A kind of two-component water-based adhesive for automotive interior decoration and preparation method thereof

A water-based adhesive, two-component technology, applied in the direction of adhesives, adhesive types, epoxy resin glue, etc., can solve the problems of high price, unstable bonding effect, etc., achieve improved performance and good application prospects , cost reduction effect

Active Publication Date: 2021-10-26
YANTAI UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adhesives used in the bonding of automotive interior materials need to have good initial tack, heat resistance, environmental stability (resistance to -40°C and 80°C under 80% humidity environment without opening, and pass the PV1200 test) and no odor , has high requirements in performance, and there are few related products in China. The production method of adhesives for automotive interiors introduced in the patent CN102863938B_CN is mainly through the compounding of foreign water-based polyurethane adhesives; currently foreign countries are used for automotive interiors The water-based adhesive for decoration is mainly a two-component system composed of hydroxyl water-based polyurethane and water-dispersed polyisocyanate. During the curing and drying process, the hydroxyl group and -NCO undergo a cross-linking reaction to form a cross-linked structure, which has good heat resistance and environmental protection. Stability, but this type of product has the disadvantages of high price of water-dispersible polyisocyanate, and the side reaction of -NCO and water makes the bonding effect unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of two-component water-based adhesive for automotive interior decoration and preparation method thereof
  • A kind of two-component water-based adhesive for automotive interior decoration and preparation method thereof
  • A kind of two-component water-based adhesive for automotive interior decoration and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] 1. Add 51g oligomer polyol (PEPA, molecular weight 2000, Huada Chemical Group Co., Ltd.), 24.3g IPDI, 0.19g bismuth laurate catalyst at 50°C, heat up to 85°C for 60min, cool to 60°C, add 12.8 g non-ionic hydrophilic monomer polyethylene glycol (PEG1000), 2.79g small molecule chain extender (1,4-butanediol, BDO), react for 30min, heat up to 80°C for 2h, cool down to 50°C and add 28.6 g acetone, add dropwise 2.08 g of sulfonic acid hydrophilic chain extender sodium ethylenediaminoethanesulfonate (AAS) for 30 min, cool down to room temperature, add 7.0 g of epoxy 828, and stir for 2 min to synthesize a polyurethane prepolymer.

[0052] II. Add 180g of deionized water to the polyurethane prepolymer for emulsification, stir at 1000r / min for 5min, then add 3.65gIPDA dropwise at 500r / min, finish adding dropwise in 20-40min, continue to react for 1h, remove the solvent in vacuum to obtain an emulsion.

[0053] III. Add 1% of polyurethane prepolymer quality non-ionic associative...

Embodiment 2

[0056] Add oligomer polyol under 1, 50 ℃, comprise: 35g polyester polyol (PEPA, molecular weight 2000), polypropylene glycol (molecular weight 2000) 10.5g, 27.5g dicyclohexylmethane diisocyanate, 0.18g bismuth laurate catalyst , heat up to 85°C for 60 minutes, cool down to 60°C, add 12.6g PEG1000, 2.5g 1,4-butanediol, react for 30min, heat up to 80°C for 2h, cool down to 50°C, add 27.5g of acetone, dropwise add 2.1g of ethyl alcohol Sodium diaminopropanesulfonate (A95, Beijing Baiyuan Chemical Co., Ltd.) was reacted for 30 minutes, cooled to room temperature and added with 7.0 g of epoxy E-44, 2.02 g of HDI trimer HT-100 (Wanhua Chemical Group Co., Ltd.), 0.87g KH560, stirred for 2min, to synthesize polyurethane prepolymer.

[0057] II. Add 78g of deionized water to the polyurethane prepolymer for emulsification, stir at 1500r / min for 5min, then add 3.72gIPDA dropwise at 300r / min, finish adding dropwise in 20-40min, continue to react for 1h, and remove the solvent in vacuum to...

Embodiment 3

[0061] 1. Add 28g polyester polyol (PEPA), 23.8gIPDI, 0.18g bismuth laurate catalyst at 50°C, heat up to 85°C for 60min, cool to 60°C, add 17.5g butanone, 12.6g PEG1000, 17.5g sulfonic acid Salt diol BY3305B (Beijing Baiyuan Chemical Co., Ltd.) 2.50g 1,4-butanediol, react for 30min, heat up to 80°C for 3h, cool down to 50°C, add 10.8g of acetone, dropwise add 1.75g ​​of silane coupling agent KH550 for reaction After 30 minutes, cool down to room temperature and add 14.0g epoxy E-828, stir for 2 minutes to synthesize polyurethane prepolymer.

[0062] II. Add 174g of deionized water to the polyurethane prepolymer for emulsification, stir at 1500r / min for 5min, then add 6.6gIPDA dropwise at 500r / min, finish adding dropwise in 20-40min, continue to react for 1h, and remove the solvent in vacuum to obtain an emulsion.

[0063] III. Add 0.2% sodium carboxymethylcellulose thickener (Jinan Haoju Chemical Co., Ltd.) of polyurethane prepolymer and 0.1% preservative of polyurethane prepo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based adhesive for automobile interior decoration and a preparation method thereof. The adhesive is a two-component water-based adhesive, wherein the synthesis process of component A is firstly oligomer polyol, non-ionic hydrophilic monomer, polyisocyanate, small molecule chain extender, sulfonate-containing hydrophilic Chain extender or polyol containing sulfonic acid groups introduce sulfonate groups into the molecular chain of polyurethane prepolymer, add a certain amount of silane coupling agent, epoxy resin, stir evenly, add water and stir to emulsify, add amine chain extender after emulsification It reacts with epoxy group and ‑NCO to form a polyurethane emulsion containing amino groups; component B is water-based epoxy resin, mix components A and B in a certain proportion, and add a water-based thickener to adjust the viscosity of the emulsion to form a new The adhesive system is used for the bonding of automotive interior materials. It has the characteristics of good initial tack, heat resistance, environmental stability and no odor, and meets the requirements for the use of automotive interior materials.

Description

technical field [0001] The invention relates to the technical field of fine chemicals, in particular to a non-odor, two-component water-based adhesive, a preparation method and application thereof. Background technique [0002] In 2016, China's total automobile production and sales were 28.119 million and 28.028 million respectively, making it the world's largest automobile production and sales country. Automotive interiors are also an important area of ​​growth in adhesive usage. Adhesives commonly used in the automotive industry are mainly solvent-based, water-based and hot-melt. Solvent-based adhesives are restricted in use because of their volatile organic solvents that pollute the environment and endanger human health. Water-based adhesives are an important development direction to replace traditional solvent-based adhesives because they are non-toxic, non-flammable, and easy to use. Adhesives used in the bonding of automotive interior materials need to have good init...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/04C09J163/00
CPCC08L2201/08C09J175/04C08L63/00
Inventor 侯立杰刘志勇季明航刘咏杭张守鹏徐同辉李世宇艾仕利刘悦杨雪吴现
Owner YANTAI UNIV