Production process of coloured polyester filament nonwoven

A technology of non-woven fabrics and colored polyester, which is applied in non-woven fabrics, rayon manufacturing, textiles and papermaking, etc. It can solve the problems of single variety and late development of spunbond needle-punched non-woven fabrics, and achieve rapid antibacterial effect , feel smooth, improve the effect of mechanical properties

Inactive Publication Date: 2020-04-07
ELITE COLOR ENVIRONMENTAL RESOURCES SCI & TECH CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The market demand for spunbonded needle-punched nonwovens is very large. Compared with foreign countries, the development of domestic spunbonded needlepunched nonwovens started relatively late, and the variety is relatively single. It is ahead of the world in terms of raw materials, technology and equipment. There is still a gap in the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of coloured polyester filament nonwoven
  • Production process of coloured polyester filament nonwoven

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of production technology of colored polyester filament nonwoven fabric, comprises the steps:

[0027] S1. Heat 100kg of ethanol solution with a concentration of 40wt% to 70°C, add 2.5kg of konjac glucomannan and stir evenly, then add 0.6kg of silane coupling agent KH550 and stir for 30min at a stirring speed of 4000r / min. ℃, add 16kg of potassium titanate whiskers and 1.5kg of nano-zinc oxide and stir vigorously for 8min at a stirring speed of 9000r / min, let stand, filter, dry at 80℃, grind, and sieve to obtain the antibacterial agent;

[0028] S2. Send the polyester chips into the high-level silo through the dry hot air conveying device, feed them into the crystallizer through the rotary valve for pre-crystallization, pass through the drying tower and contact with the dry hot air from the bottom of the drying tower countercurrently, and carry out wet, Heat transfer to obtain pretreated dry slices with a moisture content of 25 mg / kg;

[0029] S3. Mix 100kg pretr...

Embodiment 2

[0033] A kind of production technology of colored polyester filament nonwoven fabric, comprises the steps:

[0034] S1. Heat 100kg of ethanol solution with a concentration of 60wt% to 62°C, add 4.5kg of konjac glucomannan and stir evenly, then add 0.4kg of silane coupling agent KH550 and stir for 50min at a stirring speed of 2000r / min, and heat to 150 ℃, add 8kg of potassium titanate whiskers and 2.5kg of nano zinc oxide and stir vigorously for 4min at a stirring speed of 10000r / min, let stand, filter, dry at 70℃, grind, and sieve to obtain the antibacterial agent;

[0035] S2. Send the polyester chips into the high-level silo through the dry hot air conveying device, feed them into the crystallizer through the rotary valve for pre-crystallization, pass through the drying tower and contact with the dry hot air from the bottom of the drying tower countercurrently, and carry out wet, Heat transfer to obtain pretreated dry slices with a moisture content of 35 mg / kg;

[0036] S3....

Embodiment 3

[0040] A kind of production technology of colored polyester filament nonwoven fabric, comprises the steps:

[0041] S1. Heat 100kg of ethanol solution with a concentration of 45wt% to 68°C, add 3kg of konjac glucomannan and stir evenly, then add 0.55kg of silane coupling agent KH550 and stir for 35min at a stirring speed of 3500r / min, and heat to 135°C under reflux , add 14kg of potassium titanate whiskers and 1.8kg of nano-zinc oxide and stir vigorously for 7min at a stirring speed of 9300r / min, let stand, filter, dry at 77°C, grind, and sieve to obtain the antibacterial agent;

[0042] S2. Send the polyester chips into the high-level silo through the dry hot air conveying device, feed them into the crystallizer through the rotary valve for pre-crystallization, pass through the drying tower and contact with the dry hot air from the bottom of the drying tower countercurrently, and carry out wet, Heat transfer to obtain pretreated dry slices with a moisture content of 28 mg / kg; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of a coloured polyester filament nonwoven. The production process of the coloured polyester filament nonwoven comprises the steps of: heating ethanol solution, adding konjac glucomannan to stir, then, adding a silane coupling agent KH550 to stir, heating under reflux, adding potassium titanate whiskers and nano-zinc oxide to stir, standing, filtering, drying, grinding, and sieving, so that an antibacterial agent is obtained; feeding a polyester chip into a high-level bin by adopting a dry hot air conveying device, performing pre-crystallization by feeding into a crystallizer through a rotary valve, enabling the polyester chip to pass through a drying tower, furthermore, performing countercurrent contact with dry hot air introduced from the bottom of the drying tower, and performing moisture and heat transmission, so that a pre-processed dry chip is obtained; mixing the pre-processed dry chip, the antibacterial agent, a dispersing agent withcolour master batches, entering a spinning assembly after extrusion melting, obtaining nascent fibres by spinning, and obtaining fibre filaments by cooling and drawing; and, uniformly laying the fibrefilaments by splitting filaments and placing filaments, so that a fibre web is obtained, obtaining a preliminary entanglement through a pre-needling machine, and then, reinforcing by needling througha main needling machine, so that the coloured polyester filament nonwoven is obtained.

Description

technical field [0001] The invention relates to the technical field of nonwoven fabrics, in particular to a production process of colored polyester filament nonwoven fabrics. Background technique [0002] The market demand for spunbonded needle-punched nonwovens is very large. Compared with foreign countries, the development of domestic spunbonded needlepunched nonwovens started relatively late, and the variety is relatively single. It is ahead of the world in terms of raw materials, technology and equipment. There is still a certain gap in the product. At present, with the serious homogeneity of needle-punched non-woven products, the competitive pressure of chemical fiber enterprises is increasing day by day, and they are developing differentiated products with high added value. The production of spun-bonded needle-punched non-woven fabrics is difficult and has high technical content. As the technology matures, it will inevitably attract more companies to develop it. [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04H3/011D04H3/105D04H18/02D01D5/08D01F1/10
CPCD04H3/011D04H3/105D04H18/02D01D5/08D01F1/103
Inventor 朱闻宇戴泽新戴梦茜徐平康玉杰陈晴袁震
Owner ELITE COLOR ENVIRONMENTAL RESOURCES SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com