the following ingredients by weight:

[0028] Potassium feldspar 15%, albite 10%, quartz sand 20%, clay 18%, raw talc 1.0%, additive 0.5%, and the additive is methyl cellulose.

[0029] S2: The powders of different grades are sent from the raw material workshop, pressed into bricks by a press, and put into the drying kiln for drying. The drying time is 1 hour, and the temperature of the drying kiln is set. is 100°C, the c...

Embodiment 2

[0037] The preparation method of a kind of finely carved magnetic wood slab porcelain brick of the present invention comprises the following steps:

[0038] S1: Put the purchased raw materials and 32% of the total amount of water into the ball mill in the raw material workshop for ball milling into slurry, the ball mill grinds the raw materials to a particle size of 100 μm, pump the slurry to the spray tower for powder making, and enter the powder bin After being stale and qualified, it is sent to the press workshop for use. The raw materials are made of the following ingredients by weight:

[0039] Potassium feldspar 20%, albite 15%, quartz sand 25%, clay 25%, raw talc 3.0%, additive 1.0%, and the additive is sodium silicate.

[0040] S2: The powders of different grades are sent from the raw material workshop, pressed into bricks by a press, and put into the drying kiln for drying. The drying time is 2 hours, and the temperature of the drying kiln is set. at 250°C, the chemi...

Embodiment 3

[0048] The preparation method of a kind of finely carved magnetic wood slab porcelain brick of the present invention comprises the following steps:

[0049] S1: Put the purchased raw materials and 29% of the total amount of water into the ball mill in the raw material workshop for ball milling to form a slurry. The ball mill grinds the raw materials to a particle size of 88 μm, pump the slurry to the spray tower for powder making, and enter the powder bin After being stale and qualified, it is sent to the press workshop for use. The raw materials are made of the following ingredients by weight:

[0050] Potassium feldspar 17%, albite 12%, quartz sand 22%, clay 20%, raw talc 1.5%, additive 0.7%, and the additive is a water reducer.

[0051] S2: The powders of different grades are sent from the raw material workshop, pressed into bricks by a press, and put into a drying kiln for drying. The drying time is 1.5 hours, and the temperature of the drying kiln is set. is 150°C, the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of production of porcelain tiles, and discloses a method for producing a carved magnetic wood board porcelain tile. A wood grain board with a concave and convex surface and a natural, smooth and realistic texture is produced by changing the thickness of the glazing amount and applying a carved ink, the specification of the product is 900 * 1800 MM, theproduct is cut as needed to obtain wood grain strips with various different specifications, the carved ink is also called sunken ink, and the ink has a certain pH value, is corrosive, and can form a surface concave-convex line when used in order to replace a wood carving machine. The product has the advantages of stable glaze color, strong glaze texture feeling, high hardness and ultralow water absorption rate (0.5% or below); compared with natural wood, the product of the invention is more durable, is not prone to be corroded and perforated, has a surface gloss of 10-15 DEG, avoids waxing treatment during use, has good anti-fouling and anti-slip performances, and is an ideal choice for home; and the product of the invention has better performances than real wood, so the felling of wood isreduced.

Description

technical field [0001] The invention relates to the technical field of porcelain tile preparation, in particular to a method for preparing finely carved porcelain tiles made of large slabs of magnetic wood. Background technique [0002] Porcelain tiles have the texture of natural stone, and have the advantages of high gloss, high hardness, high wear resistance, high stain resistance, low water absorption, less color difference, diverse specifications and rich colors. They are commonly used wall surfaces in bathrooms. and ground materials. [0003] Traditional ceramic enterprises all produce porcelain tiles of regular size, and the process requirements for producing large-sized porcelain tiles are relatively complicated. Therefore, there are relatively few processes for producing large-sized porcelain tiles on the market, and the technology is not yet mature. , so the present invention proposes a preparation method of finely carved magnetic wood slab porcelain tiles. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/19C04B35/622C04B35/626C04B41/86C03C8/00
CPCC03C8/00C04B35/19C04B35/622C04B35/62605C04B41/5022C04B41/86C04B2235/3418C04B2235/349C04B2235/6567
Inventor 江想健万祖安周海龙黄大平陈彦龙王丽红彭斐谭荧坚
Owner 广东冠星陶瓷企业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More