Antibacterial ceramic glaze, and preparation method and application thereof

A technology of antibacterial ceramics and ceramic glazes, applied in the field of architectural ceramics, can solve the problems that antibacterial agents cannot achieve the ideal antibacterial effect, antibacterial agents are easy to agglomerate, and infection, etc., to achieve stable and sustainable sterilization effects, high-efficiency sterilization and antibacterial effects, and guaranteed coverage effect

Inactive Publication Date: 2020-02-21
FOSHAN DONGPENG CERAMIC +3
View PDF10 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As ceramic tiles commonly used in people's living rooms, there will always be some dead spots for pollution and bacterial growth, especially in places such as home kitchens and bathrooms, where bacteria are prone to breed. The surface of ceramic tiles has tiny pinholes that are invisible to the naked eye. After a long time, bacteria are easy to accumulate, breed and even infect, seriously affecting the hea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial ceramic glaze, and preparation method and application thereof
  • Antibacterial ceramic glaze, and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0041] A preparation method of antibacterial ceramic glaze, the antibacterial agent is added to the ceramic glaze according to the weight percentage and mixed evenly, the suspending agent and the debonding agent are added into the ceramic glaze containing the antibacterial agent according to the weight percentage After mixing the raw materials evenly, add water and ball mill for 5-12 hours to obtain the antibacterial ceramic glaze, wherein the fineness of the ball-milling slurry is that a specific gravity cup passes through a 325-mesh sieve, the sieve residue is 0.5-0.8%, and the flow rate is 30 ~50 seconds.

[0042] After adding the antibacterial agent and the conventional ceramic glaze and mixing evenly, then adding the suspending agent and the debonding agent to improve the mixing uniformity of the slurry, so that the suspending agent and the degumming agent can better play the role of improving the dispersion uniformity of the antibacterial agent Effect, limit the fineness...

Embodiment 1

[0064] A ceramic tile using the above-mentioned antibacterial ceramic glaze, prepared according to the following steps:

[0065] (1) Calculated according to the weight percent of the dry weight of the ceramic glaze, add 2% nano-zirconium silicate silver-loaded and 0.1% nano-zinc oxide (the particle size of nano-zirconium silicate silver-loaded and nano-zinc oxide) 25nm ± 2nm, Fe in the mixture of nano-zirconium silicate loaded with silver and nano-zinc oxide 2 0 3 ≤0.01%, TiO 2 ≤0.02%), mixed evenly to prepare ceramic glazes containing antibacterial agents, calculated according to the dry weight percentage of ceramic glazes containing antibacterial agents, adding 0.1% medium-viscosity carboxymethyl fiber in the above ceramic glazes containing antibacterial agents Sodium plain (the degree of polymerization is 600), 0.01% low-viscosity sodium carboxymethylcellulose (the degree of polymerization is 150) and 0.5% sodium metasilicate are evenly mixed, then add water and ball mill...

Embodiment 2

[0072] A ceramic tile using the above-mentioned antibacterial ceramic glaze, prepared according to the following steps:

[0073] (1) Calculate according to the weight percentage of ceramic glaze dry weight, add 5% nano zirconium silicate loaded silver and 1% nano zinc oxide (the particle diameter of nano zirconium silicate loaded silver and nano zinc oxide) in conventional ceramic glaze 25nm ± 5nm, Fe in the mixture of nano-zirconium silicate loaded with silver and nano-zinc oxide 2 0 3 ≤0.01%, TiO 2 ≤0.03%), mixed evenly to prepare ceramic glazes containing antibacterial agents, calculated according to the dry weight percentage of ceramic glazes containing antibacterial agents, adding 0.12% medium viscose carboxymethyl fiber in the above ceramic glazes containing antibacterial agents Sodium plain (the degree of polymerization is 550), 0.02% low-viscosity sodium carboxymethylcellulose (the degree of polymerization is 200) and 0.3% sodium metasilicate are evenly mixed, then a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of architectural ceramics, and in particular, relates to antibacterial ceramic glaze, and a preparation method and an application thereof. The antibacterial ceramic glaze is composed of the following raw material components: a ceramic glaze material, an antibacterial agent, a suspending agent and a peptizing agent, wherein the antibacterial agent is a mixture of nano zirconium silicate loaded silver and nano zinc oxide, and the addition amount of the nano zirconium silicate loaded silver is 2-6% and the addition amount of the nano zinc oxide is 0.05-2% according to the weight percentage of the dry weight of the ceramic glaze material; the suspending agent is a mixture of low-viscosity sodium carboxymethyl cellulose and medium-viscosity sodium carboxymethyl cellulose; the peptizing agent is one of sodium tripolyphosphate or sodium metasilicate. The invention aims to provide the antibacterial ceramic glaze, and the preparation method and the application thereof; the prepared ceramic glaze can realize uniform dispersion of an antibacterial agent in the ceramic tile surface glaze, and has efficient sterilization and bacteriostasis effects and stable sustainable sterilization effect.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to an antibacterial ceramic glaze and its preparation method and application. Background technique [0002] At present, the competition of architectural ceramics is becoming increasingly fierce. In order to continuously expand the market coverage, while reducing production costs and improving product designs, more emphasis is placed on improving the functionality and technical content of products. These properties greatly increase the added value of products, thereby strengthening products. competitiveness. At present, with the improvement of people's living standards, people have put forward higher requirements on the living environment, and how to prevent pathogenic bacteria from invading the human body is particularly urgent. As ceramic tiles commonly used in people's living rooms, there will always be some dead spots for pollution and bacterial growth, especially...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C03C8/14C04B41/86
CPCC03C8/00C03C8/14C04B41/5022C04B41/86
Inventor 林锦威钟保民徐瑜熊勋旺周燕
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap