High-adhesion ink for water-based gravure plastic films and preparation method of high-adhesion ink

A technology of plastic film and high adhesion, applied in the field of ink, can solve the problems of fluidity, poor adhesion fastness, easy anti-adhesion and migration, etc., achieve low VOC content, excellent color and good friction resistance

Inactive Publication Date: 2019-12-03
佛山市红树水性印涂材料有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the problems that the existing water-based gravure plastic film surface printing ink also has poor fluidity and adhesion fastness, and is prone to anti-sticking and migration during printing, the invention provides a water-based gravure plastic film high adhesion ink and its preparation method , the ink is safe and environmentally friendly, with low VOC content and low odor; good fluidity; high color concentration of printed products, excellent color, good adhesion fastness; printed products have good anti-blocking, anti-migration, and friction resistance, and can replace gravure plastic films Solvent Ink

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The water-based gravure plastic film high adhesion ink of the present embodiment, its component ratio by weight is: 50 parts of water-based acrylic resin, 10 parts of extra black 6500, 10 parts of deionized water, 5 parts of ethanol, same as Xianghongye's 0.5 parts of 180 defoamer, 1 part of monoethanolamine, 3 parts of Guangzhou Duwei quick-drying agent, and 0.5 parts of wax powder. Wherein: the weight percentage of water-based water-based acrylic resin is: 28.6% of dimethyl ester, 15.4% of butyl acrylate, 8.3% of acrylic acid, 8.3% of ammonia water, 1.6% of potassium persulfate, and 37.8% of ethanol.

Embodiment 2

[0031] The water-based gravure plastic film high adhesion ink of the present embodiment, its component ratio by weight is: 60 parts of water-based acrylic resin, 15 parts of titanium dioxide 996 of Lomon, 10 parts of deionized water, 4 parts of ethanol, isopropyl 1 part of alcohol, 0.5 part of Tego's 1488 defoamer, 1 part of monoethanolamine, 3 parts of propylene glycol, and 0.5 part of wax powder. Wherein: the weight percentage of water-based water-based acrylic resin is: 28.6% of dimethyl ester, 15.4% of butyl acrylate, 8.3% of acrylic acid, 8.3% of ammonia water, 1.6% of potassium persulfate, and 37.8% of ethanol.

Embodiment 3

[0033] The water-based gravure plastic film high-adhesion ink of this embodiment has the following components by weight: 70 parts of water-based acrylic resin, 10 parts of Zhengyan's phthalocyanine blue 15:3, 10 parts of deionized water, and 5 parts of ethanol ,, Tongxiang Hongye's 180 defoamer 0.5 parts, one ethanolamine 1 part, Guangzhou Duwei quick-drying agent 3 parts, wax powder 0.5 parts. Wherein: the weight percentage of water-based water-based acrylic resin is: 28.6% of dimethyl ester, 15.4% of butyl acrylate, 8.3% of acrylic acid, 8.3% of ammonia water, 1.6% of potassium persulfate, and 37.8% of ethanol.

[0034] The preparation method of the above examples is as follows: firstly weigh each raw material according to the above-mentioned ratio of parts by mass; then mix and stir the water-based acrylic resin, coloring agent, solvent and defoamer, and then grind until the fineness of the raw materials is lower than 15 μm. Grind; then add other additives except defoamer, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
photostabilityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of printing ink, and discloses high-adhesion ink for water-based gravure plastic films. The high-adhesion ink is prepared from the following components inparts by weight: 50 to 70 parts of water-based acrylic resin, 10 to 15 parts of a coloring agent, 15 to 25 parts of a solvent and 5 to 6 parts of auxiliary agents, wherein the base materials of the water-based acrylic resin are dimethyl ester, butyl acrylate and acrylic acid. The preparation method comprises the following steps: weighing the raw materials according to mass parts; then mixing the water-based acrylic resin, the coloring agent, the solvent and the defoaming agent by stirring, and then grinding the mixture until fineness of the raw materials is 15 microns or lower; then adding auxiliary agents except the defoaming agent, and carrying out uniform mixing and stirring again until the viscosity reaches 24-28 s / 25 DEG C of Zahn 4# cup; and finally carrying out filtration and packaging. The ink is safe and environmentally friendly, and is low in volatile organic compound (VOC) content and small in smell; flowability is good; a printed product is high in color concentration, excellent in color and luster and good in adhesion fastness; the printed product has good anti-blocking, anti-migration and anti-friction properties; and the high-adhesion ink can replace solvent-based ink for gravure plastic films.

Description

technical field [0001] The invention relates to the technical field of inks, in particular to a water-based gravure plastic film high adhesion ink and a preparation method thereof. Background technique [0002] With the continuous improvement of people's living standards, environmental protection and green are the general trend of today's printing and packaging industry. Therefore, non-toxic, harmless, non-flammable, non-explosive, low VOC emissions and other requirements have been put forward for gravure plastic film inks. The country has also issued the Environmental Protection Industry Standard of the People's Republic of China HJ / T371-2007 "Technical Requirements for Environmental Labeling Products Gravure Printing" Inks and Flexo Inks". In terms of gravure plastic film surface printing inks, it is imperative to replace solvent-based inks with water-based inks, and corresponding technical environmental protection standards have been formulated for this. This standard s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/107C09D11/033C09D11/03C08F220/14C08F220/18C08F220/06
CPCC09D11/107C09D11/033C09D11/03C08F220/14
Inventor 缪优房陈建平梁悦国关志坚
Owner 佛山市红树水性印涂材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com