Preparation method of ethylene copolymer

A technology for the polymerization of ethylene copolymers and olefins, which is applied in the field of preparation of ethylene copolymers, can solve problems such as complex catalyst preparation processes, and achieve the effects of low cost, high catalytic activity, and simple preparation methods

Active Publication Date: 2021-10-19
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation process of this catalyst is relatively complicated, and the yield is only about 70%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of ethylene copolymer
  • Preparation method of ethylene copolymer
  • Preparation method of ethylene copolymer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The present invention provides a method for preparing ethylene copolymer, wherein the method comprises: under olefin polymerization conditions, in the presence of an inert solvent, contacting ethylene, a comonomer and a catalyst, wherein the catalyst contains the formula ( I) post-metallocene catalyst precursors, borides and alkylaluminum compounds based on diacetylenylphenols,

[0018]

[0019] In formula (I), R 1 for hydrogen, C 1 -C 20 straight-chain or branched-chain alkyl or trimethylsilyl; R 2 for hydrogen, C 1 -C 20 straight-chain or branched-chain alkyl or phenyl; R 3 , R 4 , R 5 , R 6 and R 7 for hydrogen or C 1 -C 20 straight-chain or branched-chain alkyl; M is one of titanium, zirconium and hafnium; X 1 and x 2 The same or different, each independently halogen.

[0020] Among them, the C 1 -C 20 Specific examples of straight-chain or branched-chain alkyl groups may include, but are not limited to: methyl, ethyl, n-propyl, isopropyl, n-butyl...

preparation example 1

[0064] This preparation example is used to illustrate the preparation of the post-metallocene catalyst precursor with the structure represented by formula (II).

[0065] Dissolve 4-tert-butyl-2,6-bis(trimethylsilylacetylene)phenol (3.00mmol) in 30mL ether solvent, add n-hexane containing n-butyllithium to the solution at -78°C The solution (the concentration of n-butyllithium in the n-hexane solution is 1.67M, and the amount of n-butyllithium used is 3.00mmol) was reacted for 1 hour, returned to 25° C., and continued to react for 15 minutes. A compound having a structure represented by formula (VII) is obtained.

[0066]

[0067] At -78 ° C, the solution of the compound containing the structure shown in the formula (VII) obtained above was transferred to the titanium metal complex (3.00 mmol) containing the cyclopentadienyl group of the structure shown in the formula (VIII) through a double angle needle in ether solution (the amount of ether used is 30 mL), and reacted at ...

preparation example 2

[0072] This preparation example is used to illustrate the preparation of the post-metallocene catalyst precursor with the structure represented by formula (II).

[0073] Dissolve 4-tert-butyl-2,6-bis(trimethylsilylacetylene)phenol (3.00mmol) in 30mL of dichloromethane solvent, and add n-butyllithium to the solution at -78°C n-hexane solution (the concentration of n-butyllithium in the n-hexane solution is 1.67M, the amount of n-butyllithium used is 3.00mmol) and then reacted for 1 hour, returned to 20°C, and continued to react for 15 minutes. A compound having a structure represented by formula (VII) is obtained.

[0074] At -78°C, the solution of the compound containing the structure shown in the formula (VII) obtained above was transferred to the titanium metal complex (3.00 mmol) containing the cyclopentadienyl group of the structure shown in the formula (VIII) through a double angle needle in dichloromethane solution (the amount of dichloromethane used is 30 mL), and reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of olefin coordination polymerization, and discloses a method for preparing an ethylene copolymer. The method comprises: contacting ethylene and a comonomer with a catalyst in the presence of an inert solvent under olefin polymerization conditions, and the catalyst contains the formula The post-metallocene catalyst precursor, boride and alkylaluminum compound based on diacetylenylphenol shown in (I), in formula (I), R 1 for hydrogen, C 1 -C 20 straight-chain or branched-chain alkyl or trimethylsilyl; R 2 for hydrogen, C 1 -C 20 straight-chain or branched-chain alkyl or phenyl; R 3 , R 4 , R 5 , R 6 and R 7 for hydrogen or C 1 -C 20 straight-chain or branched-chain alkyl; M is one of titanium, zirconium and hafnium; X 1 and x 2 The same or different, each independently halogen. The preparation of the ethylene copolymer by the method has high catalytic efficiency, and the introduction ratio of the comonomer is relatively high, and the preparation process of the post-metallocene catalyst precursor used is simple.

Description

technical field [0001] The invention relates to the field of olefin coordination polymerization, in particular to a preparation method of an ethylene copolymer. Background technique [0002] Since the beginning of the 21st century, with the improvement of the national economy and the needs of the national defense industry, polymer materials, especially polyolefin materials, have played an increasingly important role: due to the abundance and low cost of polyolefin raw materials, easy processing and molding, every year in the world The polyolefin products produced within the scope exceed 100 million tons, becoming one of the largest industries; polyolefin materials have relatively small density, good chemical resistance, water resistance, good mechanical strength, electrical insulation, etc. Features, can be used for films, pipes, plates, various shaped products, wires and cables, etc., not only widely used in agriculture, packaging, automobiles, electrical appliances and oth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F210/16C08F210/14C08F4/6592C08F2/06
CPCC08F210/14C08F210/16C08F2420/04C08F4/6592C08F2/06
Inventor 韩书亮吴宁郝建国陈淑明徐林王超
Owner CHINA PETROLEUM & CHEM CORP