Processing technology of modified carbon fibers

A processing technology, carbon fiber technology, applied in the direction of carbon fiber, fiber treatment, fiber chemical characteristics, etc., can solve the problems of poor performance of composite materials, achieve the effect of increasing roughness, increasing shear strength, and improving compactness

Inactive Publication Date: 2019-11-01
DATONG XINCHENG NEW MATERIAL CO LTD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the smooth surface of carbon fiber, after the reinforcement material is compounded, it often cannot be in close contact with the composite material, resulting in poor performance of the composite material after synthesis.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] In order to make the purpose, technical solution and advantages of the present invention clearer, the technical solution of the present invention will be described in detail below. Apparently, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other implementations obtained by persons of ordinary skill in the art without making creative efforts fall within the protection scope of the present invention.

[0021] The invention provides a kind of processing technology of modified carbon fiber, comprising the following steps:

[0022] Step a. Pull back the thread collection line, select the original thread, and connect the new thread and the old thread with heat-resistant fibers after splitting, and erect them on the thread collection board;

[0023] Step b, initial drying, send the wire collecting plate together with the raw silk into the drying equipment to dry, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing technology of modified carbon fibers. The processing technology comprises the following steps of a, filament return and thread collection, wherein a protofilamentis selected, after splitting, a new filament and an old filament are connected with a heat-resistant fiber, and the mixture is erected on a thread collection plate; b, primary drying, wherein the thread collection plate and the protofilament are conveyed into a drying device for drying, and the moisture in the protofilament is removed; c, preoxidation; d, carbonization; e, electrolytic oxidation modification; f, soaking modification. The processing technology has the advantages that an electrolytic oxidation mode is adopted for modifying the surfaces of the carbon fibers, active functional groups are introduced into the surfaces of the carbon fibers, the carbon oxygen bonds of the surfaces of the carbon fibers are increased, the contact compactness of the carbon fibers and the surface of acomposite material in the compounding process is improved, and the increase and decrease shearing strength of the synthesized composite material is improved; the interface bonding force of a bondingface is improved, and accordingly the tensile strength and impact-resistance strength of the carbon fiber and resin base material composite material is improved.

Description

technical field [0001] The invention relates to the technical field of carbon fiber production, in particular to a processing technology for modified carbon fiber. Background technique [0002] Carbon fiber is a new fibrous material with high temperature resistance, friction resistance, electrical conductivity, thermal conductivity and corrosion resistance. It can be processed into fabrics or combined with organic materials to form composite materials with excellent performance. In the prior art, carbon fiber is often used as a reinforcing material to be compounded with resin, metal, ceramics and carbon, etc., and processed into a high-strength composite material. Among them, the specific strength and specific modulus of carbon fiber reinforced epoxy resin composite materials are the most important in existing projects. The highest in the material. Due to the smooth surface of carbon fiber, after the reinforcement material is compounded, it often cannot be in close contact ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F9/12D06M10/02D06M13/352C25D11/00D06M101/40
CPCC25D11/00D01F9/12D06M10/02D06M13/352D06M2101/40
Inventor 柴万红
Owner DATONG XINCHENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products