Anticorrosive coating applied to steel surfaces and spraying process

A technology for anti-corrosion coatings and steel surfaces, which is applied to anti-corrosion coatings, devices for coating liquids on surfaces, and pretreatment surfaces, etc. It can solve problems such as self-healing, poor solution stability, farmland pollution and crop production stoppage, etc., to reduce materials and Construction cost, long-term anti-corrosion life, simple effect of spraying process

Inactive Publication Date: 2019-11-22
广东天丛新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the chemical pollution of the pickling and phosphating process will cause huge damage to the environment.
The strong acid treatment solution will pollute the farmland and stop the production of crops, and the phosphating treatment solution will cause eutrophication of the water body if it is not properly treated, and a large number of algae will appear, which will affect the ecology of the water body
The sewage treatment standard requires a rather complicated process
In recent years, environmentally friendly phosphating substitute products (zirconium series, silane treatment) have technical defects: poor washing resistance after film formation, poor solution stability, and inability to self-heal
[0003] The chemical pollution of the pickling and phosphating process will cause huge damage to the environment
The strong acid treatment solution will pollute the farmland and stop the production of crops, and the phosphating treatment solution will cause eutrophication of the water body if it is not properly treated, and a large number of algae will appear, which will affect the ecology of the water body
The sewage treatment standard requires a rather complicated process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of anticorrosion paint applied on the surface of steel, comprising the following parts by weight: 40-50 parts of epoxy resin, 30-60 parts of potassium oxide, 100-200 parts of deionized water, 35-61 parts of silicon dioxide, polyether polyurethane 15-30 parts of epoxy resin, 50-70 parts of antirust filler, 50-80 parts of wetting agent, 45-60 parts of defoamer, 20-50 parts of strontium chrome yellow, 40-60 parts of isooctyl methacrylate , 50-80 parts of xylene, 50-70 parts of toluene diisocyanate.

[0020] A kind of spraying process of the anticorrosion coating applied on steel surface, comprises the following steps:

[0021] S1, removing floating rust from the steel surface;

[0022] S2, cleaning the steel surface to remove oil and dust;

[0023] S3. After the steel is left to dry, it can be sprayed with anti-corrosion materials. First, apply a thin layer and let it stand for a few minutes;

[0024] S4, carrying out two cross thick coating sprayings to steel; ...

Embodiment 2

[0031] A kind of anticorrosion paint applied on steel surface, it is characterized in that, comprises following parts by weight, epoxy resin 40 parts, potassium oxide 30 parts, deionized water 100 parts, silicon dioxide 35 parts, polyether type polyurethane epoxy resin 15 parts 50 parts, antirust filler 50 parts, wetting agent 50 parts, defoamer 45 parts, strontium chrome yellow 20 parts, isooctyl methacrylate 40 parts, xylene 50 parts, toluene diisocyanate 50 parts.

Embodiment 3

[0033] A kind of anticorrosion paint applied on steel surface, it is characterized in that, comprises following parts by weight, epoxy resin 45 parts, potassium oxide 45 parts, deionized water 150 parts, silicon dioxide 48 parts, polyether type polyurethane epoxy resin 27 parts 60 parts, antirust filler 60 parts, wetting agent 65 parts, defoamer 50 parts, strontium chrome yellow 35 parts, isooctyl methacrylate 50 parts, xylene 65 parts, toluene diisocyanate 60 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses anticorrosive coating applied to steel surfaces. The anticorrosive coating comprises the following components in parts by weight, 40-50 parts of epoxy resin, 30-60 parts of potassium oxide, 100-200 parts of deionized water, 35-61 parts of silicon dioxide, 15-30 parts of polyether type polyurethane epoxy resin, 50-70 parts of an antirust filler, 50-80 parts of a wetting agent, 45-60 parts of a defoaming agent, 20-50 parts of strontium yellow, 40-60 parts of isooctyl methacrylate, 50-80 parts of xylene and 50-70 parts of toluene diisocynate. The coating can be directly sprayed on steel or a steel structure without the need of pretreatment such as acid pickling and phosphating, achieving a disruptive change for traditional coating spraying processes, and thoroughly overcoming chemical pollution generated by pretreatment. The solid content of traditional solvent type anticorrosive coating can only reach 30-40%, the solid content of the disclosed coating can reach 78.7%, solvent is reduced, and the disclosed coating shows good environmental protection performance.

Description

technical field [0001] The invention relates to the field of spray protection, in particular to an anti-corrosion paint applied on steel surfaces and a spray process. Background technique [0002] The surface spraying of steel or steel structures still relies heavily on the pre-treatment process of pickling and phosphating, so that the coating can have a good bonding force with the surface of the workpiece and produce products that meet the requirements. There is generally an oxide layer on the surface of the steel or steel structure product, which will affect the bonding force with the coating. In order to remove the oxide layer, it is necessary to pickle the workpiece to enhance the corrosion resistance and bonding force of the workpiece. However, the chemical pollution of the pickling and phosphating process will cause great damage to the environment. The strong acid treatment solution will cause the farmland to pollute the crops to stop production, and the slightly impr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D4/06C09D5/08C09D7/61B05D3/02B05D7/00B05D7/14B05D7/24
CPCB05D3/0254B05D7/14B05D7/24B05D7/54B05D2503/00B05D2504/00C09D4/06C09D5/08C09D7/61B05D2420/01B05D2420/02
Inventor 王文超张建
Owner 广东天丛新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products